Biodegradable high-temperature-resistant disposable tableware and preparation method thereof

A biodegradable and disposable technology, applied in the field of biodegradable tableware, can solve the problems of long degradation time, poor degradation effect, and rapid processing of unfavorable materials, and achieve the effect of improving degradability, strong durability and improving degradability.

Inactive Publication Date: 2021-07-09
上海通原环保科技有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this technical solution greatly improves the high temperature resistance of tableware and can store food at higher temperature for a long time, its degradation effect is poor and the degradation time is long, which is not conducive to the rapid processing of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] (1) Add 50 parts of modified starch, 5 parts of glass fiber, 40 parts of PLA, and 20 parts of PBAT into the mixer in sequence, and mix for 5 minutes at a speed of 600 r / min at room temperature to obtain the first mixture;

[0055] (2) Add 1 part of biodegradation accelerator and 2 parts of compatibilizer to the first mixture, heat to 40°C, and mix at a speed of 500r / min for 2 minutes to obtain the second mixture;

[0056] (3) Add 10 parts of mineral powder, 30 parts of polybutylene succinate, 5 parts of mica powder, and 10 parts of polyolefin to the second mixture, heat to 50°C, and mix at a speed of 800r / min for 5 Minutes, obtain the 3rd mixing material;

[0057] (4) Add 6 parts of foaming agent, 1 part of nucleating agent, and 5 parts of surfactant to the third mixture, heat to 40°C, and mix for 2 minutes at a speed of 500r / min to obtain the fourth mixture ;

[0058] (5) Add 1 part of sodium rosinate, 0.5 parts of magnesium aluminum silicate, 10 parts of polyethylen...

Embodiment 2

[0061] (1) Add 52 parts of modified starch, 6 parts of glass fiber, 42 parts of PLA, and 22 parts of PBAT into the mixer in sequence, and mix for 6 minutes at a speed of 700 r / min at room temperature to obtain the first mixture;

[0062] (2) Add 2 parts of biodegradation accelerator and 3 parts of compatibilizer to the first mixture, heat to 42°C, and mix for 3 minutes at a speed of 550r / min to obtain the second mixture;

[0063] (3) Add 12 parts of mineral powder, 32 parts of polybutylene succinate, 6 parts of mica powder, and 12 parts of polyolefin to the second mixture, heat to 55°C, and mix at a speed of 900r / min for 6 Minutes, obtain the 3rd mixing material;

[0064] (4) Add 7 parts of foaming agent, 1 part of nucleating agent, and 6 parts of surfactant to the third mixture, heat to 45°C, and mix for 3 minutes at a speed of 600r / min to obtain the fourth mixture ;

[0065] (5) Add 2 parts of sodium abietate, 0.6 parts of magnesium aluminum silicate, 12 parts of polyethyl...

Embodiment 3

[0068] (1) Add 53 parts of modified starch, 8 parts of glass fiber, 43 parts of PLA, and 43 parts of PBAT into the mixer in sequence, and mix at a speed of 800r / min for 8 minutes at room temperature to obtain the first mixture;

[0069] (2) Add 3 parts of biodegradation accelerator and 4 parts of compatibilizer to the first mixture, heat to 43°C, and mix for 5 minutes at a speed of 800r / min to obtain the second mixture;

[0070] (3) Add 13 parts of mineral powder, 33 parts of polybutylene succinate, 8 parts of mica powder, and 13 parts of polyolefin to the second mixture, heat to 60°C, and mix at a speed of 900r / min for 7 Minutes, obtain the 3rd mixing material;

[0071] (4) Add 9 parts of foaming agent, 2 parts of nucleating agent, and 8 parts of surfactant to the third mixture, heat to 50°C, and mix for 2 to 5 minutes at a speed of 500 to 800 r / min to obtain the fourth mixture;

[0072] (5) Add 3 parts of sodium rosinate, 1 part of magnesium aluminum silicate, 13 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
linear densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides biodegradable high-temperature-resistant disposable tableware and a preparation method thereof. The tableware is prepared from the following components: modified starch, glass fibers, PLA, PBAT, mineral powder, poly (butylene succinate), mica powder, polyolefin, sodium abietate, magnesium aluminum silicate, polyethylene glycol, a biodegradation accelerant, a compatilizer, a foaming agent, a nucleating agent, a surfactant, a dispersing agent and a coupling agent. The preparation method comprises the following steps: mixing the materials, adding into a mold, and carrying out hot press molding on the mold. The tableware has the beneficial effects that the tableware prepared by mixing the modified starch, the glass fibers, the PLA, the PBAT, the mineral powder, the poly (butylene succinate), the mica powder, the polyolefin, the sodium abietate, the magnesium aluminum silicate, the polyethylene glycol, the biodegradation accelerant, the compatilizer, the foaming agent, the nucleating agent, the surfactant, the dispersing agent and the coupling agent has a better degradation effect and higher high temperature resistance; and the material can be applied to high-temperature food and can effectively protect the ecological environment.

Description

technical field [0001] The invention relates to the technical field of biodegradable tableware, in particular to a biodegradable high-temperature resistant disposable tableware and a preparation method thereof. Background technique [0002] According to relevant data releases, the overall order volume of food delivery nationwide will reach 17.12 billion, a year-on-year increase of 7.5%, and the transaction scale of the national food delivery market will reach 835.2 billion yuan, a year-on-year increase of 14.8%. The number of takeaway users in my country is close to 500 million, and the post-80s and post-90s are the backbone of food delivery service consumption. The takeaway meals they order are not limited to three meals a day. Among them, afternoon tea and supper have become consumers. The new favorite for ordering takeout. [0003] The rise of takeaway has provided a huge market demand for disposable plastic tableware. A large amount of plastic products are consumed ever...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L3/04C08L67/04C08L67/02C08L23/00C08L71/02C08K13/04C08K7/14C08K3/34C08K3/26C08J9/04
CPCC08J9/0061C08J9/0066C08J9/0085C08J9/0095C08J9/04C08J2303/04C08J2423/00C08J2467/02C08J2467/04C08J2471/02C08K3/34C08K3/346C08K7/14C08K13/04C08K2003/265
Inventor 韦利国
Owner 上海通原环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com