Ceramic-based composite material and preparation method thereof

A composite material and ceramic-based technology, applied in the field of ceramic-based composite materials and their preparation, can solve the problems of long preparation cycle, low temperature, and great influence of fiber system, and achieve the advantages of shortening the impregnation cycle, improving the ceramic yield and reducing the preparation cost. Effect

Inactive Publication Date: 2020-04-03
NAT UNIV OF DEFENSE TECH
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a ceramic matrix composite material and a preparation method thereof, which are used to overcome defects in the prior art such as long preparation period and great influence on the fiber system due to high temperature, realize low temperature preparation process and rapidly prepare ceramic matrix composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic-based composite material and preparation method thereof
  • Ceramic-based composite material and preparation method thereof
  • Ceramic-based composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The present invention proposes a preparation method of a ceramic matrix composite material, comprising the following steps:

[0027] S1: Weigh the silicone resin and the organic solvent according to the mass ratio, and stir to form a silicone resin solution;

[0028] Preferably, the organic solvent is one of methanol, acetone and dehydrated ethanol, preferably dehydrated ethanol, which has good solubility, low toxicity and low corrosion; the mass ratio of the silicone resin and dehydrated alcohol is ( 1:1)~(1:5); the stirring rate is 800~1500rpm, and the time is 2~8h. Too much silicone resin will result in a thicker solution, which is not conducive to impregnation; too little will result in a thinner solution, prolonging the impregnation cycle of the material, which is not conducive to production; fully stir to obtain a uniform silicone resin solution.

[0029] S2: Needling, puncturing or sewing the inorganic fiber cloth or fabric;

[0030] Preferably, the number of l...

Embodiment 1

[0046] This embodiment provides a preparation method of a ceramic matrix composite material, such as figure 1 shown, including the following steps:

[0047] (1) Take silicone resin and dehydrated alcohol, wherein the mass ratio of silicone resin and dehydrated alcohol is 1:1, form silicone resin solution by magnetic stirring for 4h;

[0048] (2) Lay 8 layers of T300-1K carbon fiber cloth with a thickness of 0.28mm, and then suture them. The fibers used in the sutures are commercially available common T300-1K carbon fibers. The distance between sutures is 5mm;

[0049] (3) Clamp the carbon fiber cloth sewn in step (2) with a graphite mold, place it in a vacuum container, vacuum inhale the silicone resin solution (suspension) prepared in step (1), and impregnate for 8 hours;

[0050] (4) Arranging the carbon fibers impregnated in step (3) in a vacuum cracking furnace to carry out molding cross-linking and high-temperature cracking, specifically:

[0051] Raise the temperature...

Embodiment 2

[0060] This embodiment provides a method for preparing a ceramic matrix composite material, comprising the following steps:

[0061] (1) Take silicone resin and dehydrated alcohol, wherein the mass ratio of silicone resin and dehydrated alcohol is 1:2, form silicone resin solution by magnetic stirring for 8h;

[0062] (2) 8 layers of 0.23mm thick second-generation SiC fiber cloth produced by National University of Defense Technology (Qing Wang. Effects of ZrO 2 coating on the strength improvement of 2.5D SiCf / SiO 2 composites.Ceramics International 43(2017) 884–889), and then perform suture treatment. The fiber used in the suture is the above-mentioned second-generation SiC fiber. In order to obtain better mechanical properties, the distance between every two sutures is designed to be 8mm;

[0063] (3) Clamp the carbon fiber cloth sewn in step (2) with a heat-resistant steel mold, place it in a vacuum container, vacuum inhale the silicone resin solution (suspension) prepared...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Densityaaaaaaaaaa
Shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a ceramic-based composite material and a preparation method thereof. The density of the composite material is 1.60-1.80g / cm<3>, the porosity is 11.5-14.5%, the interlaminar shear strength is 55-56MPa, the tensile strength at 1500 DEG C reaches 100MPa, and the bending strength in the fiber sewing direction at 1500 DEG C reaches 130MPa. According to the preparation method, the ceramic-based composite material is prepared by adopting a precursor impregnation-mold pressing low-temperature crosslinking-high-temperature cracking method. The composite material provided by theinvention is low in density, high in interlaminar strength and high in tensile strength at 1500 DEG C, and can be applied to the field of aerospace. The preparation method provided by the invention isshort in preparation period and low in cost, the temperature of mold pressing low-temperature crosslinking-high-temperature cracking is lower than 1000 DEG C, and the influence on a fiber system is small.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a ceramic matrix composite material and a preparation method thereof. Background technique [0002] Fiber-reinforced ceramic matrix composites are an emerging material system with high specific strength, high specific modulus, high temperature resistance and ablation resistance, which is developed rapidly in recent years with continuous fiber as reinforcement and ceramic as matrix. [0003] Fiber-reinforced ceramic matrix composites can be divided into 1D, 2D, and 3D according to the different reinforcement methods of continuous fibers inside the material, that is, composite materials are reinforced by unidirectional fibers (1D or UD, unidirectional), two-way fabric reinforcement (2D) and 3D. Three-dimensional fabric reinforcement (3D). Fiber reinforcement methods are different, and composite materials have different molding methods, pore structures, pore distributio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/56C04B35/80C04B35/622
CPCC04B35/56C04B35/622C04B2235/5248C04B2235/5244C04B2235/77C04B2235/96C04B2235/6562
Inventor 向阳曹峰彭志航刘荣军
Owner NAT UNIV OF DEFENSE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap