Water-permeable concrete and preparation method thereof

A technology of concrete and water permeability, applied in the field of concrete, can solve the problems of low water permeability and structural strength, and achieve the effect of improving bearing capacity and compressive strength, improving anti-thaw capacity and durability, and high bearing capacity

Inactive Publication Date: 2019-11-22
XIJING UNIV
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of permeable concrete and its preparation method, the permeable concrete solves the problem of low water permeability and structural strength of existing permeable concrete, can improve water permeability and bearing capacity, and is not easy to break, High freeze-thaw resistance and durability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-permeable concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of permeable concrete is prepared by the following method:

[0031] (S1) Weigh by weight: 10 parts of acrylate water-based laminating adhesive, 1500 parts of gravel, 100 parts of superabsorbent resin microspheres, 300 parts of cement, 5 parts of polyol, 5 parts of triisopropanolamine, nano 10 parts of calcium carbonate, 1 part of nano silicon particles, 2 parts of sodium lignosulfonate, 4 parts of emulsifier, 130 parts of water;

[0032] (S2) Pour the weighed gravel, cement, nano-calcium carbonate, and nano-silicon particles into a planetary ball mill, use zircon as a ball, and grind at a revolution speed of 200 rpm for 60 minutes to make it fully mixed to obtain a mixture pink;

[0033] (S3) After mixing and stirring the weighed sodium lignosulfonate, emulsifier, polyol, triisopropanolamine and 1 / 2 water for 30 minutes, pour it into the mixed powder, stir it for 30 minutes, pour it into a weighing Take the acrylate water-based laminating adhesive, stir for 30 ...

Embodiment 2

[0035] A kind of permeable concrete, its preparation method is basically the same as embodiment 1, the difference is:

[0036] In step (S1), the proportions of raw materials used are different, and the parts of raw materials used are: 15 parts of acrylate water-based laminating adhesive, 1600 parts of gravel, 200 parts of superabsorbent resin microspheres, 400 parts of cement 7 parts of polyol, 10 parts of triisopropanolamine, 15 parts of nano-calcium carbonate, 5 parts of nano-silicon particles, 4 parts of sodium lignosulfonate, 6 parts of emulsifier, and 130 parts of water.

Embodiment 3

[0038] A kind of permeable concrete, its preparation method is basically the same as embodiment 1, the difference is:

[0039] In step (S1), the proportions of the raw materials used are different, and the parts of the raw materials used are: 12.5 parts of acrylate water-based laminating adhesive, 1550 parts of gravel, 150 parts of superabsorbent resin microspheres, 350 parts of cement 6 parts of polyol, 7.5 parts of triisopropanolamine, 12.5 parts of nano-calcium carbonate, 3 parts of nano-silicon particles, 3 parts of sodium lignosulfonate, 5 parts of emulsifier, and 145 parts of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses water-permeable concrete and a preparation method thereof. The concrete is prepared from the following components in parts by weight: 10-15 parts of acrylate water-based laminating adhesive, 1500-1600 parts of crushed stone, 100-200 parts of super absorbent resin microspheres, 300-400 parts of cement, 5-7 parts of polyol, 5-10 parts of triisopropanolamine, 10-15 parts of nano calcium carbonate, 1-5 parts of nano silicon particles, 2-4 parts of sodium lignin sulfonate, 4-6 parts of an emulsifier and 130-160 parts of water. The acrylate water-based laminating adhesive isprepared from an ethylene-acrylic emulsion, an acrylate emulsion and a cross-linking agent; the cross-linking agent comprises polyetherimide. The water-permeable concrete can improve the water permeability and the bearing capacity, is not prone to breakage and has high freezing and thawing resistance and durability.

Description

technical field [0001] The invention relates to concrete, in particular to a permeable concrete and a preparation method thereof. Background technique [0002] Permeable concrete is a kind of porous lightweight concrete made by mixing gel enhancer, aggregate, cement and water. It does not contain fine aggregate, and is bonded by a thin layer of cement slurry coated on the surface of coarse aggregate. It forms a honeycomb structure with evenly distributed pores, so it has the characteristics of air permeability, water permeability and light weight. As an environmental load-reducing concrete, the research and development of water-permeable concrete has attracted more and more attention. [0003] The existing permeable concrete has low water permeability, low overall structural strength, easy to break, poor frost resistance, and easy to break under low temperature conditions. Contents of the invention [0004] The purpose of the present invention is to provide a kind of perm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/00
CPCC04B28/04C04B38/00C04B2111/00284C04B2201/50C04B24/2641C04B24/287C04B14/02C04B20/0016C04B24/02C04B24/122C04B14/28C04B24/18C04B22/002C04B14/04C04B2103/0068C04B38/0074
Inventor 杨力源徐晋李泓希
Owner XIJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com