4.5 micrometer electrolytic copper foil for lithium ion battery, preparation method and additive

A lithium-ion battery, electrolytic copper foil technology, applied in battery electrodes, electrolysis process, secondary batteries, etc., can solve the problem of high additive requirements, increase the number of nucleation, eliminate pinholes and microscopic defects, and inhibit the growth of crystal nuclei speed effect

Active Publication Date: 2020-01-03
安徽华创新材料股份有限公司
View PDF15 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that the existing 4.5 μm electrolytic copper foil for lithium-ion batteries has high requirements for additives, and the additives used in the existing 5 μm and above double-sided photoelectrolytic copper foil cannot meet the performance requirements. Therefore, a kind of 4.5 μm electrolytic copper foil for lithium ion battery, preparation method and additive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 4.5 micrometer electrolytic copper foil for lithium ion battery, preparation method and additive
  • 4.5 micrometer electrolytic copper foil for lithium ion battery, preparation method and additive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: A kind of additive for lithium ion battery 4.5 μm electrolytic copper foil, it comprises 2.5g / l polyquaternium-10, 3.5g / l polyquaternium-7, 2.5g / l polyquaternium -51, 2g / l sodium polydithiodipropane sulfonate, 0.75g / l sodium alcohol thiopropane sulfonate, 0.2g / l gelatin, 0.2g / l basic saffron dye, 0.4g / l N-butyl Thiourea, 0.75 g / l sodium mercaptoimidazole benzenesulfonate and 0.4 g / l polyethylene glycol formal.

Embodiment 2

[0028] Embodiment 2: A kind of additive for lithium ion battery 4.5 μm electrolytic copper foil, it comprises 2.7g / l polyquaternium-10, 3.7g / l polyquaternium-7, 2.7g / l polyquaternium -51, 2.2g / l sodium polydithiodipropane sulfonate, 1g / l sodium alcohol thiopropane sulfonate, 0.25g / l gelatin, 0.25g / l basic saffron dye, 0.5g / l N-butyl Thiourea, 1 g / l sodium mercaptoimidazole benzenesulfonate and 0.5 g / l polyethylene glycol formal.

Embodiment 3

[0029] Embodiment 3: A kind of additive for 4.5 μ m electrolytic copper foils for lithium ion battery, it comprises 3 g / l polyquaternium-10, 5 g / l polyquaternium-7, 3 g / l polyquaternium -51, 2.5g / l sodium polydithiodipropane sulfonate, 1.25g / l sodium alcohol thiopropane sulfonate, 0.5g / l gelatin, 0.5g / l basic saffron dye, 0.2g / l N-butyl thiourea, 1.25g / l sodium mercaptoimidazole benzenesulfonate and 0.75g / l polyethylene glycol formal.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses 4.5 micrometer electrolytic copper foil for a lithium ion battery, a preparation method and an additive. The 4.5 micrometer electrolytic copper foil is prepared from polyquaternium-10, polyquaternium-7, polyquaternium-51, dithiobis-1-propanesulfonic acid disodium salt, sodium alcohol mercaptan sulfonate, gelatin, alkaline safranine dye, N-butyl thiourea, mercaptoimidazole sodium benzenesulfonate and polyethylene glycol acetal. The 4.5 micrometer electrolytic copper foil for the lithium ion battery, the preparation method and the additive have the beneficial effects thatby means of the coupling reaction of the additive, nucleating surface energy is reduced, the growth speed of crystal nuclei is restrained, pinholes and micro-defects are removed, the nucleating quantity is increased, grains are refined, the structure of the copper coil is homogenized, and the tensile strength and the ductility are effectively improved; and industrialization of the copper foil which has the tensile strength of 35-40 kgf / mm<2> and the uniform double-face structure (Rz of the smooth and rough faces is 1.0-2.0 micrometers) and is free of defects and ultrathin (the thickness is 4.5 micrometers) is achieved, and industrialization of high-energy-density power battery copper foil products is effectively achieved.

Description

technical field [0001] The invention relates to the technical field of electrolytic copper foil preparation, in particular to a 4.5 μm electrolytic copper foil for lithium ion batteries, a preparation method and additives. Background technique [0002] At present, most of the additives used in the manufacture of ultra-thin electrolytic copper foil are gelatin, thiourea and other additives. The appearance quality and internal quality of the manufactured electrolytic copper foil products are quite different, the thickness uniformity is poor, the crystal structure is coarse and loose, and the tensile strength is low. Low ≤ 350N / mm2, low elongation ≤ 2%, the volume capacity of the lithium-ion battery made of copper foil made of this additive is relatively small, the internal resistance of the battery is large, and the service life of the battery is shortened. Faults are prone to occur during discharge. Because 4.5μm copper foil is thinner, defects are easier to enlarge, so the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D1/04C25D3/38H01M4/66H01M10/0525
CPCC25D1/04C25D3/38H01M4/661H01M10/0525Y02E60/10
Inventor 操声跃张红亮何桂青束磊
Owner 安徽华创新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com