Mask material for surface surgery anesthesia and preparation method thereof

A facial mask and surgery technology, which is applied in the field of facial mask materials for surface surgical anesthesia and its preparation, can solve the problems of slow onset, poor compliance, and unfavorable recovery of traditional Chinese medicine, and achieve fast onset, strong effect, and good effect

Inactive Publication Date: 2019-09-17
李会娟
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of traditional Chinese medicine film needs to be coated with a thick layer on the skin surface when used, and it needs to be wrapped with a fresh-keeping film. The application time is as long as more than 1 hour. The traditional Chinese medicine has a slow onset of effect and poor effect. , and there will be adverse reactions such as redness, edema, tingling, burning, etc., which is not conducive to postoperative recovery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method for surface surgical anesthesia mask material, comprising the steps of:

[0029] Ⅰ Preparation of cis-3-hexenol lactate / 2-ethylhexyl ether diethylene glycol acrylate / polyethylene glycol monoallyl ether / 3-chloro-2-hydroxypropyl acrylate copolymer: cis-3-hexenol lactate 1kg, 2-ethylhexyl ether diethylene glycol acrylate 1kg, polyethylene glycol monoallyl ether 1kg, 3-chloro-2-hydroxypropyl acrylate 0.3kg , mixed with 0.02kg of benzoin, ultrasonicated at 40°C for 10 minutes, then poured into a mold, then placed the mold in a nitrogen atmosphere, and irradiated with ultraviolet light with a wavelength of 200nm for 30 minutes to obtain cis-3-hexenol Lactate / 2-Ethylhexyl Ether Diethylene Glycol Acrylate / Polyethylene Glycol Monoallyl Ether / 3-Chloro-2-Hydroxypropyl Acrylate Copolymer;

[0030] II Acepromazine graft copolymer: Add 1kg of the copolymer prepared in step I and 0.1kg of acepromazine into 3kg of dimethyl sulfoxide, stir and react at 40°C for 3 h...

Embodiment 2

[0037] A preparation method for surface surgical anesthesia mask material, comprising the steps of:

[0038] Ⅰ Preparation of cis-3-hexenol lactate / 2-ethylhexyl ether diethylene glycol acrylate / polyethylene glycol monoallyl ether / 3-chloro-2-hydroxypropyl acrylate copolymer: cis-3-hexenol lactate 1kg, 2-ethylhexyl ether diethylene glycol acrylate 1kg, polyethylene glycol monoallyl ether 1kg, 3-chloro-2-hydroxypropyl acrylate 0.35kg , mixed with 0.025kg of benzoin ethyl ether, ultrasonicated at 45°C for 12 minutes, then poured into a mold, then placed the mold in a helium atmosphere, and irradiated with ultraviolet light with a wavelength of 210nm for 32 minutes to obtain cis-3-hexyl Enol lactate / 2-ethylhexyl ether diethylene glycol acrylate / polyethylene glycol monoallyl ether / 3-chloro-2-hydroxypropyl acrylate copolymer;

[0039] II Acepromazine graft copolymer: Add 1kg of the copolymer prepared in step I and 0.1kg of acepromazine into 3.5kg of N,N-dimethylformamide, stir and r...

Embodiment 3

[0046] A preparation method for surface surgical anesthesia mask material, comprising the steps of:

[0047] Ⅰ Preparation of cis-3-hexenol lactate / 2-ethylhexyl ether diethylene glycol acrylate / polyethylene glycol monoallyl ether / 3-chloro-2-hydroxypropyl acrylate copolymer: cis-3-hexenol lactate 1kg, 2-ethylhexyl ether diethylene glycol acrylate 1kg, polyethylene glycol monoallyl ether 1kg, 3-chloro-2-hydroxypropyl acrylate 0.4kg , mixed with 0.03kg of benzoin dimethyl ether, ultrasonicated at 50°C for 15 minutes, then poured into a mold, then placed the mold in a helium atmosphere, and irradiated with ultraviolet light with a wavelength of 210nm for 33 minutes to obtain cis-3 - Hexenyl lactate / 2-ethylhexyl ether diethylene glycol acrylate / polyethylene glycol monoallyl ether / 3-chloro-2-hydroxypropyl acrylate copolymer;

[0048] II Acepromazine graft copolymer: add 1kg of the copolymer prepared in step I and 0.1kg of acepromazine into 4kg of N-methylpyrrolidone, stir and react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a mask material for surface surgery anesthesia. The method comprises the following steps of I, preparation of a cis-3-hexenol lactate / 2-ethylhexyl ether diethylene glycol acrylate / polyethylene glycol monoallyl ether / 3-chloro-2-hydroxypropyl acrylate copolymer; II, preparation of an acetylpromazine graft copolymer; III, manufacturing of a nonwoven fabric; IV, preparation of a mask. The invention also discloses the mask material which is used for the surface surgery anesthesia and prepared by means of the preparation method of the mask material for the surface surgery anesthesia. The mask material for the surface surgery anesthesia has a good anesthesia effect on the surface of local skin to be subjected to cosmetic surgery, is convenient to use, can realize local muscle surface anesthesia in a short time, and has the advantages that the mask material takes effect quickly, the strong effect lasts for a long time and the penetrating force is high. In addition, the mask material has good air permeability and the effects of resisting bacteria and protecting the skin.

Description

technical field [0001] The invention relates to the technical field of medical equipment, in particular to a facial mask material for surface operation anesthesia and a preparation method thereof. Background technique [0002] In recent years, with the development of society, life has become more and more affluent, people's desire to pursue beauty has become more and more urgent, and the demand for laser treatment and various cosmetic plastic surgery treatments is increasing. However, these treatments are accompanied by varying degrees of pain. The pain has an invisible impact on people's psychology, and even reduces people's enthusiasm for pursuing beauty. A considerable number of patients experience the painful experience of the first treatment. In the future, fear of the pain of treatment will arise. In addition, the pain will also lead to unconscious activities of the client, which will interfere with the plastic surgeon's operation and affect the cosmetic effect. There...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K36/81A61P23/02A61K8/9789A61K8/49A61Q17/00A61Q19/00C08F283/06C08F220/22C08F218/12C08F220/28C08F8/34D04H1/42A61K31/515A61K31/5415
CPCA61K8/49A61K8/4953A61K8/9789A61K31/515A61K31/5415A61K36/236A61K36/63A61K36/66A61K36/714A61K36/81A61K36/83A61K2236/333A61K2236/39A61P23/02A61Q17/005A61Q19/00C08F8/34C08F283/065D04H1/42C08F220/22C08F218/12
Inventor 李会娟井芳王艳红
Owner 李会娟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com