Optical function modified polyurethane composite paint and preparation method thereof

A composite coating and polyurethane technology, which is applied in the field of polyurethane materials, can solve problems such as insufficient surface gloss and luster, difficulty in meeting market demand, and affecting the health of users, so as to achieve improved gloss and luster and great market competitiveness. , The effect of low equipment requirements

Inactive Publication Date: 2019-12-13
HUBEI UNIV OF ARTS & SCI
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The film formed in this way is commonly known as "coating film, also known as paint film or coating"; the existing coating formula is complicated, the gloss and color of the surface are not enough, it is difficult to meet the needs of the market, and it contains more harmful substances, affecting users. health, for this reason, we propose a light function modified polyurethane composite coating and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A light function modified polyurethane composite coating, comprising the following components (calculated by mass percentage): 25% polyurethane, 12% urea-formaldehyde resin, 8% cellulose acetate, 4.2% polyvinyl butyral, 3.6% ethanol, Anhydrous ether 2.7%, fumed silica 1.5%, dioctyl phthalate 1.2%, luminescent powder 6%, dispersant 2%, precipitant as the balance.

[0023] Further, the luminescent powder is composed of 45% silver powder and 55% aluminum powder, the precipitation agent is ammonium bicarbonate, and the dispersant is copper stearate.

[0024] A light function modified polyurethane composite coating and a preparation method thereof, comprising the following steps:

[0025] Step 1: Prepare materials according to the above components;

[0026] Step 2: Weigh polyvinyl butyral and anhydrous ether at a molar ratio of 1:2:1 to react at 110°C to obtain a prepolymer, and filter the prepolymer through a centrifugal filter for 3 Minutes, get filtrate and heat to 30 d...

Embodiment 2

[0034] A light function modified polyurethane composite coating, comprising the following components (calculated by mass percentage): 27% polyurethane, 14% urea-formaldehyde resin, 9% cellulose acetate, 4.4% polyvinyl butyral, 3.8% ethanol, Anhydrous ether 2.9%, fumed silica 1.8%, dioctyl phthalate 1.7%, luminescent powder 8%, dispersant 3%, precipitant as the balance.

[0035] Further, the luminescent powder is composed of 45% silver powder and 55% aluminum powder, the precipitation agent is ammonium bicarbonate, and the dispersant is copper stearate.

[0036] A light function modified polyurethane composite coating and a preparation method thereof, comprising the following steps:

[0037] Step 1: Prepare materials according to the above components;

[0038] Step 2: Weigh polyvinyl butyral and anhydrous ether at a molar ratio of 1:2:1 to react at 120°C to obtain a prepolymer, and filter the prepolymer through a centrifugal filter 4 Minutes, get filtrate and heat to 35 degre...

Embodiment 3

[0046] A light function modified polyurethane composite coating, comprising the following components (calculated by mass percentage): 28% polyurethane, 16% urea-formaldehyde resin, 10% cellulose acetate, 4.6% polyvinyl butyral, 4% ethanol, Anhydrous ether 3.3%, fumed silica 2.3%, dioctyl phthalate 2.1%, luminous powder 10%, dispersant 4%, precipitant as the balance.

[0047] Further, the luminescent powder is composed of 45% silver powder and 55% aluminum powder, the precipitation agent is ammonium bicarbonate, and the dispersant is copper stearate.

[0048] A light function modified polyurethane composite coating and a preparation method thereof, comprising the following steps:

[0049] Step 1: Prepare materials according to the composition of the above components;

[0050] Step 2: Weigh polyvinyl butyral and anhydrous ether at a molar ratio of 1:2:1 to react at 145°C to obtain a prepolymer, and filter the prepolymer through a centrifugal filter for 5 Minutes, get filtrate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses optical function modified polyurethane composite paint. The optical function modified polyurethane composite paint is prepared from, by mass, 25-30% of polyurethane, 12-17% ofurea-formaldehyde resin, 8-11% of cellulose acetate, 4.2-4.8% of polyvinyl butyral, 3.6-4.1% of ethanol, 2.7-3.5% of anhydrous diethyl ether, 1.5-2.5% of fumed silica, 1.2-2.3% of dioctyl phthalate, 6-12% of luminescent powder, 2-5% of dispersing agents and the balance being precipitating agents. The invention further discloses a preparation method of the optical function modified polyurethane composite paint. The method comprises the following steps of performing reacting and filtrating, performing heating and stirring, performing sputtering treatment, performing cleaning, performing high-speed stirring, and performing ultrasonic treatment. According to the optical function modified polyurethane composite paint and the preparation method thereof, the formula is more reasonable, the glossiness and the color degree of the paint are obviously improved, the addition of toxic substances is reduced to a maximum extent, that the physical health of a user is free of being damaged is ensured,the environmental friendliness is high, and the paint has larger market competitiveness; and moreover, the preparation method is simpler and low in equipment requirement, and has a good popularizationeffect.

Description

technical field [0001] The invention relates to the technical field of polyurethane materials, in particular to a light function modified polyurethane composite coating and a preparation method thereof. Background technique [0002] Paint, traditionally called paint in China. The so-called paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated. It is usually based on resin, oil or emulsion, with or without adding pigments and fillers. Agents are viscous liquids prepared with organic solvents or water. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it as follows: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a firm adhesion, a certain strength, and a continuous coating. Solid film. The film formed in this way is commonly called "coating film, also known as paint f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D161/24C09D101/12C09D129/14C09D5/22C09D7/65C09D7/20
CPCC08K2003/0806C08K2003/0812C08L2205/035C09D5/22C09D7/20C09D7/65C09D175/04C08L61/24C08L1/12C08L29/14C08K13/06C08K3/08
Inventor 朱文利
Owner HUBEI UNIV OF ARTS & SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products