Method for sintering building spoil into foamed ceramic

A technology for building spoil and ceramics, which is applied in the direction of ceramic products, ceramic material production, clay products, etc., can solve the problem of building spoils not being properly handled and so on.

Active Publication Date: 2020-05-12
TONGJI UNIV
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for sintering building spoils to foam ceramics in order to solve the above problems, to solve the problem that the building spoils in the prior art have not been properly handled, and to process the difficult-to-use building spoils and Compounding, so that it can be used as a raw material for sintered foamed ceramics, and at the same time improve the performance of traditional foamed ceramics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for sintering building spoil into foamed ceramic
  • Method for sintering building spoil into foamed ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0078] The construction spoil is excavated with earth and stone, and the spoil is blended with fly ash.

[0079] Follow the steps below to implement:

[0080] Collect earthwork excavation spoil, put earthwork excavation spoil into mobile crusher, crush it, pass through 6-mesh sieve, and screen to obtain construction spoil raw materials with a particle size not greater than 3.35mm. Add fly ash to the earth and stone excavation spoil, by weight, take 50 parts of earth and stone excavation spoil particles, 25 parts of fly ash, put the raw materials into a horizontal ribbon mixer, and stir for 20 minutes to obtain sintered bone material.

[0081] In parts by weight, 80 parts of the above sintered aggregate, 5 parts of animal hoof horn foaming agent, 5 parts of sodium bentonite, 5 parts of ordinary silicate glass shards and 60 parts of tap water are taken. Put the above-mentioned materials weighed into a ball mill, ball mill for 1 hour, add water to refine the mud, and inject it ...

Embodiment 2

[0088] The construction spoil is made of muddy construction spoil and prepared with diatomaceous earth.

[0089] Follow the steps below to implement:

[0090] Collect the silty construction spoil, and stack the silty construction spoil for 15 days, pass through a 6-mesh sieve, and screen to obtain construction spoil raw materials with a particle size not greater than 3.35mm. Add diatomite to the silty construction spoil, by weight, take 70 parts of earthwork excavation spoil particles, 25 parts of diatomite, put the raw materials into a horizontal ribbon mixer, and stir for 20 minutes to obtain sintered bone material.

[0091]In parts by weight, 80 parts of the above-mentioned sintered aggregate, 7 parts of animal hoof horn foaming agent, 7 parts of sodium bentonite, 7 parts of ordinary silicate glass shards and 20 parts of tap water are taken. Put the above-mentioned materials weighed into a ball mill, ball mill for 1 hour, add water to refine the mud, and inject it into a ...

Embodiment 3

[0098] For construction spoil, earthwork excavation spoil and silty construction spoil can be used in a mixed ratio of 1:1, without compounding.

[0099] Follow the steps below to implement:

[0100] Collect earth and stone excavation spoil, put the earth and stone excavation spoil into the mobile crusher, and crush it; collect muddy construction spoil, and pile up muddy construction spoil for 15 days. Pass the preliminarily treated construction spoil through a 6-mesh sieve to obtain construction spoil raw materials with a particle size not greater than 3.35mm.

[0101] In terms of parts by weight, 35 parts of excavation spoil for earth and stone; 35 parts of muddy construction spoil; 5 parts of animal hoof horn foaming agent; 7 parts of sodium bentonite; 5 parts of ordinary silicate glass fragments; 40 parts of tap water. Put the above-mentioned materials weighed into a ball mill, ball mill for 1 hour, add water to refine the mud, and inject it into a mold with a size of 100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for sintering building spoil into foamed ceramic. The method comprises the following steps: (1) collecting the building spoil, and treating the building spoil so as to prepare sintered aggregate; (2) preparing materials according to the following formula: 70-80 parts of the sintered aggregate, 5-7 parts of an animal foaming agent, 5-7 parts of bentonite, 5-7 partsof glass fragments and 20-60 parts of water; (3) putting the components in the step (2) into a ball mill for ball milling, adding water for pugging, injecting an obtained material into a mold, carrying out pressure molding, and carrying out demolding so as to obtain a green body; and (4) drying the green body so as to obtain a dried green body, then placing the dried green body into a muffle furnace, and carrying out sintering so as to prepare the foamed ceramic. Compared with the prior art, the method provided by the invention has the following advantages: the building spoil which is difficult to be utilized is treated and compounded, so the building spoil can be used as a raw material for sintering the foamed ceramic; meanwhile, the performance of traditional foamed ceramic is improved.

Description

technical field [0001] The invention belongs to the field of special materials for construction engineering, and in particular relates to a method for sintering foamed ceramics from construction waste soil. Background technique [0002] Construction waste includes construction waste and construction spoil. Construction spoils mainly refer to the spoils and silt excavated by earth and rock in new construction and reconstruction projects in cities. Domestic construction waste accounts for 30% to 40% of the total urban waste every year. Therefore, the total amount of construction waste is huge, and the amount of these construction wastes is Arbitrary disposal not only occupies land resources, but also causes serious pollution and damage to water, air and soil. At present, almost no construction spoils have been properly treated, and the total utilization rate of construction wastes is less than 5%. The main reason is that the construction spoils are of poor quality and difficu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/132C04B33/13C04B38/02
CPCC04B33/1305C04B33/132C04B33/1352C04B38/02C04B2235/3418C04B2235/36C04B2235/66C04B2235/77C04B2235/96C04B2235/9607C04B38/0067C04B38/0074Y02P40/60
Inventor 肖建庄胡晓龙马志鸣
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com