A kind of water-based stain-resistant white finish for woodware and preparation method thereof

A technology for white finish paint and woodware, applied to biocide-containing paints, antifouling/underwater paints, coatings, etc., can solve the problems of poor stain resistance and difficulty in high-end furniture, and achieve low VOC content and excellent adhesion Good effect of strong force and scratch resistance

Active Publication Date: 2022-02-18
WANHUA CHEM GRP CO LTD +1
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the one-component acrylic acid added to the water-based wood matt white finish is generally poor in stain resistance to coffee, red wine and mustard, and it is difficult to be applied to the field of high-end furniture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based stain-resistant white finish for woodware and preparation method thereof
  • A kind of water-based stain-resistant white finish for woodware and preparation method thereof
  • A kind of water-based stain-resistant white finish for woodware and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0097] The preparation of the aqueous acrylic polymer emulsion a of core-shell structure:

[0098] (1) Preparation of nuclear layer pre-emulsion: 120g methyl methacrylate, 180g butyl acrylate, 1.5g sodium lauryl sulfate and 90g deionized water were respectively added to a 1L reactor for pre-emulsification, pre-emulsification The time is 30min, obtains nuclear layer pre-emulsion;

[0099] (2) Prepare the shell pre-emulsion: add 230g methyl methacrylate, 54g butyl acrylate, 15g acrylic acid, 1.5g sodium lauryl sulfate and 90g deionized water to a 1L reactor for pre-emulsification , the pre-emulsification time is 30min to obtain the shell layer pre-emulsion;

[0100] (3) Preparation of seed emulsion: Add 1.2g of sodium lauryl sulfate, 680g of water and 18g of the nuclear layer pre-emulsion obtained in step (1) into a 3L reactor, start stirring and heating, and wait until the temperature rises to 85°C. Add 12g aqueous initiator solution containing 1.5g ammonium persulfate to ini...

Embodiment 2

[0117] The preparation of the aqueous acrylic polymer emulsion b of core-shell structure:

[0118] (1) Preparation of nuclear layer pre-emulsion: 150g methyl methacrylate, 150g butyl acrylate, 1.5g sodium lauryl sulfate and 90g deionized water were added to a 1L reactor for pre-emulsification, pre-emulsification The time is 30min, obtains nuclear layer pre-emulsion;

[0119] (2) Prepare the shell pre-emulsion: add 260g of methyl methacrylate, 24g of butyl acrylate, 15g of acrylic acid, 1.5g of sodium lauryl sulfate and 90g of deionized water into a 1L reactor for pre-emulsification , the pre-emulsification time is 30min to obtain the shell layer pre-emulsion;

[0120] (3) Preparation of seed emulsion: Add 1.2g of sodium lauryl sulfate, 680g of water and 18g of the nuclear layer pre-emulsion obtained in step (1) into a 3L reactor, start stirring and heating, and wait until the temperature rises to 85°C. Add 12g aqueous initiator solution containing 1.5g ammonium persulfate to...

Embodiment 3

[0137] Preparation of water-based acrylic polymer emulsion c of core-shell structure:

[0138] (1) Preparation of nuclear layer pre-emulsion: 200g methyl methacrylate, 200g butyl acrylate, 2g sodium lauryl sulfate and 120g deionized water are respectively added to a 1L reactor for pre-emulsification. The time is 30min to obtain the core layer pre-emulsion;

[0139] (2) Prepare the shell layer pre-emulsion: 180g methyl methacrylate, 5g butyl acrylate, 15g acrylic acid, 1g sodium lauryl sulfate and 60g deionized water are respectively added to a 1L reactor for pre-emulsification, The time of pre-emulsification is 30min to obtain the shell layer pre-emulsion;

[0140] (3) Preparation of seed emulsion: Add 1.2g of sodium lauryl sulfate, 680g of water and 18g of the nuclear layer pre-emulsion obtained in step (1) into a 3L reactor, start stirring and heating, and wait until the temperature rises to 85°C. Add 12g aqueous initiator solution containing 1.5g ammonium persulfate to in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of water-based wood ware paint, and particularly relates to a water-based wood stain-resistant white finish paint and a preparation method thereof. The water-based wood stain-resistant white finish paint includes a main paint A and a curing agent B; the main paint A includes: water-based acrylic acid Emulsion, 48‑60wt%, coalescent, 4‑8wt%, water-based additive, 1.3‑5.8wt%, titanium dioxide, 18‑24wt%, matting powder, 0.3‑1.2wt%, water, 1.0‑28.4wt% %; Curing agent B is a sulfonate hydrophilic modified HDI trimer. On the basis of maintaining its excellent hardness, scratch resistance and adhesion, the water-based stain-resistant white finish paint for woodware of the present invention has good resistance and tolerance to different stains, especially for red wine, mustard, coffee, alkali stains, etc. Has obvious anti-fouling effect.

Description

technical field [0001] The invention belongs to the technical field of water-based woodware paint, in particular to a water-based stain-resistant white finish paint for woodware and a preparation method thereof. Background technique [0002] Furniture is a necessary article for people's daily life and work. It is not only a practical product, but also an ornament to beautify the environment and give people aesthetic enjoyment. China is a big country in the production and export of furniture, and the total demand for furniture coatings is quite large; in 2018, the output of wood coatings in my country was more than 1.4 million tons, accounting for about 7% of the total output of coatings. increase. my country is a big exporter of furniture, and exported furniture has high requirements for environmental protection, which requires furniture manufacturers to use water-based wood coatings. With the improvement of people's awareness of environmental protection and home safety and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D151/00C09D5/16C08F265/06C08F220/14C08F220/18C08F220/06
CPCC09D151/003C09D5/1662C09D5/1687C08F265/06C08L2205/035C08L2205/025C08L2205/02C08L2207/53C08L2205/04
Inventor 林争超马吉全孙伟祖邓俊英孙家宽
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products