A kind of antibacterial and antistatic foamed elastomer material and preparation method thereof

An elastomer material, anti-static technology, applied in the field of foamed elastic materials, can solve the problems of bacteria breeding, EVA foam material does not have conductivity, affect the appearance and performance of the material, and achieve excellent antibacterial effect

Active Publication Date: 2022-05-03
QINGDAO UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the foamed elastomer made of ethylene-vinyl acetate copolymer (EVA), due to the presence of various microorganisms in its use environment, can easily cause bacteria to grow on the surface or inside of the EVA foam, seriously affecting the appearance and performance of the material; and EVA foam The material itself is not conductive, and the surface is easy to accumulate static electricity, which seriously affects the use
Usually the liquid antistatic agent added to EVA foam or the antibacterial agent sprayed on the surface has poor dispersion and poor long-term effect; ordinary solid conductive agent usually uses superconducting carbon black, which cannot be used for light-colored EVA products, and quaternary phosphonium salt modified Antimony tin oxide can be used to prepare antibacterial, antistatic, light-colored polymer materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial and antistatic foamed elastomer material and preparation method thereof
  • A kind of antibacterial and antistatic foamed elastomer material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The embodiment of the present invention provides a preparation method of an antibacterial quaternary phosphonium salt modified tin antimony oxide conductive filler and a hybrid EVA foamed elastomer thereof. It includes the following steps:

[0021] (1) Weigh 15g of nano-antimony tin oxide, heat at 60°C for 4 hours, dry, and grind to obtain antimony tin oxide powder (average particle size 0.05 μm);

[0022] (2) Mix 100g of dodecyloxymethyltributylphosphorous chloride and 0.15g of polyvinyl alcohol into an aqueous solution with a concentration of quaternary phosphonium salt of 4mg / mL, and place tin antimony oxide in it to absorb to saturation (quaternary phosphonium Salt is kept in excess), filtered, heated at 60°C for 4 hours, dried, and ground to obtain quaternary phosphonium salt modified tin antimony oxide conductive filler;

[0023] (3) Then add a solution of 1.5 g of vinyl triperoxy-tert-butylsilane and 30 g of ethanol (the mass ratio of silane to quaternary phosph...

Embodiment 2

[0027] The embodiment of the present invention provides a preparation method of an antibacterial quaternary phosphonium salt modified tin antimony oxide conductive filler and a hybrid EVA foamed elastomer thereof. It includes the following steps:

[0028] (1) Weigh 15g of nano-antimony tin oxide, heat and dry at 60°C for 4 hours, and obtain tin antimony oxide powder after grinding;

[0029] (2) Weigh 100g of tetradecyltributylphosphorus chloride and 0.25g of polyvinyl alcohol to prepare an aqueous solution with a concentration of quaternary phosphonium salt of 4mg / mL, and place tin antimony oxide in it to absorb to saturation (quaternary phosphonium salt keeps Excessive amount), after filtering, fully wash with deionized water, heat at 60°C for 4 hours, dry, and grind to obtain quaternary phosphonium salt modified tin antimony oxide conductive filler;

[0030] (3) Then add a solution mixed with 1.5g of titanate coupling agent and 30g of ethanol (the mass ratio of titanate to ...

Embodiment 3

[0034] The embodiment of the present invention provides a preparation method of an antibacterial quaternary phosphonium salt modified tin antimony oxide conductive filler and a hybrid EVA foamed elastomer thereof. It includes the following steps:

[0035] (1) Weigh 15g of nano-antimony tin oxide, heat and dry at 60°C for 4 hours, and obtain tin antimony oxide powder after grinding;

[0036] (2) According to the mass ratio of polyquaternary phosphonium salt / polyvinyl alcohol = 100 / 0.45, prepare an aqueous solution of polyquaternary phosphonium salt with a concentration of 6 mg / mL, and place tin antimony oxide in it to absorb to saturation (keep the excess of quaternary phosphonium salt) , after filtering, fully wash with deionized water, heat and dry at 60°C for 4 hours, and grind to obtain polyquaternary phosphonium salt modified tin antimony oxide conductive filler;

[0037] (3) Then add the solution mixed with aluminate coupling agent / ethanol=5 / 100 mass ratio (the mass rati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides an antibacterial and antistatic foamed elastomer material and a preparation method thereof, belonging to the technical field of foamed elastic materials. The preparation method comprises: placing tin antimony oxide particles in a quaternary phosphonium salt solution to absorb to saturation, drying and grinding after washing to obtain quaternary phosphonium salt modified tin antimony oxide; The coupling agent is modified, and then mixed with the modified polymer blend, foaming agent, cross-linking agent and modified compounding agent to obtain a rubber compound; the above-mentioned rubber compound is foamed, cross-linked and shaped to obtain an antibacterial Antistatic foam elastomer material. The foamed elastomer prepared by the present invention not only has antistatic properties, but also has excellent antibacterial effect, and can effectively destroy bacteria in the environment where EVA is used; secondly, the quaternary phosphonium salt doped tin antimony oxide is modified by a coupling agent, It can be evenly dispersed in the EVA matrix, has permanent antibacterial and antistatic effects, and can be used as packaging materials, shoe materials and other products.

Description

technical field [0001] The invention relates to the technical field of foamed elastic materials, in particular to an antibacterial and antistatic foamed elastic material and a preparation method thereof. Background technique [0002] In packaging or wearing materials in food, medicine, clothing and other industries, antibacterial and antistatic are two very critical but difficult properties to have at the same time. For example, the foamed elastomer made of ethylene-vinyl acetate copolymer (EVA), due to the presence of various microorganisms in its use environment, can easily cause bacteria to grow on the surface or inside of the EVA foam, seriously affecting the appearance and performance of the material; and EVA foam The material itself is not conductive, and the surface is easy to accumulate static electricity, which seriously affects the use. The liquid antistatic agent added to the EVA foam or the antibacterial agent sprayed on the surface is poorly dispersed and has p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L7/00C08L9/06C08L23/06C08K13/06C08K9/04C08K9/06C08K3/22C08K7/26C08K5/14C08K5/09C08K3/26C08J9/10
CPCC08J9/103C08J9/105C08J9/009C08J9/0066C08J9/0061C08J9/0023C08J2323/08C08J2423/08C08J2407/00C08J2409/06C08J2423/06C08K13/06C08K9/04C08K9/08C08K9/06C08K2003/2231C08K3/2279C08K7/26C08K5/14C08K2003/2296C08K5/09C08K2003/265C08J2203/04C08K2201/017
Inventor 翟俊学翟晋葶李想王琳肖建斌赵树高
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com