A kind of anti-aging PC sunshine board and preparation method thereof

A technology of sunlight board and aging resistance, applied in chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problems of short service life, yellowing and aging of sunlight boards, etc. The effect of aging resistance, enhanced UV resistance, and enhanced stability

Active Publication Date: 2022-04-19
无锡希尔丽塑胶板材有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned related technologies, the inventors found that PC polycarbonate solar panels are prone to yellowing and aging in areas with high humidity and heat, especially in Hainan and Fujian, where the ultraviolet rays are strong and rainy, and the overall service life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-aging PC sunshine board and preparation method thereof
  • A kind of anti-aging PC sunshine board and preparation method thereof
  • A kind of anti-aging PC sunshine board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1- Embodiment 6

[0053] The preparation methods of the PC solar panels in Example 1-Example 6 are all the same, the only difference is that the types and dosages of the raw material components in the main material layer are different, see Table 2 for details:

[0054] Table 2, the type and dosage of raw material components in the main material layer

[0055]

[0056] The hydrophobic agent in Example 1-Example 6 includes polyvinyl fluoride and ethylene-tetrafluoroethylene copolymer in a weight ratio of 1.3:2.5.

[0057] The thickness of anti-ultraviolet layer in embodiment 1-embodiment 6 is 50 μ m, the raw material of anti-ultraviolet layer in embodiment 1-embodiment 3 is phenyl o-hydroxybenzoate, the thickness of anti-ultraviolet layer in embodiment 4-embodiment 6 The starting material is 2-hydroxy-4-n-octyloxybenzophenone.

[0058]Taking Example 5 as an example to illustrate the preparation method of PC solar panels, it may further comprise the steps:

[0059] S1. According to the propor...

Embodiment 7

[0062] The difference between this embodiment and embodiment 5 is that the hydrophobic agent includes polyvinyl fluoride and ethylene-tetrafluoroethylene copolymer in a weight ratio of 1:2.

Embodiment 8

[0064] The difference between this embodiment and embodiment 5 is that the hydrophobic agent includes polyvinyl fluoride and ethylene-tetrafluoroethylene copolymer in a weight ratio of 1.5:2.7.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of PC solar panels, and specifically discloses an aging-resistant PC solar panel and a preparation method thereof. The anti-aging PC sunlight board includes a main material layer, an anti-ultraviolet layer covering the upper surface and the lower surface of the main material layer; the main material layer is made of the following raw materials by weight: polycarbonate; organic montmorillonite; hydrophobic agent; Oxygen agent; its preparation method is: mix the raw material components in the main material layer uniformly to form a primary mixture; put the primary mixture and the anti-ultraviolet layer raw materials into the extruder for high temperature melting, and adopt the co-extrusion process to melt the melted anti-ultraviolet The raw materials of the ultraviolet layer cover the upper surface and the lower surface of the primary board formed by extruding the primary mixture, and after cooling, the final product is obtained. The aging-resistant PC solar panel of the present invention has better aging resistance; in addition, the preparation method of the present invention has a simple manufacturing process, and at the same time can ensure that the obtained PC solar panel has the advantages of better aging resistance.

Description

technical field [0001] The invention relates to the field of PC solar panels, more specifically, it relates to an aging-resistant PC solar panel and a preparation method thereof. Background technique [0002] Polycarbonate (PC) is an important thermoplastic engineering plastic developed in the late 1950s. It has excellent and balanced mechanical, thermal and electrical properties, especially the impact strength is the crown of general thermoplastics, and is widely used in the production of various Sunshine panels and endurance panels can be used to make carports, balcony canopies and greenhouse lighting carports. [0003] The existing Chinese patent application publication number CN108047681A discloses a PC polycarbonate solar panel capable of sound and heat insulation. 10-18 parts of ether sulfone, 2-5 parts of formaldehyde scavenger, 30-40 parts of melamine resin, 1-2 parts of plasticizer, 1-2 parts of dispersant, 0.5-1 part of antioxidant, 0.5-1 part of modifier share. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08B32B27/20B32B27/28B32B27/36C08J5/18C08L69/00C08L27/12C08L23/08C08K13/02C08K3/34C08K5/134C08K5/132B29C48/07B29C48/92
CPCB32B27/08B32B27/20B32B27/365B32B27/28C08J5/18B29C48/07B29C48/92B32B2250/24B32B2307/552B32B2307/54B32B2307/71B29C2948/92704
Inventor 唐德云
Owner 无锡希尔丽塑胶板材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com