Environment-friendly pervious concrete and preparation method thereof

A permeable concrete and environmental protection technology, applied in the field of building materials, can solve the problems of rubber powder easily blocking the pores and channels of permeable concrete, unfavorable promotion, etc., to achieve good fatigue resistance and water permeability, convenient operation and control, and improve various performances. Effect

Inactive Publication Date: 2020-11-13
韩昌龙
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in practical application, rubber powder is easy to block the pores and channels of permeable concrete, and it does not take advantage of market promotion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1 provides a kind of environment-friendly permeable concrete, is characterized in that, comprises the following components by weight: 20 parts of cement, 0.5 part of aluminum oxide nanotube, N-(trimethoxysilylpropyl) ethylenediaminetriacetic acid 2 parts of ammonium salt modified nano-aluminum powder, 60 parts of coarse aggregate, 0.5 part of nanoporous hollow cage titanium oxide, 1 part of porous polysaccharide microsphere, 0.1 part of sodium sulfonate-based hyperbranched poly(amine-ester), water 20 parts; Described cement is ordinary portland cement.

[0031] The preparation method of the N-(trimethoxysilylpropyl) ammonium ethylenediamine triacetate modified nano-aluminum powder comprises the following steps: dispersing the nano-aluminum powder in an organic solvent, and then adding N-( Trimethoxysilylpropyl) ethylenediaminetriacetic acid sodium salt, stirred and reacted at 60°C for 3-5 hours, then added ammonium chloride to it, continued to stir and reacte...

Embodiment 2

[0037] Embodiment 2 provides a kind of environment-friendly permeable concrete, is characterized in that, comprises the following components by weight: 23 parts of cement, 0.8 part of aluminum oxide nanotubes, N-(trimethoxysilylpropyl) ethylenediaminetriacetic acid 3 parts of ammonium salt modified nano-aluminum powder, 63 parts of coarse aggregate, 0.8 part of nanoporous hollow cage titanium oxide, 1.3 parts of porous polysaccharide microspheres, 0.2 part of sodium sulfonate-based hyperbranched poly(amine-ester), water 23 parts; The cement is slag portland cement.

[0038] The preparation method of the N-(trimethoxysilylpropyl) ammonium ethylenediamine triacetate modified nano-aluminum powder comprises the following steps: dispersing the nano-aluminum powder in an organic solvent, and then adding N-( Trimethoxysilylpropyl) ethylenediaminetriacetic acid sodium salt, stirred and reacted at 65°C for 3.5 hours, then added ammonium chloride therein, continued to stir and reacted f...

Embodiment 3

[0043] Embodiment 3 provides a kind of environment-friendly permeable concrete, is characterized in that, comprises the following components by weight: 25 parts of cement, 1 part of aluminum oxide nanotube, N-(trimethoxysilylpropyl) ethylenediaminetriacetic acid 3.5 parts of ammonium salt modified nano-aluminum powder, 65 parts of coarse aggregate, 1 part of nanoporous hollow cage titanium oxide, 1.5 parts of porous polysaccharide microspheres, 0.25 parts of sodium sulfonate-based hyperbranched poly(amine-ester), water 25 parts; Described cement is pozzolan Portland cement.

[0044] The preparation method of the N-(trimethoxysilylpropyl) ammonium ethylenediamine triacetate modified nano-aluminum powder comprises the following steps: dispersing the nano-aluminum powder in an organic solvent, and then adding N-( Trimethoxysilylpropyl) ethylenediaminetriacetic acid sodium salt, stirred and reacted at 70°C for 4 hours, then added ammonium chloride therein, continued to stir and re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses environment-friendly pervious concrete. The environment-friendly pervious concrete is characterized in that the environment-friendly pervious concrete comprises the following components in parts by weight: 20-30 parts of cement, 0.5 to 1.5 parts of aluminum oxide nanotubes, 2 to 5 parts of N-(trimethoxysilyl propyl) ethylenediamine triacetic acid ammonium salt modified nanoaluminum powder, 60 to 70 parts of rough aggregate, 0.5 to 1.5 parts of nano porous hollow cage-shaped titanium oxide, 1 to 2 parts of porous polysaccharide microspheres, 0.1 to 0.4 part of sodium sulfonate-based hyperbranched poly (amine-ester) and 20 to 30 parts of water. The invention further discloses a preparation method of the environment-friendly pervious concrete. The environment-friendlypervious concrete disclosed by the invention is excellent in mechanical property, good in fatigue resistance and water permeability, good in comprehensive performance, wear resistance and durability,and safe and environment-friendly to use.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an environment-friendly permeable concrete and a preparation method thereof. Background technique [0002] With the rapid development of our country's economy and the continuous acceleration of the pace of modern urban construction, the urban ground has gradually been covered by buildings and concrete pavement, rainwater cannot be infiltrated and collected, the land cannot breathe, and environmental problems are becoming more and more prominent. , has brought environmental impacts such as heat island effect and groundwater level drop to the city. Due to the impermeability of urban roads and the lack of drainage system functions, the phenomenon of urban waterlogging is increasing day by day. In severe cases, traffic paralysis is caused, and the safety of life and property is threatened. There are many cases of urban cars and people being flooded by heavy rain every summ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/08C04B38/08C04B111/40
CPCC04B28/04C04B28/08C04B38/08C04B2111/00017C04B2111/00284C04B2111/40C08G83/006C04B14/303C04B24/42C04B14/305C04B24/38C04B24/166C04B18/16
Inventor 韩昌龙
Owner 韩昌龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com