A kind of tial alloy with low temperature superplasticity and its component preparation method

A superplastic and alloy technology, applied in metal rolling and other directions, can solve the problems of harsh deformation process, easy cracking, high mold requirements, etc., achieve the effect of low equipment requirements, small grain size, and superplastic forming

Active Publication Date: 2021-07-13
SHANGHAI SPACE PRECISION MACHINERY RES INST
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical solution problem of the present invention is: to overcome the deficiencies in the prior art, propose a kind of TiAl alloy with low-temperature superplasticity and its component preparation method, the purpose is to solve existing method to prepare components such as TiAl alloy corrugated plate, spherical shape, honeycomb shape There are problems such as easy cracking, harsh deformation process, high mold requirements, etc., to provide a TiAl alloy with low temperature superplasticity and its component preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment is a method for preparing a TiAl alloy with low-temperature superplasticity and its components, which is specifically carried out according to the following steps:

[0026] A. Preparation of TiAl alloy slab: Ti-43Al-2Cr-2Nb-0.3La (at.%) alloy with an average grain size of 20 μm was prepared by pre-alloyed powder + hot isostatic pressing method.

[0027] B. TiAl alloy sheathed rolling: put the above-mentioned TiAl alloy sealed with stainless steel into a furnace with a heating temperature of 1150 ° C for 40 minutes, adopt a rolling speed of 30 ± 5 mm / s, and the pass deformation is 22 ± 3% , Each pass is rolled back to the furnace with a heat preservation time of 3-5 minutes.

[0028] C. Heat treatment of the TiAl alloy plate: put the TiAl alloy plate obtained above with a sheath in a furnace with a furnace temperature of 1120° C. for 120 min. The sheath is removed to obtain a TiAl alloy plate, and a TiAl alloy plate with a thickness of about 2±0.1mm is o...

Embodiment 2

[0033] This embodiment is a method for preparing a TiAl alloy with low-temperature superplasticity and its components, which is specifically carried out according to the following steps:

[0034] A. Preparation of TiAl alloy slab: Ti-42Al-2Nb-4Mn-0.2C (at.%) alloy with an average grain size of about 80 μm was prepared by vacuum arc melting.

[0035] B. TiAl alloy sheathed rolling: put the above-mentioned TiAl alloy sealed with stainless steel in a furnace with a heating temperature of 1120°C for 60 minutes, adopt a rolling speed of 20±5mm / s, and the deformation of each pass is 20±2% , and the heat preservation time for each pass is 5±2min.

[0036]C. Heat treatment of the TiAl alloy plate: put the TiAl alloy plate obtained above with a sheath in a furnace with a furnace temperature of 950° C. for 180 min. The sheath is removed to obtain a TiAl alloy sheet with a thickness of about 1.8±0.2 mm.

[0037] D. Superplastic forming of TiAl alloy sheet: Put the TiAl alloy coated wit...

Embodiment 3

[0040] This embodiment is a method for preparing a TiAl alloy with low-temperature superplasticity and its components, which is specifically carried out according to the following steps:

[0041] A. Preparation of TiAl alloy slab: Ti-44Al-2Cr-2Mn-0.5Mo-0.3C (at.%) alloy with an average grain size of about 50 μm was prepared by plasma beam cooling furnace melting method.

[0042] B. TiAl alloy sheath rolling: put the above-mentioned TiAl alloy sealed with stainless steel into a furnace with a heating temperature of 1180 ° C for 60 minutes, adopt a rolling speed of 25 ± 5 mm / s, and the deformation of each pass is 20%. The heat preservation time for each pass return to the furnace is 5±3min.

[0043] C. Heat treatment of the TiAl alloy plate: Put the TiAl alloy plate obtained above with a sheath in a furnace with a furnace temperature of 1160° C. for 120 minutes. The sheath is removed to obtain a TiAl alloy sheet with a thickness of about 2.1 mm.

[0044] D. Superplastic formin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a TiAl alloy with low-temperature superplasticity and a method for preparing a component thereof, belonging to the technical field of preparation of titanium-aluminum alloy components. TiAl alloy slabs are prepared by powder metallurgy or ingot metallurgy, and TiAl alloy slabs are sheathed and rolled near the eutectoid temperature, and then heat treated near the eutectoid temperature to prepare TiAl alloy sheets with a nearly equiaxed structure, and then combined with After the forming die is assembled, it is subjected to low temperature superplastic deformation as a whole, followed by stress relief annealing to prepare TiAl alloy components. The reduced Al content in the TiAl alloy designed by the invention can ensure that the TiAl alloy can be formed at a lower temperature, and meanwhile the prepared TiAl alloy has a fine grain size. Then keep warm near the eutectoid temperature to further obtain a fine and uniform equiaxed structure with a high content of γ phase, which ensures the effective progress of low-temperature superplastic forming. The invention has simple process and low equipment requirements, and can realize superplastic forming of TiAl alloy at low temperature.

Description

technical field [0001] The invention relates to a TiAl alloy with low-temperature superplasticity and a preparation method for its component, belonging to the technical field of titanium alloy component preparation. Background technique [0002] TiA1 alloy has high specific strength, high specific stiffness, low density, good flame retardancy, high temperature oxidation resistance and creep resistance, and has broad application prospects in aerospace, automobile manufacturing and other industrial fields. In addition to being directly used as structural materials, TiAl alloy sheets can also be used for parts of near-net-shape aviation and aerospace engines, as well as wings, shells, hot zone skins, turbine blades, and missile tails of ultra-high-speed aircraft. However, TiAl has poor deformation ability, and it is difficult to prepare components with complex shapes or large sizes, such as aircraft shells and turbine blades, by traditional methods. The use of superplastic for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C14/00C22C30/00C22F1/18B21B1/38B21D13/02
CPCB21B1/38B21B2001/386B21D13/02C22C14/00C22C30/00C22F1/183
Inventor 周海涛肖旅徐玉棱孙京丽陈舸
Owner SHANGHAI SPACE PRECISION MACHINERY RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products