A method for preparing furfural co-production glue-free fiberboard from reed

A technology of fiberboard and reed, which is applied in the field of furfural co-production of glue-free fiberboard from reed, can solve the problems of underutilization of hemicellulose, uneven distribution of laccase enzyme activity, long microbial growth cycle, etc., to facilitate equipment selection, Reduce the side reaction of furfural and reduce the effect of corrosion

Active Publication Date: 2021-09-28
SICHUAN GOLDEN ELEPHANT SINCERITY CHEM CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method does not require an external adhesive, the production efficiency of the press plate is low due to the long microbial growth cycle, and the uneven distribution of laccase activity can easily lead to product instability.
Simultaneously these methods fail more valuable utilization of reed raw material
Another problem is that hemicellulose is not fully utilized during processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing furfural co-production glue-free fiberboard from reed
  • A method for preparing furfural co-production glue-free fiberboard from reed
  • A method for preparing furfural co-production glue-free fiberboard from reed

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] A method for preparing furfural co-production glue-free fiberboard from reeds, comprising the following steps:

[0059] (1) The raw material reed is fractured and cut into sections to make the length 20-40mm;

[0060] (2) by wind conveying, the reed leaves, reed flowers and flute membrane impurities in the reeds are separated, and the remaining reeds are raw materials for steam explosion;

[0061] (3) adding mass concentration to the reed steam explosion raw material obtained in step (2) is 1% dilute acetic acid, mix homogeneously with a mixer and maintain 30 minutes, the solid-to-liquid ratio in the mixer is 1:6; the mixer is Ribbon mixer or tumble mixer. Then the reed after the mixed acid is sent into the steam blaster for instant blasting. The conditions for instant blasting in the steam blaster are: steam pressure 1.4Mpa, temperature 180-200°C, holding time 8 minutes; the material after steam explosion is made into 24wt % thick pulp, grind into fluffy fibrous form...

Embodiment 2

[0071] A method for extracting xylose by reed steam explosion to prepare furfural, comprising the following steps:

[0072] (1) The raw material reed is fractured and cut into sections to make the length 20-40mm;

[0073] (2) by wind conveying, the reed leaves, reed flowers and flute membrane impurities in the reeds are separated, and the remaining reeds are raw materials for steam explosion;

[0074] (3) adding concentration to the reed steam explosion raw material obtained in step (2) is 1% dilute acetic acid, mix uniformly with a mixer and maintain 30 minutes, the solid-liquid ratio in the mixer is 1:6; Ribbon mixer or tumble mixer. Then the reed after the mixed acid is sent into the steam blaster for instant blasting in the steam blaster. The conditions for instant blasting in the steam blaster are: steam pressure 1.4Mpa, temperature is 180-200°C, and the maintenance time is 8 minutes; % thick pulp, grind into fluffy fibrous form with high consistency mill, and then wash...

Embodiment 3

[0082] The operating conditions are the same as in Example 1, except that the concentration of the xylose solution is changed to 24%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of comprehensive utilization of crop straw resources, and specifically relates to a method for extracting xylose from reeds by steam explosion to prepare furfural co-production fiberboards. The method comprises the following steps: 1) fracturing and segment cutting; 2) winnowing; 3) steam explosion after pressing and dehydration after dilute acetic acid pretreatment, and water washing of the material after steam explosion; 4) water extract liquid is sent to fractionation tower; electrodialysis separation Formic acid, acetic acid and furfural aqueous solution; 5) microfiltration after fermentation of the reducing sugar mixture; 6) reverse osmosis; 7) furfural; 8) drying after treatment to obtain a mixture containing solid cellulose, lignin and a small amount of hemicellulose; 9 ) made of glue-free fiberboard. The method uses high-pressure steam explosion to make the hemicellulose in the reed more easily hydrolyzed into monosaccharides or oligosaccharides under relatively low-temperature steam explosion conditions, and reducing the temperature of steam explosion can also reduce the further generation of xylose and other pentoses. Degradation, improve the utilization rate of reed.

Description

technical field [0001] The invention belongs to the field of comprehensive utilization of crop straw resources, and relates to a process technology for producing furfural through co-production of crop straw, especially focusing on the method of directly preparing furfural and remaining solid matter to make glue-free fiberboard from steam-exploded water-washed materials of crop straw, specifically a reed A method for preparing furfural co-production glue-free fiberboard. Background technique [0002] With the increasingly tight supply of wood, the search for wood substitute raw materials has received more and more attention. Studies have proved that reed can replace wood for the production of wood-based panels. my country has relatively sufficient reed resources, and the distribution area is very wide. There are as many as 14 main reed producing areas. Previously, reeds were used as raw materials for papermaking, and had no other industrial uses. The felled reeds were disca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D307/50
CPCB27N3/12B27N3/18B27N3/203C07D307/50
Inventor 唐印郭志刚雷林刘朝慧李旭初武长安李刚王明权
Owner SICHUAN GOLDEN ELEPHANT SINCERITY CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com