Metal carbon nanotube composite film modified by porous polymer and its preparation method and application

A carbon nanotube composite, porous polymer technology, used in chemical instruments and methods, membrane technology, water pollutants, etc., can solve problems such as affecting the growth of aquatic organisms and microorganisms, reducing water transparency, and affecting human health, etc. Effects of suitability for dye separation, enhanced stability and durability, large application potential

Active Publication Date: 2021-09-28
SUZHOU UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The dyes in wastewater can absorb light, reduce the transparency of water, affect the growth of aquatic organisms and microorganisms, not conducive to the self-purification of water, and even seriously affect human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal carbon nanotube composite film modified by porous polymer and its preparation method and application
  • Metal carbon nanotube composite film modified by porous polymer and its preparation method and application
  • Metal carbon nanotube composite film modified by porous polymer and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1 The preparation of a porous polymer-modified metal-carbon nanotube composite membrane, the specific steps are as follows:

[0022] (1) Synthesis of modified multi-walled carbon nanotube (MWCNT) films. First, 30 ml of concentrated hydrochloric acid and 10 ml of concentrated nitric acid were prepared into aqua regia at a volume ratio of 3:1, and the existing MWCNT film was placed in it and soaked at 50 °C for 6 hours for acidification. Then, the acidified MWCNT film Wash with ultrapure water and dry;

[0023] Accurately weigh 0.112 g of zirconium tetrachloride and 0.087 g of terephthalic acid, dissolve them in 60 ml of N,N-dimethylformamide (DMF), then sonicate for 20 minutes, and subsequently, add 8.3 Milliliter of acetic acid to obtain the mixture, then transfer the mixture and acidified dried MWCNT film (10*10 cm2) into a 100 ml stainless steel autoclave, heat at 120 °C for 24 hours; after natural cooling, wash with DMF and methanol, Finally, dry at 60 degr...

Embodiment 2

[0030] Example 2 Comparative test of the dye separation effect of the metal-loaded modified MWCNT membrane before and after modifying the porous polymer

[0031] attached figure 2 Separation experiments of two single-component dye solutions were carried out to compare the separation effects of membranes before and after coating with porous polymers; figure 2 Among them, a is the separation efficiency of Congo red by the composite membrane modified with porous polymer, b is the separation efficiency of Congo red by the modified MWCNT membrane loaded with metal, and c is the separation efficiency of Congo red solution by the composite membrane modified with porous polymer. Cycle separation efficiency, d is the separation efficiency of rhodamine B by the composite membrane modified with porous polymer, e is the separation efficiency of rhodamine B by the modified MWCNT membrane loaded with metal, f is the separation efficiency of rhodamine B by the composite membrane modified w...

Embodiment 3

[0040] Example 3 Dye Separation Performance Test of Composite Membrane Modified with Porous Polymer

[0041] The separation efficiency of the composite membrane for dyes with different molecular weights was tested. The results show that the separation efficiency of the membrane for various dyes with a molecular weight of 200 to 1300 is above 90%, which indicates that the separation performance of the composite membrane has wide applicability. In addition, chrome black T was selected as the dye for testing the cycle performance of the membrane. After 10 cycles, the separation efficiency of Chrome Black T decreased from 98% to 96%, and the separation flux remained at 40 L m -2 the s -1 MPa -1 Above, it is shown that composite membranes modified with porous polymers can effectively perform a variety of separation operations.

[0042] attached image 3 is the separation efficiency of dyes with different molecular weights; Figure 4 is the recirculation separation efficienc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
separationaaaaaaaaaa
separationaaaaaaaaaa
separationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a metal carbon nanotube composite film modified by a porous polymer and its preparation method and application. The acidified carbon nanotube film is mixed with a modification solution and heated to react to obtain a modified carbon nanotube film; and then the carbon nanotube film is modified. The surface of the tube membrane is coated with polyethylene glycol and then coated with a porous polymer solution, and heat-treated to obtain a porous polymer-modified metal carbon nanotube composite membrane. The invention successfully prepares the metal carbon nanotube composite film coated with the porous polymer, and realizes the high-efficiency nanofiltration separation of various dyes, and the separation efficiency of the tested various dyes reaches 90% or higher. In addition, the membrane material is easy to fabricate and has wide applicability for dye separation, showing great application potential.

Description

technical field [0001] The invention belongs to the technical field of functional materials, and in particular relates to a metal carbon nanotube composite film modified by a porous polymer and a preparation method thereof, and is specifically applied to the separation of dye-containing wastewater. Background technique [0002] In the textile printing and dyeing industry, the use of dyes is very large, so the discharged industrial wastewater often contains a variety of dyes, which has become one of the important reasons for water pollution. The dyes in wastewater can absorb light, reduce the transparency of water, affect the growth of aquatic organisms and microorganisms, not conducive to the self-purification of water, and even seriously affect human health. At present, in order to solve the dyes contained in sewage, various water purification processes have been developed, such as chemical oxidation, adsorption, photodegradation, biodegradation, and membrane separation, et...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01D67/00B01D69/02B01D69/12B01D71/60C02F1/44C02F101/30
CPCB01D71/021B01D71/022B01D71/60B01D69/02B01D69/12B01D67/0079B01D61/027C02F1/442C02F2101/308Y02W10/10
Inventor 路建美陈冬赟
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap