A kind of bis-secondary amine containing siloxane group and its preparation method and application

A technology of siloxane group and di-secondary amine, which is applied in the preparation of moisture-cured spray polyurea elastomer and its preparation field, can solve the problem of difficult-to-wet base material, fast reaction speed of A/B mixed components, and poor adhesion. To achieve the effect of excellent thermal oxygen aging performance, excellent adhesion performance and good toughness

Active Publication Date: 2022-04-19
WANHUA CHEM GRP CO LTD
View PDF30 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the method of introducing silicone into polyurea is mainly to physically mix it with other diamines in component B and then spray it. The reaction speed of the A / B mixed component sprayed out by this method is too fast, and it is difficult to effectively infiltrate the substrate. The interior of the polyurea material has poor adhesion, and the cross-linking points in this system are urea groups, resulting in poor toughness of the polyurea material in the later stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bis-secondary amine containing siloxane group and its preparation method and application
  • A kind of bis-secondary amine containing siloxane group and its preparation method and application
  • A kind of bis-secondary amine containing siloxane group and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] A preparation method of moisture-cured spray polyurea elastomer, comprising:

[0077] Preparation of component A:

[0078] Add 40 parts of polyoxypropylene diol (N210, Mn=1000) into the reactor, dehydrate at 110°C for 3 hours under a vacuum of 0.09MPa, and then lower the temperature to 60°C. Add 48 parts of isophorone diisocyanate to a reaction kettle with a stirrer and nitrogen protection, and add 5 parts of dibutyl phthalate and 0.1 part of dibutyltin dilaurate, and then dehydrate The polyoxypropylene diol is slowly added dropwise into the reaction kettle. After the dropwise addition, the temperature of the reaction system is raised to 90°C, and the temperature is kept for 3 hours. After defoaming, the temperature is lowered to obtain the isocyanate prepolymer group A with the -NCO content of 15.9%. Minute;

[0079] Preparation of component B:

[0080] equipped with a stirrer, thermometer and N 2 Add 30 parts of isophorone diamine and 0.39 parts of tetraalkylammon...

Embodiment 2

[0083] A preparation method of moisture-cured spray polyurea elastomer, comprising:

[0084] Preparation of component A:

[0085] Add 51.25 parts of polyoxypropylene diol (N204, Mn=400) into the reactor, dehydrate at 110°C for 3 hours under a vacuum of 0.09MPa, and then lower the temperature to 60°C. The hexamethylene diisocyanate of 59 parts is joined in the reactor with agitator and nitrogen protection, the dibutyl phthalate of 15 parts and the dibutyltin dilaurate of 0.66 parts are added, then the dehydrated Slowly add polyoxypropylene diol to the reaction kettle dropwise. After the dropwise addition, raise the temperature of the reaction system to 90°C, keep it warm for 3 hours, and cool down after defoaming to obtain the isocyanate prepolymer A component with a -NCO content of 15%. ;

[0086] Preparation of component B:

[0087] equipped with a stirrer, thermometer and N 2 Add 46.75 parts of diaminodicyclohexylmethane and 1.12 parts of tetraalkylammonium hydroxide to ...

Embodiment 3

[0090] A preparation method of moisture-cured spray polyurea elastomer, comprising:

[0091] Preparation of component A:

[0092] Add 37.2 parts of polyoxypropylene diol (N210, Mn=1000) into the reactor, dehydrate at 110°C for 3 hours under a vacuum of 0.09MPa, and then lower the temperature to 60°C. 62.8 parts of dicyclohexylmethane diisocyanate are added to a reactor with a stirrer and nitrogen protection, 10 parts of dibutyl phthalate and 0.4 part of dibutyltin dilaurate are added, and then the dehydrated Slowly add polyoxypropylene diol into the reaction kettle dropwise. After the dropwise addition, raise the temperature of the reaction system to 90°C, keep it warm for 3 hours, and cool down after defoaming to obtain component A of the isocyanate prepolymer with a -NCO content of 15.4%. ;

[0093] Preparation of component B:

[0094] equipped with stirrer, thermometer and N 2 Add 15 parts of 1,3-propylenediamine and 0.64 parts of tetraalkylammonium hydroxide to the react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bis-secondary amine containing siloxane group and its preparation method and application. The bis-secondary amine containing siloxane group is composed of one or more than one dibasic primary amine and containing Siloxanes with unsaturated double bonds are obtained by Michael addition. The B component of the spray polyurea is prepared by mixing the bis-secondary amine and its additives, and the isocyanate prepolymer generated by the reaction of polyether polyol and isocyanate is used as the A component, and the volume ratio of A\B components is 1 : 1 mixed and sprayed to obtain polyurea material. The two active hydrogens of the bis-secondary amine can react with isocyanate to form linear polyurea, while the siloxane group can be hydrolyzed to form Si‑O‑Si crosslinking points, which reduces the crosslinking speed of amine and isocyanate and improves the polyurea The mechanical properties of the material.

Description

technical field [0001] The invention relates to the technical field of spray-coated polyurea elastomers, in particular to bis-secondary amines containing siloxane groups and a preparation method thereof, which is used as a raw material to prepare moisture-cured spray-coated polyurea elastomers and a preparation method thereof. Background technique [0002] Spray polyurea elastomer is a new multi-functional material widely used in waterproof and anti-corrosion fields. It has excellent waterproof performance, anti-corrosion performance and wear resistance. Traditional waterproof materials such as acrylic emulsion waterproof coatings are not resistant to aging, cannot be exposed, have low strength, poor puncture resistance, high requirements on the construction environment, slow curing, low construction efficiency, etc., and the raw material system does not contain solvents. According to the current environmental protection requirements, it can be continuously sprayed on the su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/38C08G18/66C08G18/48C09D175/02C09D7/61C07F7/18
CPCC08G18/3893C08G18/6685C09D175/02C09D7/61C07F7/1892C08K3/36
Inventor 杜秀才刘赵兴任树杰陈杰方璞吴鹏超姜庆梅
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com