Organic/inorganic composition for consolidating quicksand and preparation method thereof

A composition and organic technology, applied in the directions of organic fertilizers, fertilizer mixtures, chemical instruments and methods, etc., can solve the problems of limited use range and toxic acrylamide, and achieve the effects of increasing viscosity, low viscosity and good fluidity

Inactive Publication Date: 2021-06-08
山西凝固力新型材料股份有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The viscosity of acrylamide grouting material grout is similar to that of water. The grout can fill the water seepage parts below 0.1mm in the structural cracks. The grouting performance is far better than all current grouting materials, but the acrylamide monomer is toxic, thus limiting the scope of use of this material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic/inorganic composition for consolidating quicksand and preparation method thereof
  • Organic/inorganic composition for consolidating quicksand and preparation method thereof
  • Organic/inorganic composition for consolidating quicksand and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of organic / inorganic composition that is used for consolidating quicksand described in this embodiment, comprises the component of following parts by weight:

[0038] Component A: 40 parts of hydroxyethyl acrylate, 30 parts of acrylamide, 2 parts of N,N-methylenebisacrylamide, 3 parts of triethanolamine, 5 parts of triacetin, and 20 parts of water;

[0039] Component B: 67 parts of water glass, 3 parts of initiator, 27 parts of water, and 3 parts of emulsifier.

[0040] The initiator described in this embodiment is ammonium persulfate.

[0041] The emulsifier described in this embodiment is the condensation product of O-10 fatty alcohol and ethylene oxide.

[0042] The water glass described in this embodiment has a modulus of 2.2 to 2.4 and a density of 1.4 to 1.5 g / cm 3 (20°C) sodium silicate water glass.

[0043] This embodiment is used for the preparation method of the organic / inorganic composition of consolidation quicksand, comprises the steps:

[0044] ...

Embodiment 2

[0050] A kind of organic / inorganic composition that is used for consolidating quicksand described in this embodiment, comprises the component of following parts by weight:

[0051] Component A: 41 parts of hydroxyethyl acrylate, 29 parts of acrylamide, 1.6 parts of N,N-methylenebisacrylamide, 2.4 parts of triethanolamine, 4 parts of triacetin, and 22 parts of water;

[0052] Component B: 69 parts of water glass, 3 parts of initiator, 25 parts of water, and 3 parts of emulsifier.

[0053] Initiator described in the present embodiment is potassium persulfate.

[0054] The emulsifier described in this embodiment is TX-13 alkylphenol polyoxyethylene ether.

[0055] The water glass described in this embodiment has a modulus of 2.2 to 2.4 and a density of 1.4 to 1.5 g / cm 3 (20°C) sodium silicate water glass.

[0056]This embodiment is used for the preparation method of the organic / inorganic composition of consolidation quicksand, comprises the steps:

[0057] The first step, the...

Embodiment 3

[0063] A kind of organic / inorganic composition that is used for consolidating quicksand described in this embodiment, comprises the component of following parts by weight:

[0064] Component A: 43 parts of hydroxyethyl acrylate, 28 parts of acrylamide, 1.4 parts of N,N-methylenebisacrylamide, 2 parts of triethanolamine, 2.6 parts of triacetin, and 23 parts of water;

[0065] Component B: 72 parts of water glass, 2 parts of initiator, 24 parts of water, and 2 parts of emulsifier.

[0066] The initiator described in this embodiment is ammonium persulfate.

[0067] The emulsifier described in this embodiment is the condensation product of O-10 fatty alcohol and ethylene oxide.

[0068] The water glass described in this embodiment has a modulus of 2.2 to 2.4 and a density of 1.4 to 1.5 g / cm 3 (20°C) sodium silicate water glass.

[0069] This embodiment is used for the preparation method of the organic / inorganic composition of consolidation quicksand, comprises the steps:

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an organic / inorganic composition for consolidating quicksand and a preparation method thereof. The organic / inorganic composition comprises the following components: a component A, which comprises hydroxyethyl acrylate, acrylamide, N,N-methylene bisacrylamide, triethanolamine, glycerol triacetate and water; and a component B, which comprises water glass, an initiator, water and an emulsifier. The preparation method comprises the following steps: preparation of a composition A: dissolving acrylamide and N,N-methylene bisacrylamide into water, adding hydroxyethyl acrylate, triethanolamine and glycerol triacetate into the water after acrylamide and N,N-methylene bisacrylamide are completely dissolved, and uniformly stirring to obtain the composition A; preparation of the composition B: dissolving an initiator and an emulsifier in water to form a mixture dissolving solution, and adding the mixture dissolving solution into water glass to obtain the composition B; and mixing the composition A and the composition B through a grouting machine at the temperature of 10-25 DEG C and then injecting into quicksand. The mixture solution is forcibly diffused, permeated, reacted and solidified, and then the quicksand can be consolidated. The composition is nontoxic or is low in toxicity.

Description

technical field [0001] The invention belongs to the technical field of composite grouting materials, and in particular relates to an organic / inorganic composition for consolidating quicksand and a preparation method thereof. [0002] technical background [0003] Chemical grouting and sand fixation is to prepare a certain chemical material (inorganic or organic material) into a solution, and use a chemical grouting pump and other pressure-feeding equipment to pour it into the formation or gap to make it diffuse, gel or solidify, so as to increase the strength of the formation, It is a ground treatment and concrete building crack repairing technology to reduce the permeability of the ground and prevent the deformation of the ground. [0004] Chemical grouting and sand-fixing materials are widely used in infrastructure construction. It is mainly divided into inorganic grouting materials and organic grouting materials. Inorganic grouting materials are mainly cement and water g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K17/40E02D3/12C08F220/20C08F220/56C08F222/38
CPCC09K17/40E02D3/12C08F220/20C09K2105/00C09K2103/00C08F220/56C08F222/385
Inventor 王建中王二中王涛范福洋柴亚跃常澔南薄鸿鹏
Owner 山西凝固力新型材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap