Steel for steel structure bolts

A technology for steel structures and bolts, applied in the field of fastener materials, to achieve high-strength performance grades, uniform precipitation, and prevention of grain boundary cracking.

Active Publication Date: 2021-03-23
LUOYANG SUNRUI SPECIAL EQUIP
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In improving the delayed fracture resistance of the material matrix, the crack source area of ​​the delayed fracture bolts in practical applications shows intergranular fracture morphology, and the existing patents rarely have targeted solutions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel for steel structure bolts
  • Steel for steel structure bolts
  • Steel for steel structure bolts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0044] A 50Kg steel ingot was smelted in a vacuum furnace. The chemical analysis composition of the smelted material is shown in Table 1: billet forging to a φ38mm round bar, sawing and turning to a φ33*200mm smooth bar.

[0045] Table 1, embodiment chemical composition and performance index

[0046]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

A kind of steel for steel structure bolts, the steel material contains C: 0.1~0.3, Si: 0.10~0.35, Mn: ≤1.5, S≤0.01, P≤0.015, Cr: 0.5~1.4, Mo: 0.6~1.2 in mass percentage , the rest is Fe, unavoidable impurities, and the tempering temperature of the steel material is ≥600°C during the final heat treatment. The present invention is based on the actual steel structure application environment and the fracture morphology of the existing delayed fracture fracture analysis, and optimizes the alloy composition to improve the precipitation quantity and precipitation form of grain boundary carbides and improve the delayed fracture resistance of the material. The tensile strength of the invented steel for steel structure bolts can reach more than 1040MPa after heat treatment, and the upper limit can reach 1240MPa. The performance grade of the fastener meets GB / T1231-2006 standard 10.9S grade, and has excellent resistance to delayed fracture.

Description

technical field [0001] The invention belongs to the field of fastener materials, and specifically relates to a high-strength steel structure bolt steel with good delayed fracture resistance and formability, which is suitable for the manufacture and production of large hexagon head bolts and flange surface bolts for steel structures. application. Background technique [0002] Steel structure large hexagonal head bolts have large size and specifications, large hexagonal opposite sides, large deformation of the head for upsetting and forging, and high requirements on the plasticity of the bolt material. For example, the common size of large hexagonal head bolts for railway steel structure bridges is M22 ~ M30. For example, in the GB / T1231-2006 standard, the 10.9S grade bolt materials are: 20MnTiB, ML20MnTiB, 35VB, etc. Medium and low carbon B steel has been widely used in the field of fasteners due to its low content of alloy elements, good plastic formability, and low cost. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/22C21D1/18
CPCC21D1/18C22C38/02C22C38/04C22C38/22
Inventor 范芳雄陈继志杨俊峰孙永伟
Owner LUOYANG SUNRUI SPECIAL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap