Preparation method of porous carbon-nitrogen material loaded nano bimetallic catalyst and use method of catalyst in benzoic acid hydrogenation reaction

A technology of bimetallic catalyst and porous carbon, which is applied in the direction of catalyst activation/preparation, preparation of carboxylic acid by ozone oxidation, nanotechnology for materials and surface science, etc. It can solve the problem of difficult separation of catalyst and product and low catalytic activity of metal sulfides , difficult to recycle and other issues

Active Publication Date: 2021-03-12
WEIFANG UNIV OF SCI & TECH
View PDF20 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These catalysts play a key role in various hydrogenation synthesis processes, but there are also some problems: the catalyst is difficult to separate from the product, and it is not easy to recycle; the noble metal catalyst is easily deactivated by organic sulfur and organic nitrogen poisoning; the catalytic activity of metal sulfide inferior
[0005] In summary, there are obviously inconveniences and defects in the actual use of the existing technology, so it is necessary to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of porous carbon-nitrogen material loaded nano bimetallic catalyst and use method of catalyst in benzoic acid hydrogenation reaction
  • Preparation method of porous carbon-nitrogen material loaded nano bimetallic catalyst and use method of catalyst in benzoic acid hydrogenation reaction
  • Preparation method of porous carbon-nitrogen material loaded nano bimetallic catalyst and use method of catalyst in benzoic acid hydrogenation reaction

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] A kind of porous carbon-nitrogen material supported nano bimetallic catalyst, its preparation method comprises the steps:

[0034] Step 1, preparation of biomass-based porous carbon-nitrogen carrier material;

[0035] (1) Pretreatment: Take loofah vines, air dry them naturally, remove leaves and leave stems, first rinse with tap water 2 to 3 times to remove contaminated dust, soil and other large particles visible to the naked eye; then soak in 2% detergent for 10 ~ After soaking for 20 minutes, rinse with tap water 3 times, 12-18 minutes each time; then blanched with boiling water at 100°C for 1-2 minutes; finally rinsed with deionized water 3 times, 1-2 minutes each time; Cut into sections, bake in a constant temperature drying oven at 90°C for 30 hours to remove free water in the material; after drying, crush, pass through a 17-19 mesh standard sieve, and pack into bags for later use.

[0036] (2) High-temperature pyrolysis: Weigh 3 g of pretreated raw materials, pl...

Embodiment 1

[0045] (1) Pretreatment: take loofah vines, air dry them naturally, remove leaves and keep stems, first rinse twice with tap water to remove contaminated dust, soil and other large particles visible to the naked eye; then soak in 2% detergent for 15 minutes, soak Then rinse with tap water for 3 times, each time for 15 minutes; then blanched with 100°C boiling water for 1 minute; finally, rinse with deionized water for 3 times, each time for 1 minute; cut the above-mentioned rinsed materials into sections, and place them at 90°C In a constant temperature drying oven, bake for 30 hours to remove free water in the material; after drying, crush, pass through a 18-mesh standard sieve, and bag for later use.

[0046] (2) High-temperature pyrolysis: Weigh 3 g of pretreated raw materials, place them in a tube furnace, and blow nitrogen (N 2 The flow rate was 100 sccm), and the temperature was programmed to 800 °C; after 800 °C constant temperature carbonization for 2 h, the temperatur...

Embodiment 2

[0050] (1) Pretreatment: take loofah vines, air dry them naturally, remove leaves and keep stems, first rinse twice with tap water to remove contaminated dust, soil and other large particles visible to the naked eye; then soak in 2% detergent for 15 minutes, soak Then rinse with tap water for 3 times, each time for 15 minutes; then blanched with 100°C boiling water for 1 minute; finally, rinse with deionized water for 3 times, each time for 1 minute; cut the above-mentioned rinsed materials into sections, and place them at 90°C In a constant temperature drying oven, bake for 30 hours to remove free water in the material; after drying, crush, pass through a 18-mesh standard sieve, and bag for later use.

[0051] (2) High-temperature pyrolysis: Weigh 3 g of pretreated raw materials, place them in a tube furnace, and blow nitrogen (N 2 The flow rate was 100 sccm), and the temperature was programmed to 900 °C; after carbonization at a constant temperature of 900 °C for 2 h, the te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is applicable to the technical field of catalysts, and provides a preparation method of a porous carbon-nitrogen material loaded nano bimetallic catalyst. The preparation method comprises the following steps: 1, preparing a biomass-based porous carbon-nitrogen carrier material, and carrying out pretreatment, high-temperature pyrolysis, cleaning, drying and grinding; 2, preparing a porous carbon-nitrogen loaded Fe / CoS2 / HCCS nano bimetallic catalyst; The invention relates to a method for using a porous carbon-nitrogen material loaded nano bimetallic catalyst in benzoic acid hydrogenation reaction. The method comprises the following steps: sealing a mixture of benzoic acid, a solvent and the porous carbon-nitrogen material loaded nano bimetallic catalyst in a reaction kettle forreaction. Therefore, the dispersity of the catalyst in the reaction solvent can be enhanced, the active sites of the carbon material are increased, the activity of the catalyst is enhanced through the cooperation of double metals, and the product yield is increased.

Description

technical field [0001] The invention relates to the technical field of catalysts, in particular to a preparation method of a porous carbon-nitrogen material-loaded nanometer bimetallic catalyst and a method for using it in the hydrogenation reaction of benzoic acid. Background technique [0002] Cyclohexanecarboxylic acid and its derivatives are widely used in all walks of life, especially nowadays, pharmaceutical and chemical products are becoming more and more important to people's lives. The economical and efficient synthesis of cyclohexanecarboxylic acid and its derivatives has high significance and value . [0003] It is well known that the selective benzene ring hydrogenation of benzoic acid is the most direct and effective method for the synthesis of cyclohexanecarboxylic acid. However, because the hydrogenation of benzoic acid needs to overcome the high resonance energy of the benzene ring, the hydrogenation of benzoic acid is much more difficult than the reduction ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24B01J27/043B01J37/08B01J37/16B01J35/10B82Y30/00B82Y40/00C07C51/36C07C61/08
CPCB01J27/24B01J27/043B01J37/082B01J37/16B82Y30/00B82Y40/00C07C51/36C07C2601/14B01J35/23B01J35/613B01J35/651B01J35/633B01J35/647C07C61/08
Inventor 张姗姗李成杰张英超冯丽娟刘燕峰于磊
Owner WEIFANG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com