A kind of metal cleaning liquid and cleaning method thereof

A technology of metal cleaning and cleaning liquid, which is applied in the field of metal surface treatment, can solve problems such as secondary corrosion of metal copper materials, and achieve the effects of reducing waste liquid discharge, reducing excessive erosion, and inhibiting secondary erosion or secondary corrosion

Active Publication Date: 2021-04-27
SUZHOU CHAMPION COATING TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even if the rinse is thorough, the dissolved oxygen in the deionized water will cause secondary corrosion to the metal copper material during the hot air drying process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of metal cleaning liquid and cleaning method thereof
  • A kind of metal cleaning liquid and cleaning method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Preparation of cleaning solution: 80 parts of oxalic acid, 32 parts of citric acid, 53 parts of sodium dihydrogen phosphate, 18 parts of sodium pyrophosphate, 3 parts of tetrasodium iminodisuccinate, 0.5 parts of dopamine, 0.6 parts of agar, 90 parts of ethanol, with 820 1 part deionized water as solvent. Prepare the cleaning solution at a temperature of 75°C. After the preparation is completed, stir the cleaning solution quickly for 2 hours when the temperature of the cleaning solution drops to 25-28°C.

[0029] Chemical cleaning treatment: Take the metal copper plate with natural corrosion products on the surface and hang it on one end of the ultrasonic vibration head, then immerse the metal copper plate in the cleaning solution, keep the temperature of the cleaning solution at 25°C, turn on the ultrasonic vibration head vibration frequency of 100kHz, and clean for 15 minutes.

[0030] Freeze-drying: Take the metal copper plate out of the cleaning solution and remove ...

Embodiment 2

[0033] Preparation of cleaning solution: 120 parts of oxalic acid, 43 parts of citric acid, 62 parts of sodium dihydrogen phosphate, 20 parts of sodium pyrophosphate, 3.5 parts of tetrasodium iminodisuccinate, 0.6 parts of dopamine, 0.9 parts of agar, 105 parts of ethanol, and 850 parts 1 part deionized water as solvent. Prepare the cleaning solution at a temperature of 75°C. After the preparation is completed, stir the cleaning solution quickly for 3 hours when the temperature of the cleaning solution drops to 25-28°C.

[0034] Chemical cleaning treatment: Take the metal copper plate with natural corrosion products on the surface and hang it on one end of the ultrasonic vibration head, then immerse the metal copper plate in the cleaning solution, maintain the temperature of the cleaning solution at 35°C, turn on the ultrasonic vibration head vibration frequency of 100kHz, and clean for 20 minutes.

[0035] Freeze-drying: Take the metal copper plate out of the cleaning solutio...

Embodiment 3

[0038] Preparation of cleaning solution: 80 parts of oxalic acid, 32 parts of citric acid, 53 parts of sodium dihydrogen phosphate, 18 parts of sodium pyrophosphate, 3 parts of tetrasodium iminodisuccinate, 0.5 parts of dopamine, 0.6 parts of agar, 90 parts of ethanol, with 820 1 part deionized water as solvent. Prepare the cleaning solution at a temperature of 75°C. After the preparation is completed, stir the cleaning solution quickly for 2 hours when the temperature of the cleaning solution drops to 25-28°C.

[0039] Chemical cleaning treatment: Take the metal copper plate with natural corrosion products on the surface and hang it on one end of the ultrasonic vibration head, then immerse the metal copper plate in the cleaning solution, keep the temperature of the cleaning solution at 25°C, turn on the ultrasonic vibration head vibration frequency of 100kHz, and clean for 15 minutes.

[0040] Freeze-drying: Take the metal copper plate out of the cleaning solution and remove ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a metal cleaning liquid, which is used for cleaning stains and corrosion layers on the surface of metal copper. 16-48 parts of sodium, 2-5 parts of tetrasodium iminodisuccinate, 0.3-1.2 parts of dopamine, 0.4-1.8 parts of agar, 110-195 parts of ethanol, and 785-950 parts of water. The present invention also discloses a cleaning method using the above-mentioned cleaning solution, the steps of which include: S1, preparation of cleaning solution; S2, chemical cleaning treatment; S3, freeze-drying; S4, high-pressure gas injection. The cleaning liquid and the cleaning method thereof of the present invention can realize effective cleaning of stains and corrosion products on the surface of metallic copper materials, and simultaneously effectively avoid the occurrence of secondary corrosion or secondary oxidation corrosion in the final drying process.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, and relates to a metal surface cleaning liquid and a cleaning method thereof. Background technique [0002] Metal copper has good electrical conductivity, thermal conductivity, welding and plastic processing properties, and is widely used in electrical and electronic, light industry, machinery manufacturing, defense industry and other fields. In the atmospheric environment, copper is prone to chemical reactions with environmental media, and copper corrosion occurs. Generally speaking, the corrosion products of copper are mainly copper oxides, hydroxides, and basic carbonates. These corrosion products adhere to the surface of metal copper, which will greatly deteriorate its electrical, thermal and welding properties. In addition, the texture of copper is relatively soft. In industrial applications, different types of coatings are often plated on its surface to increase its hardne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23G1/06C23G1/10C23G3/00
CPCC23G1/06C23G1/103C23G3/00
Inventor 陈君乐务时
Owner SUZHOU CHAMPION COATING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com