Preparation method of hmx/anpyo co-crystal under confined doping conditions for two-dimensional materials

A technology of two-dimensional materials and conditions, applied in offensive equipment, explosives processing equipment, nitrated acyclic/alicyclic/heterocyclic amine explosive composition, etc., can solve the problem of inability to ensure the crystal eutectic state and the molar ratio of the constituent molecules The same problems, to achieve the effect of improving crystal surface defects, precise control of material structure and performance, and high yield

Active Publication Date: 2021-10-22
NORTHWESTERN POLYTECHNICAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the eutectic technique, it is not guaranteed that all crystals are in the eutectic state, or that the molar ratios of the constituent molecules in each crystal are the same

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of hmx/anpyo co-crystal under confined doping conditions for two-dimensional materials
  • Preparation method of hmx/anpyo co-crystal under confined doping conditions for two-dimensional materials
  • Preparation method of hmx/anpyo co-crystal under confined doping conditions for two-dimensional materials

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0028] A preparation method of HMX / ANPyO eutectic under the confinement doping condition of a two-dimensional material, comprising the following process steps:

[0029] Dissolution of triaminoguanidine nitrate: Weigh 0.235g of triaminoguanidine nitrate and add it to 7.01ml dimethyl sulfoxide, heat to 140°C in a water bath (oil bath, electric heating), and magnetically stir (rotor speed 1000r / min) 10min to completely dissolve triaminoguanidine nitrate.

[0030] Dissolution of ammonium nitrate explosive: Weigh 1 g of Octogold, 0.168 g of ANPyO (the molar ratio of Octogold to ANPyO is 4:1, the total molar ratio of triaminoguanidine nitrate to the two explosives is 1:3) and add Into the dissolved triaminoguanidine nitrate solution, use a magnetic stirrer to stir for a period of time until Octogen and ANPyO are completely dissolved, and the solution turns reddish orange (the time in this example is 1h).

[0031] Formation of high-nitrogen two-dimensional conjugated structure mater...

example 2

[0039] A preparation method of HMX / ANPyO eutectic under the confinement doping condition of a two-dimensional material, comprising the following process steps:

[0040] Dissolution of triaminoguanidine nitrate: Weigh 0.564g of triaminoguanidine nitrate and add it to 16.18ml dimethyl sulfoxide, heat to 140°C in a water bath (oil bath, electric heating), and magnetically stir (rotor speed 1000r / min) 10min to completely dissolve triaminoguanidine nitrate.

[0041] Dissolution of ammonium nitrate explosive: Weigh 2g of Octogold, ANPyO0.6723g (the molar ratio of Octogold to ANPyO is 2:1, the total molar ratio of triaminoguanidine nitrate to the two explosives is 1:3) and add Into the dissolved triaminoguanidine nitrate solution, use a magnetic stirrer to stir for a period of time until Octogen and ANPyO are completely dissolved, and the solution turns reddish orange (the time in this example is 1h).

[0042] Formation of high-nitrogen two-dimensional conjugated structure material:...

example 3

[0050] A preparation method of HMX / ANPyO eutectic under the confinement doping condition of a two-dimensional material, comprising the following process steps:

[0051] Dissolution of triaminoguanidine nitrate: Weigh 0.212g triaminoguanidine nitrate and add it to 6.48ml dimethyl sulfoxide, heat to 140°C in a water bath (oil bath, electric heating), and magnetically stir (rotor speed 1000r / min) 10min to completely dissolve triaminoguanidine nitrate.

[0052] Dissolution of ammonium nitrate explosive: Weigh 1g of Octogold, ANPyO0.0840g (the molar ratio of Octogold to ANPyO is 8:1, the total molar ratio of triaminoguanidine nitrate to the two explosives is 1:3) and add Into the dissolved triaminoguanidine nitrate solution, use a magnetic stirrer to stir for a period of time until Octogen and ANPyO are completely dissolved, and the solution turns reddish orange (the time in this example is 1h).

[0053] Formation of high-nitrogen two-dimensional conjugated structure material: add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a preparation method of HMX / ANPyO eutectic under the confinement doping condition of a two-dimensional material. Triaminoguanidine nitrate (TAGN) is mixed with dimethyl sulfoxide (DMSO), and then HMX and ANPyO are added and waited for Dissolve completely, add glyoxal to obtain a two-dimensional conjugated structure material; grow HMX / ANPyO on this two-dimensional conjugated structure, and obtain HMX / ANPyO co-crystal under confined doping conditions. The method of the invention is simpler, the final material structure and performance can be precisely controlled through reaction conditions and doping amount, the product yield is high, the cost of raw materials used is low, and industrial production is easy to realize. Secondly, under the confinement doping conditions of two-dimensional materials, its crystal stiffness and molecular order packing density are improved, thereby improving its detonation performance. Finally, under the confinement doping conditions of 2D materials, HMX and ANPyO can form co-crystals in any ratio, and the experimental conditions are easy to control.

Description

technical field [0001] The invention belongs to the technical field of energetic materials, and relates to a preparation method of HMX / ANPyO eutectic under the condition of confined doping of two-dimensional materials. Background technique [0002] Low-fragility propellants show good stability against severe external stimuli such as heating, impact, and shock waves, and can greatly improve the battlefield survivability of combatants and weapons and equipment. There is an essential contradiction between the energy and safety of energetic materials, and the lack of high-energy insensitive energetic materials is the main bottleneck technology for the development of low-vulnerability propellants. [0003] Researchers continue to design and synthesize new energetic materials to obtain new high-energy insensitive explosives, such as 1,1-diamino-2,2-dinitropyrazine (FOX-7), 4,10-dinitro-2 ,6,8,12-tetraoxa-2,10-diazaisowurtzitane (TEX), 2,6-diamino-,3,5-dinitropyridine was also suc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C06B25/34C06B21/00
CPCC06B21/0008C06B25/34
Inventor 严启龙薛智华张雪雪黄彬彬何伟
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com