Environment-friendly water-based ink, and environment-friendly high-strength compression-resistant color box and manufacturing method thereof

A water-based ink, environmental protection technology, applied in the direction of ink, chemical instruments and methods, lamination, etc., can solve problems such as difficult to guarantee quality, achieve the effect of ensuring aesthetics and user experience, reducing environmental pollution, and improving strength

Inactive Publication Date: 2020-12-29
晋江市顺力纸箱有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

No matter which process is used to produce the color box, its bearing pressure and compressive strength are much lower than that of ordinary cartons of the same material (produced by cardboard lines), and it is difficult to guarantee the quality when customers are in urgent need or in rainy days.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly water-based ink, and environment-friendly high-strength compression-resistant color box and manufacturing method thereof
  • Environment-friendly water-based ink, and environment-friendly high-strength compression-resistant color box and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A kind of environment-friendly water-based ink, is made from the raw material that comprises following parts by weight:

[0061] 28 parts of epoxy-acrylic resin,

[0062] Fluorosilicone modified acrylate emulsion 12 parts,

[0063] 7 parts of hydroxycellulose,

[0064] 10 parts of colorant,

[0065] 20 parts of nano calcium carbonate,

[0066] 2 parts of cerium dioxide,

[0067] Butyl cellosolve 10 parts,

[0068] 10 parts of triethanolamine,

[0069] 0.5 part of defoamer,

[0070] 0.6 parts of sodium hexametaphosphate,

[0071] Trimethoprim 0.5 part,

[0072] 1.2 parts of additives,

[0073] 15 parts of deionized water,

[0074] 5 parts isopropanol.

[0075] The purity of the ceria of the present embodiment is 99.9-99.99%, and the density is 7.13-7.15g / cm 3 .

[0076] The preparation technology of the auxiliary agent of the present embodiment comprises the following steps:

[0077] Step 1. In N 2 Add nano-titanium dioxide into water and stir under the atmo...

Embodiment 2

[0091] A kind of environment-friendly water-based ink, is made from the raw material that comprises following parts by weight:

[0092] 35 parts of epoxy-acrylic resin,

[0093] Fluorosilicone modified acrylate emulsion 11 parts,

[0094] 8 parts of hydroxycellulose,

[0095] 20 parts of colorant,

[0096] 15 parts of nanometer calcium carbonate,

[0097] 3 parts of cerium dioxide,

[0098] Butyl cellosolve 5 parts,

[0099] 8 parts of triethanolamine,

[0100] 0.6 parts of defoamer,

[0101] 0.7 parts of sodium hexametaphosphate,

[0102] Trimethoprim 0.9 parts,

[0103] 0.5 parts of additives,

[0104] 22 parts of deionized water,

[0105] 3 parts isopropanol.

[0106] The purity of the ceria of the present embodiment is 99.9-99.99%, and the density is 7.13-7.15g / cm 3 .

[0107] The preparation technology of the auxiliary agent of the present embodiment comprises the following steps:

[0108] Step 1. In N 2 Add nano-titanium dioxide to water under atmosphere a...

Embodiment 3

[0122] A kind of environment-friendly water-based ink, is made from the raw material that comprises following parts by weight:

[0123] 25 parts of epoxy-acrylic resin,

[0124] Fluorosilicone modified acrylate emulsion 15 parts,

[0125] 6 parts of hydroxycellulose,

[0126] 30 parts of colorant,

[0127] 5 parts of nanometer calcium carbonate,

[0128] 2.5 parts of cerium dioxide,

[0129] 6 parts of triethanolamine,

[0130] 0.7 part of defoamer,

[0131] Sodium hexametaphosphate 1.0 part,

[0132] Trimethoprim 1.0 parts,

[0133] Auxiliary 1.0 parts,

[0134] 25 parts of deionized water,

[0135] 4 parts isopropanol.

[0136] The purity of the ceria of the present embodiment is 99.9-99.99%, and the density is 7.13-7.15g / cm 3 .

[0137] The preparation technology of the auxiliary agent of the present embodiment comprises the following steps:

[0138] Step 1. In N 2 Add nano-titanium dioxide into water and stir under the atmosphere, add ammonia water after heat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly water-based ink, and an an environment-friendly high-strength compression-resistant color box and a manufacturing method thereof. The environment-friendlywater-based ink is prepared from the following raw materials in parts by weight: 25-35 parts of epoxy acrylic resin, 10-15 parts of fluorosilicone modified acrylate emulsion, 5-8 parts of hydroxy cellulose, 10-30 parts of colorant, 5-20 parts of nano calcium carbonate, 1-3 parts of cerium dioxide, 0-11 parts of butyl cellosolve, 5-10 parts of triethanolamine, 0.5-0.8 part of defoamer, 0.5-1.0 partof sodium hexametaphosphate, 0.5-1.1 parts of trimethoprim, 0.5-1.5 parts of an auxiliary agent, 15-25 parts of deionized water and 3-5 parts of isopropanol. According to the invention, the corrugated paper of the middle layer of the color box is folded into a corrugated structure, so that the stability of the structure of the middle layer is improved, and the situation that the corrugated paperis impacted and deformed, and consequently the corrugated structure in the corrugated paper is damaged is reduced.

Description

technical field [0001] The invention relates to the technical field of packaging cartons, in particular to an environment-friendly water-based ink, an environment-friendly high-strength pressure-resistant color box and a manufacturing method thereof. Background technique [0002] The rise of the green revolution has brought a huge impact to the packaging and printing industry. The volatilization of solvents in traditional solvent-based inks will not only pollute the air, but also cause product symptoms, posing a threat to the health of printing workers and consumers. In this context, water-based inks emerged as the times require. As an environmentally friendly ink, water-based ink eliminates the hazards of toxic and harmful substances in solvent-based inks to human health and pollution to packaged goods, and is suitable for packaging and printing of food, beverages, and pharmaceuticals. Water-based ink can reduce the risk of static electricity and solvent flammability, red...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/03C09D11/102C09D11/107C09D11/14B32B29/08B32B29/00B32B3/08B32B7/12B32B37/12B32B37/24
CPCC09D11/03C09D11/102C09D11/107C09D11/14B32B29/08B32B29/005B32B29/00B32B3/08B32B7/12B32B37/12B32B37/24B32B2037/243
Inventor 李培养
Owner 晋江市顺力纸箱有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com