Polypropylene material with low linear expansion coefficient and preparation method of polypropylene material

A low linear expansion, polypropylene material technology, applied in the field of materials, can solve the problems of reducing the shrinkage rate of the material, the appearance of floating fibers, the decrease of the rigidity of the material, etc., and achieve the effect of reducing the coefficient of linear expansion, low equipment requirements, and reducing the crystallinity.

Inactive Publication Date: 2020-02-07
GUANGDONG ALDEX NEW MATERIAL CO LTD
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the shrinkage rate of the material is mainly reduced by adding toughening agent (POE) and increasing the proportion of talcum powder to meet the requirement of low linear expansion. High talcum powder dosage will have a great impact on the impact performance of the material. ) amount will lead to higher cost and lower material rigidity
There are also problems such as reducing material shrinkage and linear expansion coefficient by adding glass fibers and whiskers, but it will cause problems such as product deformation
[0004] Chinese patent CN103044775A uses chopped glass fiber to reduce the linear expansion coefficient of the polypropylene composite material, and the large amount of glass fiber will cause the appearance of floating fibers and product warpage.
Chinese patents CN201511019839, CN201711167913, and CN201711447917 use whiskers and needle-shaped wollastonite to reduce the linear expansion coefficient of the material. The ratio of the length of the whiskers and wollastonite is relatively large, so that the shrinkage rate of the material flow direction and the vertical flow direction differ greatly. , will affect product size, warpage, etc.
Chinese patent CN201710726681 uses glass beads to reduce the linear expansion coefficient of the material. Glass beads are fragile during processing and difficult to process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene material with low linear expansion coefficient and preparation method of polypropylene material
  • Polypropylene material with low linear expansion coefficient and preparation method of polypropylene material
  • Polypropylene material with low linear expansion coefficient and preparation method of polypropylene material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] The functionalized ethylene-octene copolymer was prepared as follows:

[0056] In parts by weight of raw materials, get 97 parts of ethylene-octene copolymer (POE), 0.1 part of dicumyl peroxide, 1 part of vinyl triisopropoxysilane and 0.5 part of auxiliary crosslinking agent triene Add propyl isocyanurate (TAIC) into a mixer and mix evenly, then put the resulting mixture into an extruder for granulation to obtain the functionalized ethylene-octene copolymer, and the extrusion temperature is 160°C to 180°C ℃.

[0057] The toughening agent in the comparative example refers to ethylene-octene copolymer.

Embodiment 1

[0059] This embodiment provides a polypropylene material with a low coefficient of linear expansion, which is prepared from the following components in parts by weight of raw materials:

[0060]

[0061] The preparation method of the polypropylene material with low linear expansion coefficient is as follows:

[0062] Polypropylene resin, functionalized ethylene-octene copolymer, compatibilizer, talcum powder, flat glass fiber, antioxidant and weathering agent are added into a high-speed mixer and stirred evenly (the mixer speed is 1000 rpm), and then the resulting The mixed material is fed into the parallel twin-screw extruder from the main feeding port for melt extrusion and granulation. The process parameters include: the temperature of the first zone is 160°C, the temperature of the second zone is 190°C, the temperature of the third zone is 190°C, and the temperature of the fourth zone The temperature of the fifth zone is 190°C, the temperature of the sixth zone is 190°C...

Embodiment 2

[0065] This embodiment provides a polypropylene material with a low coefficient of linear expansion, which is prepared from the following components in parts by weight of raw materials:

[0066]

[0067] The preparation method of the polypropylene material with low linear expansion coefficient is as follows:

[0068] Polypropylene resin, functionalized ethylene-octene copolymer, compatibilizer, talcum powder, flat glass fiber, antioxidant and weathering agent are added into a high-speed mixer and stirred evenly (the mixer speed is 1000 rpm), and then the resulting The mixed material is fed into the parallel twin-screw extruder from the main feeding port for melt extrusion and granulation. The process parameters include: the temperature of the first zone is 140°C, the temperature of the second zone is 220°C, the temperature of the third zone is 220°C, and the temperature of the fourth zone The temperature of the fifth zone is 220°C, the temperature of the sixth zone is 220°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a polypropylene material with a low linear expansion coefficient and a preparation method of the polypropylene material. The polypropylene material with the low linear expansion coefficient is prepared from the following raw materials: polypropylene resin, a functional ethylene-octylene copolymer, a compatilizer, talcum powder, flat glass fiber, an antioxidant and a weather resistant agent. By adjusting components and proportions of the raw materials, the polypropylene material has the low linear expansion coefficient and good mechanical properties, and can be appliedto automobile bumpers, apron boards and the like.

Description

technical field [0001] The invention relates to the field of materials, in particular to a polypropylene material with a low linear expansion coefficient and a preparation method thereof. Background technique [0002] Polypropylene has been widely used in the interior and exterior of automobiles because of its excellent comprehensive performance, wide range of sources, light weight and low price, and easy molding and processing. In automotive exterior parts, such as automobile bumpers, skirts, fenders, etc., are in a state of alternating cold and heat for a long time, resulting in large changes in material size, resulting in assembly gaps or deformation, so materials are required to have a low linear expansion coefficient . [0003] At present, the shrinkage rate of the material is mainly reduced by adding toughening agent (POE) and increasing the proportion of talcum powder to meet the requirement of low linear expansion. High talcum powder dosage will have a great impact ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08K13/04C08K7/14C08K3/34C08K5/134C08K5/526C08F255/02C08F230/08
CPCC08F255/02C08L23/12C08L2205/025C08L2205/035C08L51/06C08K13/04C08K7/14C08K3/34C08K5/1345C08K5/526C08F230/08
Inventor 洪剑城张东冯刚卢健体
Owner GUANGDONG ALDEX NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com