A kind of polysiloxane and its application

A technology of polysiloxane and organosiloxane, applied in the direction of coating, etc., can solve the problems of continuous industrial production and low hardness, high energy consumption, long curing time, etc., and achieve excellent anti-fog effect, good water resistance, The effect of high bonding strength

Active Publication Date: 2021-11-05
武汉中科先进材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Transparent organosiloxane polymers are used for anti-fog on the surface of various transparent glass and plastic materials, such as optical lenses, goggles, face shields, helmet panels, automotive parts, etc., but they are in the form of heat curing and require long curing Time and high energy consumption, low production efficiency, not suitable for continuous industrial production and low hardness and poor scratch resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polysiloxane and its application
  • A kind of polysiloxane and its application
  • A kind of polysiloxane and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The preparation of embodiment 1 anti-fog coating

[0040](a) Preparation of semi-blocked isocyanate prepolymer: add 133.38g (0.6mol) isophorone diisocyanate IPDI and 0.2g (0.1wt%) dibutyltin dilaurate DBTDL in the three-neck flask of 500mL and start stirring; Sequentially weigh 0.5394g (0.262wt%) p-hydroxyanisole MEHQ, 1.0788g (0.525wt%) 2,6-di-tert-butyl-4-methylphenol BHT and 70.05g (0.602mol) hydroxyethyl acrylate HEA, mixed well until completely dissolved, transferred to a constant pressure dropping funnel, and slowly added dropwise to the above-mentioned three-necked flask at room temperature (the reaction is violently exothermic, control the dropping speed to avoid local overheating), after dropping, continue to react at room temperature for 30 minutes , heat up to 70°C and react until the content of the isocyanate group (-NCO) of the mixture reaches the theoretical value (measured by the di-n-butylamine hydrochloride method), then cool down to obtain a semi-block...

Embodiment 2

[0047] The preparation of embodiment 2 anti-fog coating

[0048] (a) Preparation of semi-blocked isocyanate prepolymer: add 266.76g (1.2mol) isophorone diisocyanate IPDI and 0.4g (0.1wt%) dibutyltin dilaurate DBTDL in the three-necked flask of 500mL and start stirring; Weigh in turn 1.0788g (0.262wt%) p-hydroxyanisole MEHQ, 2.1576g (0.525wt%) 2,6-di-tert-butyl-4-methylphenol BHT and 140.1g (1.204mol) hydroxyethyl acrylate HEA, mixed well until completely dissolved, transferred to a constant pressure dropping funnel, and slowly added dropwise to the above-mentioned three-necked flask at room temperature (the reaction is violently exothermic, control the dropping speed to avoid local overheating), after dropping, continue to react at room temperature for 30 minutes , heat up to 70°C and react until the content of the isocyanate group (-NCO) of the mixture reaches the theoretical value (measured by the di-n-butylamine hydrochloride method), then cool down to obtain a semi-blocked...

Embodiment 3

[0055] The preparation of embodiment 3 anti-fog coating

[0056] (a) Preparation of semi-blocked isocyanate prepolymer: add 266.76g (1.2mol) isophorone diisocyanate IPDI and 0.4g (0.1wt%) dibutyltin dilaurate DBTDL in the three-necked flask of 500mL and start stirring; Weigh in turn 1.0788g (0.262wt%) p-hydroxyanisole MEHQ, 2.1576g (0.525wt%) 2,6-di-tert-butyl-4-methylphenol BHT and 140.1g (1.204mol) hydroxyethyl acrylate HEA, mixed well until completely dissolved, transferred to a constant pressure dropping funnel, and slowly added dropwise to the above-mentioned three-necked flask at room temperature (the reaction is violently exothermic, control the dropping speed to avoid local overheating), after dropping, continue to react at room temperature for 30 minutes , heat up to 70°C and react until the content of the isocyanate group (-NCO) of the mixture reaches the theoretical value (measured by the di-n-butylamine hydrochloride method), then cool down to obtain a semi-blocked...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Functional group degreeaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polysiloxane and an application thereof. The polysiloxane is formed by reacting a semi-closed isocyanate prepolymer and an organic polymer silanol. The polysiloxane itself has an anti-fog function, and applying the polysiloxane to the anti-fog coating can realize UV ​​curing and increase the hardness of the coating.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to polysiloxane and its application. Background technique [0002] Highly transparent materials are indispensable materials in our daily production, but they are prone to fogging during use, which reduces the light transmittance on the surface of the material, affects the line of sight, brings a lot of inconvenience to life, and even causes serious harm . In recent years, anti-fog technology has gradually attracted people's attention. The research and development of hydrophilic anti-fog coatings has made the fastest progress, and a series of advanced technologies and relatively mature products have been formed. Hydrophilic anti-fog coating is a functional material. It is a chemical product with anti-fog function formulated with a polymer material with a hydrophilic group as the main component, and a corresponding proportion of other additives and organic solvents. , i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G77/388C09D183/12C09D183/04C09D7/65C08J7/054C08G77/46C08G77/26C08G18/10C08G18/79C08L67/02
CPCC08G18/10C08G18/792C08G18/794C08G77/26C08G77/388C08G77/46C08J2367/02C08J2483/04C08J2483/12C08K2201/014C09D183/04C09D183/12C09D7/63C09D7/65C08J7/054C08L71/02C08K5/42
Inventor 喻学锋康翼鸿杨新耕边式
Owner 武汉中科先进材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com