Production method of low-carbon low-silicon aluminum killed molten steel

A low-carbon, low-silicon, production method technology, applied to the improvement of process efficiency, manufacturing converters, etc., can solve the problem of low-carbon, low-silicon, aluminum-killed molten steel cleanliness, deoxidation cost reduction, high deoxidation cost, low-carbon, low-silicon, aluminum-killing Poor cleanliness of molten steel and other problems, to achieve the effect of reducing deoxidation cost, stable yield and high pass rate

Inactive Publication Date: 2019-11-22
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF8 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a production method of low-carbon, low-silicon, aluminum-killed molten steel, which mainly solves the technical problems of poor cleanliness and high deoxidation cost of low-carbon, low-silicon, aluminum-killed molten steel produced by converter smelting in the prior art; The invented method realizes the improvement of the cleanliness of low-carbon, low-silicon and aluminum-killed molten steel and the substantial reduction of deoxidation cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of low-carbon low-silicon aluminum killed molten steel
  • Production method of low-carbon low-silicon aluminum killed molten steel
  • Production method of low-carbon low-silicon aluminum killed molten steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention will be further illustrated below in conjunction with specific embodiments, and it should be understood that the following specific embodiments are only used to illustrate the present invention and are not intended to limit the scope of the present invention.

[0016] In the embodiment of the present invention, the low-carbon, low-silicon and aluminum-killed molten steel is smelted in a 250-ton top-bottom double-blown converter, wherein the smelted steel types in Examples 1 and 2 are both SPHC, and the smelted steel types in Examples 3 and 4 are both DC51D+Z. The bottom blowing gas in the converter smelting process is argon; the production method includes: converter smelting, molten steel treatment at the argon blowing station. The control parameters of molten steel production in the embodiment of the present invention are shown in Table 1 to Table 6.

[0017] Table 1 Parameters of converter smelting metal material in the embodiment of the present ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of low-carbon low-silicon aluminum killed molten steel. The production method mainly solves the technical problems of poor cleanliness and high deoxidationcost of the low-carbon low-silicon aluminum killed molten steel produced and smelted through a converter in the prior art. According to the technical scheme, the production method of the low-carbon low-silicon aluminum killed molten steel comprises the following steps that a top-bottom combined blowing converter is adopted for smelting, wherein metal main raw materials are composed of, in percentage by mass, 75%-100% of molten iron, and the balance waste steel; the smelting end point of the converter is controlled, and the w [ C ] and the temperature in the molten steel at the converter blowing end point are detected; molten steel tapping is immediately carried out after converter blowing is ended; the molten steel in a steel ladle is transported to an argon blowing station for molten steel temperature regulation and molten steel aluminum content regulation, and weak stirring is carried out on the molten steel with aluminum wires fed. The low-carbon low-silicon aluminum killed steel molten steel produced by the production method is high in cleanliness and low in deoxidation cost.

Description

technical field [0001] The invention relates to a production method of aluminum-killed steel, in particular to a production method of low-carbon and low-silicon aluminum-killed molten steel, which belongs to the technical field of steel smelting and continuous casting. Background technique [0002] The market demand for low-carbon, low-silicon, aluminum-killed steel has always been great, and many steel mills at home and abroad are producing it. The representative steel type is SPHC steel. Generally, SPHC steel requires high stamping formability, and the market demand is very large, which belongs to low-carbon aluminum-killed steel. In the prior art, the deoxidation treatment process of molten steel for smelting low-carbon, low-silicon, aluminum-killed steel in the converter is that during the alloying process of the converter tapping, 2.4-4.8 kg / t of aluminum-iron alloy is added to fully deoxidize the molten steel, and the aluminum content in the molten steel is 0.015%. Ab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C5/35C21C7/06C21C7/00
CPCC21C5/35C21C7/0056C21C7/0087C21C7/06Y02P10/20
Inventor 王多刚虞大俊郑毅邓丽琴
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com