Iron phosphotungstate flame-retardant smoke-suppressing semi-hard PVC sheet and preparation method thereof

A phosphotungstic acid and semi-rigid technology, which is applied in the field of iron phosphotungstic acid flame retardant and smoke-suppressing semi-rigid PVC sheet and its preparation, can solve the problem of life-threatening and property safety, and the smoke suppressing effect of inorganic flame retardants is not obvious. and other problems, to achieve the effect of improving product quality, facilitating promotion and application, and high yield

Inactive Publication Date: 2020-08-18
安徽奥凯材料股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, antimony-based, tin-based, boron-based, etc. are mostly used as auxiliary flame retardants, while metal hydroxides are generally used as flame-retardant fillers, which require a large amount of filling to exert the flame-retardant effect, and the smoke suppression effect of these inorganic flame retardants is not good. Obviously, PVC materials will still produce a lot of smoke during the combustion process, threatening people's lives and property safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] This example is to prepare a semi-rigid PVC sheet made of iron phosphotungstate for flame retardancy and smoke suppression. Specific steps are as follows:

[0032] (1) Heating and stirring: Take 100 parts by weight of PVC resin powder, 2 parts of rare earth composite heat stabilizer, 0.2 part of lubricant polyethylene wax, 15 parts of plasticizer dioctyl phthalate, iron phosphotungstate 2 parts of flame suppressant; first put in PVC resin powder, let the PVC resin take off the water first, and at the same time open the skin pores on the surface, add stabilizer and plasticizer at this time to achieve better absorption effect; then add stabilizer and Plasticizer, after the plasticizer fully swells PVC, add lubricant and flame retardant and smoke suppressant on this basis; it can make them easier to attach to PVC particles. The heating and stirring is that after the PVC resin powder is added into the high-speed mixer, it starts to stir while heating, the heating rate is 1...

Embodiment 2

[0037] This example also prepares a semi-rigid PVC sheet with iron phosphotungstate for flame retardancy and smoke suppression. The steps are the same as in Example 1, except that the components of the PVC sheet prepared in this example include by weight: 100 parts of PVC resin powder, 3 parts of rare earth composite heat stabilizer, and 0.4 part of lubricant polyethylene wax , 13 parts of plasticizer dioctyl phthalate, 6 parts of ferric phosphotungstate flame retardant and smoke suppressant.

Embodiment 3

[0039]This example is also to prepare a semi-rigid PVC sheet of iron phosphotungstate flame retardant and smoke suppression. Its steps are also the same as in Example 1. Each component of the PVC sheet prepared in this embodiment comprises by weight: 100 parts of PVC resin powder, 4 parts of rare earth composite heat stabilizer, 0.6 part of lubricant polyethylene wax, plasticizer dioctyl phthalate 11 parts, 8 parts of ferric phosphotungstate flame retardant and smoke suppressant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an iron phosphotungstate flame-retardant smoke-suppressing semi-hard PVC sheet and a preparation method thereof. The PVC sheet comprises the following components: PVC resin powder, a stabilizer, a lubricant, a plasticizer and a flame-retardant smoke-suppressing agent. The flame-retardant smoke suppressant is a compound containing four elements of iron, phosphorus, tungstenand oxygen, wherein the phosphorus element can be used as a gas source and an acid source of the intumescent flame retardant, and has a remarkable flame retardant effect; the iron and tungsten can react with HCl to form strong Lewis acid, and trans-conjugated polyene, hydrogen chloride and chloride are generated through catalytic reaction, so that a smoke suppression effect is achieved; and meanwhile, the tungsten element also has a promoting effect on the flame-retardant effect of nitrogen and phosphorus, so that the problem that the personal safety is endangered due to the fact that a largeamount of harmful smoke is generated during combustion of the PVC sheet is solved; therefore, the application range of the PVC sheet is widened, and further popularization and application of the PVC sheet in the field of buildings are facilitated.

Description

technical field [0001] The invention relates to a flame-retardant and smoke-suppressing semi-rigid PVC sheet made of ferric phosphotungstate and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is one of the five major synthetic thermoplastics, and has become the second largest general-purpose plastic in the world after polyethylene, and PVC is mainly hard products. Therefore, PVC sheets are widely used in furniture, building materials, and decoration industries, and are developing at a relatively fast speed. However, PVC sheets will produce a lot of smoke during the combustion process, which will cause greater casualties in the event of a fire, which limits its application in building materials and decorative materials. Therefore, improving the flame retardancy and smoke suppression of PVC sheets is the development of PVC sheets. It is the key to application and helps to promote its application in related industries. [0003] At present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/06C08K13/02C08K3/32C08K5/12C08J5/18
CPCC08J5/18C08J2327/06C08J2423/06C08L27/06C08L2201/02C08L23/06C08K13/02C08K3/32C08K5/12
Inventor 马青赛朱山宝陈绪煌
Owner 安徽奥凯材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com