High-strength inorganic artificial stone and manufacturing method thereof

A manufacturing method and artificial stone technology, applied in the field of building materials, can solve the problems of safety and health hazards and high manufacturing costs

Inactive Publication Date: 2020-02-28
CHINA STATE CONSTR HAILONG TECH CO LTD
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Due to the need to achieve a certain flexural strength requirement and increase the toughness of the product, the inorganic artificial stone raw materials on the market are often mixed with a certain amount of organic toughening materials to improve the flexural strength of the product. Therefore, for interior decoration, Inorganic artificial stones on the market have certain safety and health risks, and the manufacturing cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength inorganic artificial stone and manufacturing method thereof
  • High-strength inorganic artificial stone and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The present invention proposes a high-strength inorganic artificial stone. In parts by weight, the high-strength inorganic artificial stone comprises the following components: 60-70 parts of quartz sand, 5-10 parts of quartz powder, 22-25 parts of cement, and an inorganic active additive of 2.5-4 parts, 0.5-1.5 parts of water reducer, 2-4 parts of water.

[0036] The above-mentioned quartz sand, quartz powder, cement, inorganic active additives, water reducing agent and water are all inorganic raw materials. The high-strength inorganic artificial stone of the present invention is prepared by using all inorganic raw materials, and no organic materials are used in the whole process. The preparation of artificial stone can effectively avoid the pollution of the environment when artificial stone is used. For example, organic raw materials such as glue, resin and organic toughening materials are not used, which can effectively reduce the emission of toxic gases; and by using ...

Embodiment 2

[0050] The present invention proposes a high-strength inorganic artificial stone. In parts by weight, the high-strength inorganic artificial stone comprises the following components: 60-70 parts of quartz sand, 5-10 parts of quartz powder, 22-25 parts of cement, and an inorganic active additive of 3-4 parts, 0.5-1.5 parts of water reducer, 2-4 parts of water.

[0051] Compared with Example 1, the inorganic active additive used in this example is 3-4 parts by weight. The proportions by weight and specific materials of the remaining inorganic raw materials in Example 2 are the same as those in Example 1, and Example 1 may be referred to.

[0052] The high-strength inorganic artificial stone of the present invention uses all inorganic raw materials to prepare inorganic artificial stone, and does not use organic materials to prepare artificial stone in the whole process, effectively preventing artificial stone from polluting the environment during use, such as not using glue and r...

Embodiment 3

[0054] The present invention also proposes a high-strength inorganic artificial stone, which comprises the following components in parts by weight: 60-70 parts of quartz sand, 5-10 parts of quartz powder, 22-25 parts of cement, and inorganic active additives 3.5 parts, 0.5-1.5 parts of water reducer, 2-4 parts of water.

[0055] Compared with Example 1, the inorganic active additive used in this example is 3.5 parts by weight. The proportions by weight and specific materials of the remaining inorganic raw materials in Example 3 are the same as those in Example 1, so refer to Example 1.

[0056] The high-strength inorganic artificial stone of the present invention uses all inorganic raw materials to prepare inorganic artificial stone, and does not use organic materials to prepare artificial stone in the whole process, effectively preventing artificial stone from polluting the environment during use, such as not using glue and resin Organic raw materials such as organic toughen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength inorganic artificial stone and a manufacturing method thereof. The high-strength inorganic artificial stone comprises the following components: 60-70 parts of quartz sand, 5-10 parts of quartz powder, 22-25 parts of cement, 2.5-4 parts of an inorganic active additive, 0.5-1.5 parts of a water reducing agent and 2-4 parts of water. According to the high-strength inorganic artificial stone provided by the invention, the inorganic artificial stone is prepared by completely using inorganic raw materials, so that the environmental pollution caused by the inorganic artificial stone in use is avoided; and the inorganic active additive is used as a preparation material, so that the flexural strength of the inorganic artificial stone is ensured to meet the use requirements.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a high-strength inorganic artificial stone and a manufacturing method thereof. Background technique [0002] Artificial stone is a new product that has developed rapidly in recent years. Inorganic artificial stone can be divided into two molding methods: press plate type and block type. , fillers, inorganic additives, inorganic pigments, etc., and then vacuum-pressed to form a blank (block, board) material for architectural decoration and veneer. After a certain period of curing and curing at room temperature, it is then cut, thickened, polished, etc. After processing, it is finally made into decorative panels or profiles of various specifications. [0003] Compared with organic artificial stone, inorganic artificial stone does not contain organic components such as resin and glue, so it has the advantages of hard and durable, healthy and environmentally friendly, no color diff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B14/06C04B18/141C04B14/106C04B18/146C04B2103/302C04B22/002
Inventor 张海鹏姜绍杰张宗军赵宝军吴琛王铁柱李朗蓝柳波王俊
Owner CHINA STATE CONSTR HAILONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com