Preparation method of high bonding force coating taking anodic alumina as base material
An anodized aluminum, anodic oxidation technology, applied in the direction of coating, surface reaction electrolytic coating, electrolytic coating, etc., can solve the problems of unfavorable electroplating process, undisclosed etching method, non-uniform corrosion, etc., and achieve simple and easy positioning corrosion, Good wash-off and high solubility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0112] The pretreatment step used in embodiment 1-3 is consistent with the solution, all including mechanical polishing-degreasing-hot water washing-alkali washing-hot water washing-cold water washing-acid washing-water washing:
[0113] The mechanical polishing is sandblasting,
[0114] Described degreasing is alkaline degreasing, and degreasing liquid is the mixed aqueous solution of 23g / L sodium carbonate and 2.5g / L sodium phosphate, temperature 67 o C, soaking time 5.5min;
[0115] Described alkali washing liquid is the sodium citrate aqueous solution of 25g / LNaOH, 4g / L, and temperature is 15 o C, soaking time 17.5min;
[0116] The pickling and deashing solution is 60g / L HNO 3 and a mixed aqueous solution of 6g / LNaF at room temperature for 2.5 minutes.
[0117] (2) Anodizing: use the aluminum material treated in step (1) as the anode, graphite as the cathode, immerse in the electrolyte, and connect the power supply through wires respectively. The electrolyte is a mixtu...
Embodiment 2
[0125] (2) Anodizing: use the aluminum material treated in step (1) as the anode, graphite as the cathode, immerse in the electrolyte, and connect the power supply through wires respectively. The electrolyte is a mixture of oxalic acid, phosphoric acid and sulfosalicylic acid , the concentration of oxalic acid is 0.275M, the concentration of phosphoric acid is 0.3M, the concentration of sulfosalicylic acid is 0.1M, the electrolysis parameters are as follows, the voltage is 25V, the temperature is 30 o C, current density 2.5A / dm 2 , time 25min; after anodizing, soak and clean in ethanol, and use vacuum drying to remove the electrolyte in the oxide film. The whole process strictly avoids the aluminum after anodizing from contacting air or water to avoid sealing holes.
[0126] (3) Protective film for positioning marks: Soak the aluminum material treated in step (2) in a toluene solution of γ-chloropropyltrimethylsilane, the concentration is 15wt.%, and the amount is 1% of the we...
Embodiment 3
[0133] (2) Anodizing: use the aluminum material treated in step (1) as the anode, graphite as the cathode, immerse in the electrolyte, and connect the power supply through wires respectively. The electrolyte is a mixture of oxalic acid, phosphoric acid and sulfosalicylic acid , the concentration of oxalic acid is 0.275M, the concentration of phosphoric acid is 0.3M, the concentration of sulfosalicylic acid is 0.1M, the electrolysis parameters are as follows, the voltage is 25V, the temperature is 30 o C, current density 2.5A / dm 2 , time 25min; after anodizing, soak and clean in ethanol, and use vacuum drying to remove the electrolyte in the oxide film. The whole process strictly avoids the aluminum after anodizing from contacting air or water to avoid sealing holes.
[0134] (3) Protective film for positioning marks: Soak the aluminum material treated in step (2) in a toluene solution of γ-chloropropyltrimethylsilane, the concentration is 15wt.%, and the amount is 1% of the we...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
pore size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com