A kind of sound-absorbing and noise-reducing interior decoration material and preparation method thereof

A technology for interior decoration and raw materials, applied in the field of decorative materials, can solve the problems of low impact resistance, short service life, unfavorable promotion of polyvinyl chloride resin keels, etc., to improve impact resistance, enhance dissipation, and improve sound absorption and noise reduction effect of ability

Active Publication Date: 2022-03-15
广东正通博雅装饰工程有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the disadvantage of polyvinyl chloride resin keels is low impact resistance, resulting in short service life of polyvinyl chloride resin keels, which is not conducive to the promotion of polyvinyl chloride resin keels

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sound-absorbing and noise-reducing interior decoration material and preparation method thereof
  • A kind of sound-absorbing and noise-reducing interior decoration material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0048] Preparation of modified liquid:

[0049] At room temperature, mix and stir 0.1kg of γ-aminopropyltriethoxysilane, 0.1kg of hexamethyldisiloxane, 0.06kg of water-based polyurethane, 1kg of water and 0.15kg of ethanol in a reaction flask for 1.5 hours to obtain modifier fluid.

preparation example 2

[0051] Preparation of modified liquid:

[0052] At room temperature, mix and stir 0.1kg of γ-aminopropyltriethoxysilane, 0.15kg of hexamethyldisiloxane, 0.1kg of water-based polyurethane, 0.9kg of water and 0.1kg of ethanol in a reaction flask for 1.5 hours. Obtain modified solution.

Embodiment 1

[0055] A preparation method of a sound-absorbing and noise-reducing interior decoration material:

[0056] S1. under room temperature, 3kg polyvinyl chloride resin, 0.7kg styrene-methylstyrene copolymer, 0.13kg dilauryl thiodipropionate, 0.6kg tributyl citrate, 0.1kg calcium stearate and 0.05kg epoxidized soybean oil is dropped into the mixer, mixed and stirred for 20min, then added 0.2kg polycrystalline mullite fiber and continued to stir for 10min to obtain a mixture;

[0057] S2. put the mixture into the mill for milling, the milling temperature is 135°C, the milling time is 15min, and milled flakes are obtained;

[0058] S3. Put the refined flakes into the mould, then put the mold into a flat vulcanizing machine, vulcanize and form, molding temperature 150°C, molding time 10min, molding pressure 2Mpa, to obtain a sound-absorbing and noise-reducing interior decoration material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The application relates to the field of decoration materials, and specifically discloses a sound-absorbing and noise-reducing interior decoration material and a preparation method thereof. A sound-absorbing and noise-reducing interior decoration material, prepared from the following raw materials in parts by weight: 30-50 parts of polyvinyl chloride resin; 7-12 parts of styrene-methylstyrene copolymer; 2-3.5 parts of reinforcing fiber ; Plasticizer 6~10 parts; Antioxidant 0.8~1.3 parts; Stabilizer 1.5~2 parts. The preparation method is as follows: mixing and stirring the raw materials in advance to obtain a mixture, and then kneading to obtain kneaded flakes, and then vulcanizing molding to obtain a sound-absorbing and noise-reducing interior decoration material, which has the ability to improve the impact resistance of polyvinyl chloride resin, The advantages of maintaining good sound absorption and noise reduction capabilities.

Description

technical field [0001] The application relates to the field of decoration materials, more specifically, it relates to a sound-absorbing and noise-reducing interior decoration material and a preparation method thereof. Background technique [0002] Modern life pays more and more attention to the health of the indoor environment, and the indoor noise reduction effect directly affects the quality of life. The indoor noise reduction treatment is mainly to confine the noise in a small space, or absorb the noise, so as to provide a comfortable acoustic environment; Indoor noise reduction methods are generally divided into sound insulation and sound absorption. Sound insulation is to use dense materials to isolate sound waves from the outside. . [0003] For sound absorption and noise reduction, people generally install sound-absorbing panels indoors, such as high-density foam boards and sound-absorbing cotton panels, and the installation of sound-absorbing panels generally uses l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L25/08C08L91/00C08K13/06C08K9/06C08K7/10C08K7/08C08K5/098C08K5/372C08K5/11C08J5/06
CPCC08J5/06C08J2327/06C08J2425/08C08J2491/00C08K13/06C08K9/06C08K9/08C08K7/10C08K7/08C08K5/098C08K5/372C08K5/11
Inventor 李承先冯巨昌
Owner 广东正通博雅装饰工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products