Production process of multi-layer brazed diamond hole drill

A production process, diamond technology, applied in the direction of metal processing equipment, manufacturing tools, grinding devices, etc., can solve the problems of complex production, high requirements on substrate materials, etc., and achieve the effect of improving work efficiency, simple preparation process, and convenient clamping

Active Publication Date: 2021-07-09
JIANGSU FUNLIN SUPER HARD TOOLS
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the multi-layer structure of the existing hole drill: adopt the way of pointing, open grooves and slits on the substrate, and weld and embed the diamond material on the substrate. This preparation process has complex production, For the problem of high requirements on the substrate material, a production process of multi-layer brazing diamond hole drill is proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of multi-layer brazed diamond hole drill
  • Production process of multi-layer brazed diamond hole drill
  • Production process of multi-layer brazed diamond hole drill

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A production process for multi-layer brazing diamond hole drills, comprising the following preparation steps:

[0031] The first step: prepare the abrasive block; the abrasive block is made up of the following raw materials in parts by weight: 80 parts of solder, 10 parts of abrasive and 5 parts of binder; the solder is Cr-Ni brazing powder, the abrasive is diamond, and the binder is PVP- K30; The particle size of Cr-Ni brazing powder is 100 mesh, and the particle size of diamond is 300 mesh;

[0032] Add the abrasive blocks of raw materials in parts by weight into a stainless steel reaction kettle, mix them, take them out, place them in an oven and dry them for 30 minutes at a temperature of 100°C, take them out and cool them at room temperature;

[0033] The cooled abrasive blocks are crushed, and then screened through a particle size vibrating sieve to obtain a powdery abrasive block with a particle size of 1.5mm; two sets of screens should be installed in the sieve ...

Embodiment 2

[0038] A production process for multi-layer brazing diamond hole drills, comprising the following preparation steps:

[0039] The first step: prepare the abrasive block; the abrasive block is made up of the following raw materials in parts by weight: 100 parts of solder, 20 parts of abrasive and 10 parts of binder; the solder is Cr-Ni brazing powder, the abrasive is diamond, and the binder is PVP- K30; The particle size of Cr-Ni brazing powder is 200 mesh, and the particle size of diamond is 40 mesh;

[0040] Add the abrasive blocks of raw materials in parts by weight into a stainless steel reaction kettle, mix them, take them out, place them in an oven and dry them for 30 minutes at a temperature of 110°C, take them out and cool them at room temperature;

[0041] The cooled abrasive blocks are crushed, and then screened through a particle size vibrating sieve to obtain a powdery abrasive block with a particle size of 1.8 mm; two sets of screens should be installed in the scre...

Embodiment 3

[0046] A production process for multi-layer brazing diamond hole drills, comprising the following preparation steps:

[0047] The first step: prepare the abrasive block; the abrasive block is made up of the following raw materials in parts by weight: 120 parts of solder, 30 parts of abrasive and 15 parts of binder; the solder is Cr-Ni brazing powder, the abrasive is diamond, and the binder is PVP- K30; The particle size of Cr-Ni brazing powder is 300 mesh, and the particle size of diamond is 50 mesh;

[0048] Add the abrasive blocks of raw materials in parts by weight into a stainless steel reaction kettle, mix them, take them out, place them in an oven and dry them for 30 minutes at a temperature of 120°C, take them out and cool them at room temperature;

[0049] The cooled abrasive blocks are crushed, and then screened through a particle size vibrating sieve to obtain a powdery abrasive block with a particle size of 2.0mm; two sets of screens should be installed in the sieve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of a multi-layer brazed diamond hole drill. The production process comprises the following preparation steps: preparing abrasive blocks; adding the abrasive blocks prepared from raw materials in parts by weight into a stainless steel reaction kettle, mixing, taking out, drying and cooling; smashing and screening the cooled abrasive blocks to obtain powdery abrasive blocks; feeding the abrasive blocks; firstly, coating the outer wall of the bottom of a hole drill base body with a glue solution, loading the powdery abrasive blocks into an open tank and below the hole drill base body, and placing a magnet at the top end of the hole drill base body so that the hole drill base body generates magnetism; then, placing the bottom of the hole drill base body above the abrasive blocks so that the abrasive blocks are adsorbed on the outer wall of the hole drill base body in a layered mode; and brazing the abrasive blocks to the hole drill base body to obtain a diamond hole drill body. According to the production process, the abrasive blocks are distributed on the hole drill in a multi-layer form, so that the hole drill has very high strength and long service life during use; and the preparation process is simple.

Description

technical field [0001] The invention belongs to the technical field of drill bits, in particular to a production process of a multi-layer brazing diamond hole drill. Background technique [0002] The main function of the drill bit is to break the rock, form a wellbore and drill a hole in a hard object. [0003] The multi-layer structure of the existing hole drill: the way of pointing is adopted, grooves and gaps are opened on the substrate, and the diamond material is welded and embedded into the substrate. This preparation process has the problems of complicated production and high requirements for the substrate material. . Contents of the invention [0004] The purpose of the present invention is to solve the multi-layer structure of the existing hole drill: adopt the way of pointing, open grooves and slits on the substrate, and weld and embed the diamond material on the substrate. This preparation process has complex production, In order to solve the problem of high r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B24D18/00
CPCB24D18/0054B24D18/0072
Inventor 庄政伟庄敏伟
Owner JIANGSU FUNLIN SUPER HARD TOOLS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products