A process method for strengthening the pressure resistance quality of aluminum alloy

A process method and aluminum alloy technology, applied in the field of aluminum alloy castings, can solve the problems of thermal joint dispersion, box casting leakage, small porosity and pinhole defects, and achieve the effect of improving the seepage effect and preventing pressure leakage.

Active Publication Date: 2021-09-07
INNER MONGOLIA NORTH HEAVY INDS GROUP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the limitation of product use conditions, the wall thickness difference of castings is large, and the thermal joints are dispersed. At the same time, due to the influence of high-strength aluminum alloy materials, it is difficult to achieve sequential solidification during the solidification process of castings, and small looseness is easy to occur at the connection of casting wall thickness and isolated thermal joints. and pinhole defects
Such casting defects will cause leakage of the box casting during the pressure test after processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A process method for strengthening the pressure resistance quality of aluminum alloy
  • A process method for strengthening the pressure resistance quality of aluminum alloy
  • A process method for strengthening the pressure resistance quality of aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0036] Mix according to the requirements of the ingredients of the infusion solution, stir to make it even and fully wet, and the stirring time is not less than 1 hour.

[0037] See the attachment for the schematic diagram of parts assembly figure 1 , after the casting 1 is finished, install the sealing side plate 2, add an appropriate amount of infiltration fluid 3 that is evenly stirred, install the sealing upper plate 4 on the casting 1, and reserve 2 processing holes on the sealing upper plate 4 to install valves. After the installation of the air inlet pipe 5 and pressure gauge 6 is completed, place the casting 1 on the test bench 7 to ensure that the leakage position 8 is at the deepest point of the liquid surface.

[0038] Fill compressed air through the inlet pipe 5 with a valve to make the inner cavity pressure of the casting 1 reach 0.48-0.50 MPa, close the valve, and maintain the pressure for 1-2 hours according to the degree of leakage. Remove the sealing upper pl...

Embodiment 3

[0041] Take the infiltration process of the reduction box as an example.

[0042] The embodiment is as follows: the raw material of the infiltration fluid is selected with a particle size of 20-25 μm Fe 2 o 3 Powder, 800-mesh glass fiber, water glass with a modulus M=3.1-3.3, and industrial distilled water are mixed according to the requirements of the infiltration fluid composition, stirred to make it even and fully wet, and the stirring time is 1 hour.

[0043] The schematic diagram of the assembly of the parts is shown in the attached figure 1 , after the casting 1 is finished, install the sealing side plate 2, add an appropriate amount of infiltration fluid 3 that is evenly stirred, install the sealing upper plate 4 on the casting 1, and reserve 2 processing holes on the sealing upper plate 4 to install valves. After the installation of the air inlet pipe 5 and pressure gauge 6 is completed, place the casting 1 on the test bench 7 to ensure that the leakage position 8 is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
modulusaaaaaaaaaa
Login to view more

Abstract

The invention provides a process method for strengthening the pressure resistance quality of aluminum alloy, which belongs to the technical field of aluminum alloy castings. The process method for strengthening the pressure resistance quality of aluminum alloy can improve the aluminum The pressure resistance quality of alloy castings. The process method configures a kind of percolating fluid, which gradually infiltrates the internal looseness and pinholes of the casting under positive pressure conditions, and heats, heats, and cools the casting in sections, so that there is always a certain temperature gradient on the inner wall of the casting, improving the quality of the casting. The infiltration effect of the casting makes the infiltration fluid finally condense and solidify under positive pressure, preventing the final pressure leakage.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy castings, and in particular uses positive pressure to fill inorganic fillers to repair defects such as small looseness and pinholes inside the casting, strengthen the internal quality of the casting, and improve the pressure resistance of the aluminum casting. Background technique [0002] A certain type of military product is a key scientific research and production project of Inner Mongolia Beizhong Group. There are different types of high-, medium-, low-speed and high-precision transmission box castings. The material is high-strength cast aluminum alloy independently developed by the company. Carry out the air tightness test, the bearing pressure is 0.4MPa. [0003] Due to the limitation of product use conditions, the wall thickness difference of castings is large, and the thermal joints are dispersed. At the same time, due to the influence of high-strength aluminum alloy materials, it i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D31/00C04B28/26C09K3/12
CPCB22D31/005C04B28/26C04B2111/00482C04B2111/00663C09K3/12C04B14/308C04B14/42
Inventor 霍志刚张文用许君韩卓孙宁李佳蔚白燕芳陈鑫王卫东裴志义
Owner INNER MONGOLIA NORTH HEAVY INDS GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap