Hydrophilic self-adhesive glue suitable for cold compress self-adhesive compression bandages, preparation method and application

A compression bandage, hydrophilic technology, applied in bandages, dressings, viscous dressings, etc., can solve problems such as poor compression effect, decreased adhesion, and lack of hydrophilicity

Active Publication Date: 2021-04-27
杭州高斯博医疗用品有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional cold compress bandage is composed of elastic cotton base material and cold compress liquid, the compression effect is poor, and the outer layer needs to be fixed with PP non-woven self-adhesive elastic bandage to strengthen the compression effect
However, the adhesive and substrate of ordinary self-adhesive bandages are not hydrophilic, so they cannot absorb cold compress fluid, and the adhesive force decreases significantly after wetting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: Ingredients: 50 parts of polyisoprene latex (IR-550) (solid content 50%), 5 parts of liquid paraffin, 5 parts of polyacrylate emulsion, 5 parts of PEG (600), 5 parts of PVA (1799) 5 parts, 5 parts of PVP (K90), 50 parts of water.

[0021] Add 50 kg of cold water, 5 kg of PEG600, 5 kg of PVA1799, and 5 kg of PVP K90 into the batching kettle A in sequence, start stirring, heat to the system temperature of 85-90 degrees and maintain the temperature, and stop heating after the materials are completely dissolved and the system is transparent. (about 3 hours), continue to stir until system temperature drops below 45 degrees.

[0022] Add 50 kg of polyisoprene latex (50% solid content) into batching kettle B, start stirring, heat to system temperature 40-45 degrees and maintain this temperature, then add 5 kg of liquid paraffin, 5 kg of polyacrylate Emulsion, after stirring for 2 hours, add the aforementioned materials, and continue stirring for 1 hour before disch...

Embodiment 2

[0025] Ingredients: 50 parts of polyisoprene latex (solid content 50%), 8 parts of liquid paraffin, 5 parts of polyacrylate emulsion, 4 parts of PEG (2000), 6 parts of PVA (2099), 3 parts of PVP (K90), 50 parts of water.

[0026] Add 50 kg of cold water, 4 kg of PEG2000, 6 kg of PVA2099, and 3 kg of PVP K90 into the batching kettle A in sequence, start stirring, heat to the system temperature of 85-90 degrees and maintain the temperature, and stop heating after the materials are completely dissolved and the system is transparent. (about 3 hours), continue to stir until system temperature drops below 45 degrees.

[0027] Add 50 kilograms of polyisoprene latex (50% solid content) into batching kettle B, start stirring, heat to system temperature 40-45 degrees and maintain this temperature, then add 8 kilograms of liquid paraffin, 5 kilograms of polyacrylate Emulsion, after stirring for 2 hours, add the aforementioned materials, and continue stirring for 1 hour before dischargin...

Embodiment 3

[0030] Ingredients: 50 parts of natural latex (solid content 60%), 12 parts of liquid paraffin, 6 parts of polyacrylate emulsion, 6 parts of PEG (1500), 4 parts of PVA (2499), 2 parts of PVP (K90), 60 parts of water,

[0031] Add 60 kg of cold water, 6 kg of PEG1500, 4 kg of PVA2499, and 2 kg of PVP K90 into the batching kettle A in sequence, start stirring, heat to the system temperature of 85-90 degrees and maintain the temperature, and stop heating after the materials are completely dissolved and the system is transparent. (about 3 hours), continue to stir until system temperature drops below 45 degrees.

[0032] 50 kilograms of natural rubber latex (60% solid content) are added in batching kettle B, start stirring, be heated to system temperature 40-45 degree and maintain this temperature, then add 12 kilograms of liquid paraffins successively, 6 kilograms of polyacrylate emulsions, stir 2 After one hour, the above-mentioned materials were added, and the stirring was conti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses hydrophilic self-adhesive glue suitable for cold compress self-adhesive compression bandages, a preparation method and an application. The hydrophilic self-adhesive glue comprises the following components in percentage by weight: 1%-10% of polyvinyl alcohol, 1%-10% of polyethylene glycol, 0%-10% of polyvinylpyrrolidone, 20%-30% of natural latex or polyisoprene latex, 3%-10% of liquid paraffin, 2%-5% of polyacrylate emulsion, 50%-70% of water and the balance other components, wherein the percentage by weight of the natural latex or the polyisoprene latex is calculated according to dry glue. According to the hydrophilic self-adhesive glue suitable for the cold compress self-adhesive elastic bandages, the natural latex or the polyisoprene latex is compounded with PVA, PVP, PEG and the like, so that the hydrophilic self-adhesive glue can still achieve enough adhesive force under the wetting condition, and the peel strength is larger than or equal to 0.03KN / m.

Description

technical field [0001] The invention belongs to the technical field of self-adhesives, in particular to a hydrophilic self-adhesive suitable for cold compress self-adhesive compression bandages. Background technique [0002] The traditional cold compress bandage is composed of elastic cotton base material and cold compress liquid, and the compression effect is poor. The outer layer needs to be fixed with PP non-woven self-adhesive elastic bandage to strengthen the compression effect. However, the adhesive and substrate of ordinary self-adhesive bandages are not hydrophilic, so they cannot absorb cold compresses, and the adhesive force decreases significantly after wetting. Contents of the invention [0003] The invention provides a hydrophilic self-adhesive adhesive suitable for cold compress self-adhesive compression bandages with good hydrophilicity and strong adhesive force after wetting. The invention also provides a preparation method for the above-mentioned hydrophi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/24A61L15/26A61L15/10A61L15/58A61F13/02
CPCA61L15/26A61L15/24A61L15/10A61L15/58A61F13/0253A61F13/0256C08L71/02C08L29/04C08L39/06C08L23/20C08L33/08
Inventor 来焱郑乐回
Owner 杭州高斯博医疗用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap