Production method for aluminized steel plate plating material aluminum-silicon alloy

A technology of aluminum-magnesium alloy and silicon alloy materials, which is applied in the field of aluminum-silicon alloy materials for coating aluminum-plated steel sheets, can solve the problems of split metal structure, decline in material mechanical properties, and uneven pits and pits, so as to reduce surface tension, The effect of prolonged modification time and grain refinement

Inactive Publication Date: 2020-10-27
JIANGSU LINLONG NEW MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, if the aluminum-silicon alloy exists in a liquid state and has not been modified, there are α and β phases in the alloy liquid. When it cools, the liquid begins to shrink, pits appear on the surface, and the silicon phase is a coarse sheet structure. Therefore, it is also called primary crystal silicon, which splits the metal structure and reduces the mechanical properties of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for aluminized steel plate plating material aluminum-silicon alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] The hot-dip aluminum-silicon alloy material provided by the invention mainly contains Si: 6-13%; RE: 0.02-0.3%; Ti: 0.02-0.5%; B: 0.01-0.25%, and the balance is Al and unavoidable impurities (such as Fe) content. In order to describe the technical solution of the present invention to those skilled in the art, the numerical values ​​listed in Table 1 below are the specific numerical values ​​of some preferred embodiments that have been selected and achieved better technical effects within the protection scope of the present invention. However, the content of each component of the present invention is not limited to the numerical values ​​listed in Table 1. For those skilled in the art, they can be reasonably summarized and deduced on the basis of the numerical range listed in Table 1.

[0038] Table 1: The mass percentage (%) of each component in the total weight

[0039] Si RE Ti B Al Impurities (Fe, etc.) 11.0 0.1 0.15 0.038 margin ≤0.03 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel hot dip aluminum-silicon alloy material and a production method thereof. The material mainly contains 6 to 13 percent of Si, 0.02 to 0.3 percent of RE, 0.02 to 0.5 percent of Ti, 0.01 to 0.25 percent of B and the balance of Al and inevitable impurities. The invention further discloses the production method for preparing the material.

Description

technical field [0001] The invention relates to an aluminum-silicon alloy material for coating an aluminum-coated steel sheet, in particular to a production method for an aluminum-silicon alloy coating material for a hot-dip aluminum-coated steel sheet. Background technique [0002] In addition to galvanizing, most of the hot-dip steel sheets, steel strips, and wires use zinc-aluminum-silicon alloys, and there are also a small amount of tin-plated materials. Recently, because the corrosion resistance of pure aluminum is higher than that of pure zinc, but the mechanical properties of pure aluminum are low, other elements must be added, such as copper, iron and other elements to improve the mechanical strength of aluminum alloy materials, but some elements make aluminum alloy materials hard and flaky. Brittle, high melting point, if used as a hot-dip alloy material, there are great difficulties in the hot-dip production process. [0003] In order to solve the above problems, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/04C22C1/03C22C1/06C23C2/12C23C2/40
CPCC22C1/026C22C1/03C22C1/06C22C21/04C23C2/12C23C2/40
Inventor 冯立新严锦山魏小昕
Owner JIANGSU LINLONG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com