Anionic veneer dyeing material and preparation process thereof

An anionic dye and anionic technology, applied in the field of dyeing materials, can solve problems such as poor color fastness, general permeability, and low dyeing efficiency, and achieve the goal of improving color fastness, penetration, and dyeing efficiency Effect

Inactive Publication Date: 2020-03-27
深圳市前海幸运色彩科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the general permeability of existing veneer dyeing materials, when veneer dyeing is dipped and dyed, only the surface layer of veneer can only be dyed, and the color fastness of existing dyes is also general, which will lead to dyeing. The veneer fades after a short period of time; it also takes longer to stain the veneer with off-the-shelf dyes
Therefore, the existing technology has the problems of poor color fastness performance and low dyeing efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anionic veneer dyeing material and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1. An anionic veneer dyeing material, made of the following components by weight: resin, 20-25 parts; anionic dye, 30-35 parts; cetyltrimethylammonium chloride, 1.5-1.8 parts; lignin sulfonate acid salt, 2-3 parts; bisphenol-A polyoxyethylene ether, 2.1-2.5 parts; blocked water-based isocyanate crosslinking agent, 2-3 parts; deionized water, 15-20 parts.

[0021] The anionic dye is an acid dye neutralizer.

[0022] The acid dye neutralizer is an acid complex dye, which does not contain a sulfonic acid group, but contains a hydrophilic group such as a sulfonylamino group. The ratio of the metal atom to the dye molecule in the molecule is 1:2, so it is also called 1 :2 metal complex dyes.

[0023] The resin includes anionic water-based polyurethane resin and anionic acrylic resin, and the weight ratio between the anionic water-based polyurethane resin and the anionic acrylic resin is 2:1-3:1.

[0024] A kind of preparation technology of anionic veneer dyeing ma...

Embodiment 2

[0039] Example 2. An anionic veneer dyeing material, comprising the following components by weight: resin, 22 parts; anionic dye, 32 parts; cetyltrimethylammonium chloride, 1.6 parts; lignosulfonate, 2.5 parts; Bisphenol-A polyoxyethylene ether, 2.3 parts; blocked water-based isocyanate crosslinking agent, 2.5 parts; deionized water, 18 parts.

[0040] The anionic dye is an acid dye neutralizer.

[0041] The acid dye neutralizer is an acid complex dye, which does not contain a sulfonic acid group, but contains a hydrophilic group such as a sulfonylamino group. The ratio of the metal atom to the dye molecule in the molecule is 1:2, so it is also called 1 :2 metal complex dyes.

[0042]The resin includes anionic water-based polyurethane resin and anionic acrylic resin, and the weight ratio between the anionic water-based polyurethane resin and the anionic acrylic resin is 2:1.

[0043] A kind of preparation technology of anionic veneer dyeing material, comprises the following...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anionic veneer dyeing material and a preparation process thereof. The anionic veneer dyeing material comprises the following components in parts by weight: 20-25 parts of resin, 30-35 parts of an anionic dye, 1.5-1.8 parts of cetyltrimethylammonium bromide chloride, 2-3 parts of lignosulfonate, 2.1-2.5 parts of ethoxylatedbisphenol A, 2-3 parts of a blocked water-based isocyanate cross-linking agent, and 15-20 parts of deionized water. The preparation process comprises the steps of: A, pouring resin, cetyltrimethylammonium bromide chloride and lignosulfonate into a negative-pressure vacuum tank to obtain a product B; and C, pouring the product B, 1 / 2 of the anionic dye, ethoxylatedbisphenol A, the residual anionic dye, the blocked water-based isocyanate cross-linking agent and deionized water into a high-pressure stirring tank, and performing uniform stirring to obtain a finished product. The anionic veneer dyeing material and the preparation process thereofhave the characteristics that the color fastness can be effectively improved, and the dyeing efficiency is improved.

Description

technical field [0001] The invention relates to a dyeing material, in particular to an anionic veneer dyeing material and a preparation process thereof. Background technique [0002] During the growth process of wood, affected by the external environment, there may be defects such as discoloration and wormholes. This kind of wood is not suitable for use as a board alone. In order to make reasonable use of this kind of wood, the researchers cut it into veneer , and then use dyeing technology to treat the blemishes on its surface. After coloring, a beautiful and exquisite new decorative material can be produced. Because of its smooth surface and rich colors, it can well meet the requirements of different decoration places and the majority of customers. Buyer's own texture preference. Veneer dyeing methods are usually used for veneer dyeing, solid wood dyeing and standing wood dyeing; the so-called veneer dyeing refers to the uniform dyeing of the veneer obtained by rotary cut...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D15/00
CPCC09D15/00
Inventor 杨年富
Owner 深圳市前海幸运色彩科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap