Deoxidizing agent packaging film and preparation method thereof

A technology of packaging film and deoxidizer, which is applied in the field of packaging materials, can solve the problems that the oxygen concentration in the packaging cannot be reduced to a safe range, the ratio of oxygen and carbon dioxide is unbalanced, and the quality and appearance of the product are affected, so as to save raw materials and maintain no deformation , Guarantee the effect of strength requirements

Pending Publication Date: 2020-11-13
KAIDA GRP CO LTD FJ
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, all deoxidizers use through-through, single-proof or multi-proof packaging materials. When this kind of deoxidizer is used in dry environment products, the moisture contained in the raw material of the deoxidizer will be easily absorbed by the dry environment and lost due to the air holes of the packaging materials. The performance of the deoxidizer will deteriorate, and the oxygen concentration in the package cannot be effectively reduced to a safe range
[0004] For products that have requirements on the appearance of the packaging container, the replacement type deoxidizer used in general packaging materials releases an unbalanced and unstable ratio of oxygen and carbon dioxide, which can easily lead to a negative pressure state in the packaging container; thus affecting product quality and appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Deoxidizing agent packaging film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A packaging film for a deoxidizer. The packaging film comprises oil-resistant and waterproof paper, and the opposite sides of the oil-resistant and waterproof paper are covered with a layer of perforated PE film and perforated PET film respectively.

[0031] The thickness of the perforated PE film in this embodiment is 25-50 μm, and the thickness of the perforated PET film is 10-15 μm.

[0032] The hole pitch of the perforated PE film in this embodiment is 0.1-2.5 mm.

[0033] This embodiment also provides a method for preparing a deoxidizer packaging film, comprising the following steps:

[0034] Step 1. Glue the oil-resistant and waterproof paper with a gluing mesh roller, dry it in an oven, and bond it to the PE film. Then corona treat the exposed surface of the PE film, and put it in a drying room for 24-48 hours. Made into semi-finished product I; corona treatment process: speed 100m / min, power 4200KW, test corona value> 38 dynes.

[0035] Step 2. Add a needle ro...

Embodiment 2

[0042] A packaging film for a deoxidizer. The packaging film comprises oil-resistant and waterproof paper, and the opposite sides of the oil-resistant and waterproof paper are covered with a layer of perforated PE film and perforated PET film respectively.

[0043] The thickness of the perforated PE film in this embodiment is 25-50 μm, and the thickness of the perforated PET film is 10-15 μm.

[0044] The hole pitch of the perforated PE film in this embodiment is 0.1-2.5 mm.

[0045] This embodiment also provides a method for preparing a deoxidizer packaging film, comprising the following steps:

[0046] Step 1. Glue the oil-resistant and waterproof paper with a gluing mesh roller, dry it in an oven, and bond it to the PE film. Then corona treat the exposed surface of the PE film, and put it in a drying room for 24-48 hours. Made into semi-finished product I; corona treatment process: speed 100m / min, power 4200KW, test corona value> 38 dynes.

[0047] Step 2. Add a needle ro...

Embodiment 3

[0054] A packaging film for a deoxidizer. The packaging film comprises oil-resistant and waterproof paper, and the opposite sides of the oil-resistant and waterproof paper are covered with a layer of perforated PE film and perforated PET film respectively.

[0055] The thickness of the perforated PE film in this embodiment is 25-50 μm, and the thickness of the perforated PET film is 10-15 μm.

[0056] The hole pitch of the perforated PE film in this embodiment is 0.1-2.5mm.

[0057] This embodiment also provides a method for preparing a deoxidizer packaging film, comprising the following steps:

[0058] Step 1. Glue the oil-resistant and waterproof paper with a gluing mesh roller, dry it in an oven, and bond it to the PE film. Then corona treat the exposed surface of the PE film, and put it in a drying room for 24-48 hours. Made into semi-finished product I; corona treatment process: speed 100m / min, power 4200KW, test corona value> 38 dynes.

[0059] Step 2. Add a needle rol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Hole spacingaaaaaaaaaa
Login to View More

Abstract

The invention discloses a deoxidizing agent packaging film and a preparation method thereof. The deoxidizing agent packaging film comprises oil-resistant waterproof paper, and the two opposite sides of the oil-resistant waterproof paper are coated with a layer of perforated PE film and a layer of perforated PET film respectively. The thickness of the perforated PE film is 25-50 [mu] m, and the thickness of the perforated PET film is 10-15 [mu] m. The perforated holes in the step 2 and the step 3 do not break through the oil-resistant waterproof paper so that the powder leakage phenomenon of the deoxidizing agent package is avoided, the package can be in direct contact with inclusions, and no dust leaks out. Meanwhile, the oil-resistant waterproof paper can prevent moisture and oil in the inclusions from eroding the deoxidizing agent, and potential safety hazards and hazards such as inclusion pollution caused by leakage of the deoxidizing agent are avoided. The deoxidizing agent packaging film is simple in preparation process and structure, convenient to use, good in transparency and particularly suitable for deoxidizing agent packaging containing indication marks.

Description

technical field [0001] The invention relates to the technical field of packaging materials, in particular to a deoxidizer packaging film and a preparation method thereof. Background technique [0002] Deoxygenation packaging (FOA) refers to the use of a deoxidizer that can chemically react with oxygen or catalyze oxygen in a sealed packaging container to remove free oxygen in the packaging container, so that the packaged objects can be stored at a high oxygen concentration. Low (oxygen < 0.1%), even an oxygen-free state of preservation of a technology. [0003] Packaging materials used for deoxygenation packaging are required to have good airtightness, especially high barrier properties to oxygen, and the specific requirement is that the permeability to oxygen is less than 20mL / (m2·24h·0.1MPa, at 20°C) . The packaging material or container should preferably have a certain strength to avoid unattractive appearance caused by shrinkage caused by negative pressure. At pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/32B32B27/10B32B29/06B32B27/36B32B3/24B32B7/12B32B7/02B32B7/022B32B7/023B32B33/00B32B37/12B32B38/16B32B38/04B32B38/00B65D65/40
CPCB32B27/32B32B27/10B32B29/06B32B27/36B32B3/266B32B7/12B32B7/02B32B7/022B32B7/023B32B33/00B32B37/1284B32B38/164B32B38/04B32B38/0008B65D65/40B32B2307/724B32B2307/7265B32B2307/558B32B2307/5825B32B2307/412B32B2553/00
Inventor 吕江鹏
Owner KAIDA GRP CO LTD FJ
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com