PVC wood-plastic foaming antibacterial plate and preparation method thereof

A wood-plastic foaming and antibacterial board technology, applied in the field of PVC plastic sheets, can solve the problems of affecting the market positioning of PVC plastic sheets, limiting the development speed and application scope, and producing mold on the sheets, so as to achieve less visual fatigue and improve the ability to absorb ink. , the effect of reducing the specific gravity

Inactive Publication Date: 2020-05-05
SHANDONG BODO PLASTICS CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the inherent defects of PVC plastics, PVC plastic sheets have some quality shortcomings, such as: mold and mildew spots on the sheet when it is damp and used for a long time; the sheet has low strength, low hardness, and is easy to warp; when used in advertising printing Weak adsorption to ink, easy to drop ink and other defects; easy to generate static electricity, dust absorption, etc.; these defects have seriously affected the market positioning of PVC plastic sheets, limiting its development speed and application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC wood-plastic foaming antibacterial plate and preparation method thereof
  • PVC wood-plastic foaming antibacterial plate and preparation method thereof
  • PVC wood-plastic foaming antibacterial plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The PVC wood-plastic foamed antibacterial board described in the present embodiment, in parts by weight, the raw material composition is as follows:

[0033]

[0034] in:

[0035] The PVC resin powder is a mixture of SG-8 and SG-7 resin powders. The composite mass ratio of SG-8 resin powder and SG-7 resin powder is 1:1; the polymerization degree of SG-8 resin powder is 700 , The degree of polymerization of SG-7 resin powder is 800.

[0036] The foam regulator is a mixture of acrylates and styrenes, acrylates are polymers of methyl methacrylate and butyl acrylate, styrenes are polymers of styrene and acrylonitrile, styrene and acrylonitrile The mass ratio of acrylate and styrene is 4:1; the mass ratio of acrylate and styrene is 1:1.

[0037] The filler is heavy calcium carbonate.

[0038] The wood flour is activated Chinese fir flour with a particle size of 100 mesh.

[0039] The foaming agent is a compound of organic yellow foaming agent and inorganic white foami...

Embodiment 2

[0053] The PVC wood-plastic foamed antibacterial board described in the present embodiment, in parts by weight, the raw material composition is as follows:

[0054]

[0055]

[0056] in:

[0057] The PVC resin powder is a composite of SG-8 and SG-7 resin powders. The composite mass ratio of SG-8 resin powder and SG-7 resin powder is 1:1; the polymerization degree of SG-8 resin powder is 700, the polymerization degree of SG-7 resin powder is 800.

[0058] The foam regulator is a mixture of acrylates and styrenes, acrylates are polymers of methyl methacrylate and butyl acrylate, styrenes are polymers of styrene and acrylonitrile, styrene and acrylonitrile The mass ratio of acrylates to styrenes is 7:3; the mass ratio of acrylates to styrenes is 2:1.

[0059] The filler is light calcium carbonate.

[0060] The wood flour is activated Chinese fir flour with a particle size of 200 mesh.

[0061] The foaming agent is a compound of organic yellow foaming agent and inorganic w...

Embodiment 3

[0075] The PVC wood-plastic foamed antibacterial board described in the present embodiment, in parts by weight, the raw material composition is as follows:

[0076]

[0077] in:

[0078] The PVC resin powder is a mixture of SG-8 and SG-7 resin powders. The composite mass ratio of SG-8 resin powder and SG-7 resin powder is 1:1; the polymerization degree of SG-8 resin powder is 700 , The degree of polymerization of SG-7 resin powder is 800.

[0079] The foam regulator is a mixture of acrylates and styrenes, acrylates are polymers of methyl methacrylate and ethyl acrylate, styrenes are polymers of styrene and acrylonitrile, styrene and acrylonitrile The mass ratio of acrylates and styrenes is 3:1; the mass ratio of acrylates to styrenes is 3:1.

[0080] The filler is heavy calcium carbonate.

[0081] The wood powder is activated poplar wood powder with a particle size of 100 mesh.

[0082] The foaming agent is a compound of organic yellow foaming agent and inorganic white ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Densityaaaaaaaaaa
Melting pointaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of PVC plastic plates, and particularly relates to a PVC wood-plastic foaming antibacterial plate and a preparation method thereof. Raw materials comprisePVC resin powder, a foaming regulator, a filler, wood flour, a foaming agent, an antibacterial agent, a stabilizer, a lubricant, a matting agent and an ink absorption agent. According to the PVC wood-plastic foaming antibacterial plate, the wood powder filler is added into the formula of the plate, so that the specific gravity of the plate is reduced, and the plate is good in size stability, goodin rigidity, low in weight, high in strength and strong in wood texture; the matting agent compounded by silicon dioxide and a polypropylene graft is added, so that the prepared plate is low in surface reflectance and soft in gloss, the matt effect can improve the comfort level of the light environment, and people are not prone to visual fatigue; and the plate surface gloss is uniform and consistent, secondary processing and painting are not needed, and the cost is saved.

Description

technical field [0001] The invention belongs to the technical field of PVC plastic boards, and in particular relates to a PVC wood-plastic foamed antibacterial board and a preparation method thereof. Background technique [0002] At present, with the development of social economy, people's living standards have been greatly improved, and the requirements for living environment and quality are getting higher and higher. Coupled with the international emphasis on environmental protection, traditional wooden decoration and decoration materials have gradually been replaced by artificial materials. , PVC plastic sheet is one of the products, it has been widely used in decoration, decoration, medical and health and transportation and other fields. However, due to the inherent defects of PVC plastics, PVC plastic sheets have some quality shortcomings, such as: mold and mildew spots on the sheet when it is damp and used for a long time; the sheet has low strength, low hardness, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L97/02C08L39/08C08L51/06C08K13/02C08K5/19C08K3/22C08K3/36C08K3/015C08K5/17C08J9/10C08J9/08
CPCC08J9/0028C08J9/0061C08J9/0066C08J9/0071C08J9/0095C08J9/08C08J9/103C08J2203/02C08J2203/04C08J2203/18C08J2327/06C08J2439/08C08J2451/06C08J2497/02
Inventor 周学卫赵明春马健苗祥成苗伟
Owner SHANDONG BODO PLASTICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com