Preparation method of antibacterial and mildew-proof luminous decorative coating

A decorative coating, antibacterial and anti-mildew technology, applied in the field of coatings, can solve the problems of insufficient anti-bacterial and anti-mildew performance, and achieve good biocompatibility and degradability, no toxic side effects, good anti-bacterial and anti-corrosion effects

Inactive Publication Date: 2019-09-10
陈玲玲
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention: Aiming at the problem of insufficient antibacterial and antifungal properties of existing luminous materials, a preparation method of antibacterial and antifungal luminous decorative coatings is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of antibacterial and mildew-proof luminous decorative coating

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025]Take 0.1mol / L silver nitrate solution, mass fraction is 5% chitosan-acetic acid solution, 0.2mol / L sodium borohydride solution, KH-570, nanometer titanium dioxide, epichlorohydrin, mix 0.1mol / L silver nitrate solution Mix with a mass fraction of 5% chitosan-acetic acid solution, and magnetically stir to obtain the mixed solution A, add 0.2mol / L sodium borohydride solution to the mixed solution A, and continue stirring for 1h to obtain the mixed solution B; Add KH-570 to the mixed solution B, and ultrasonically disperse it to obtain the mixed solution C. Add nano-titanium dioxide and epichlorohydrin to the mixed solution C, and stir to obtain the mixed solution D; after soaking the zeolite molecular sieve, Filter to obtain the filter residue, wash the filter residue with deionized water until neutral, and then obtain the antibacterial and antifungal agent; take epoxy resin, acrylate resin, antibacterial and antifungal agent, luminous powder, No. 200 solvent oil, and mix ep...

example 2

[0027] Take 0.1mol / L silver nitrate solution, mass fraction is 5% chitosan-acetic acid solution, 0.2mol / L sodium borohydride solution, KH-570, nanometer titanium dioxide, epichlorohydrin, mix 0.1mol / L silver nitrate solution Mix with chitosan-acetic acid solution with a mass fraction of 5%, and magnetically stir to obtain mixed solution A, add 0.2mol / L sodium borohydride solution to mixed solution A, and continue stirring for 1.5h to obtain mixed solution B; Add KH-570 to the mixed solution B, and ultrasonically disperse to obtain the mixed solution C. Add nano-titanium dioxide and epichlorohydrin to the mixed solution C, and stir to obtain the mixed solution D; after soaking the zeolite molecular sieve , filter to obtain the filter residue, wash the filter residue with deionized water to neutrality, and obtain the antibacterial and antifungal agent; take epoxy resin, acrylic resin, antibacterial and antifungal agent, luminous powder, No. 200 solvent oil, and mix epoxy resin an...

example 3

[0029] Take 0.1mol / L silver nitrate solution, mass fraction is 5% chitosan-acetic acid solution, 0.2mol / L sodium borohydride solution, KH-570, nanometer titanium dioxide, epichlorohydrin, mix 0.1mol / L silver nitrate solution Mix with a mass fraction of 5% chitosan-acetic acid solution, and magnetically stir to obtain the mixed solution A, add 0.2mol / L sodium borohydride solution to the mixed solution A, and continue stirring for 2h to obtain the mixed solution B; Add KH-570 to the mixed solution B, and ultrasonically disperse it to obtain the mixed solution C. Add nano-titanium dioxide and epichlorohydrin to the mixed solution C, and stir to obtain the mixed solution D; after soaking the zeolite molecular sieve, Filter to obtain the filter residue, wash the filter residue with deionized water until neutral, and then obtain the antibacterial and antifungal agent; take epoxy resin, acrylate resin, antibacterial and antifungal agent, luminous powder, No. 200 solvent oil, and mix e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of an antibacterial and mildew-proof luminous decorative coating, and belongs to the technical field of coatings. The invention adopts a chemical reduction method, takes sodium borohydride as a reducing agent and chitosan as a stabilizer to prepare a chitosan nanometer silver solution, wherein nanometer silver can bind to phosphides and sulfides on a bacterial cell membrane; nanometer silver entering the cell membrane can react with sulfides or phosphides of protein and DNA in the cell, block the function of enzymes and replication and transcription of DNA in the cell. A large amount of hydroxyl and amino groups exist in the molecular chain of chitosan and can interact with nanometer silver, stabilize nanometer silver nanoparticles and improvethe antibacterial property. A silane coupling agent is adopted to modify the surface of the silver-loaded chitosan, which has good affinity. The invention combines the antibacterial performance of nano titanium dioxide and silver-loaded chitosan, and the antibacterial and mildew inhibitor has photocatalytic activity under daily illumination conditions, so that the prepared luminous decorative coating has good antibacterial and mildew-proof effect and photocatalytic activity.

Description

technical field [0001] The invention relates to a preparation method of an antibacterial and mildew-proof luminous decorative coating, which belongs to the technical field of coatings. Background technique [0002] Today's world pays great attention to energy saving and environmental protection. Due to the limited mining of natural wood and the increasing demand for decorative materials, wood-grain melamine-impregnated film paper and boards (particle board, MDF) are used in architectural decoration, furniture and other industries. , multi-layer board and medium fiber board), the steel plate is pressed and pasted into a veneer board by a hot press. The Polaboard made of traditional Polaroid paper is printed with oil-based ink, which will leave solvent residues, and the product has a peculiar smell, which is harmful to health. Moreover, the surface hardness of the traditional Polaroid board is not enough, the hand feeling is poor, it is not resistant to corrosion, and the pat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D163/00C09D5/14C09D5/22
CPCC08K2003/0806C08K2003/2241C08K2201/011C09D5/14C09D5/22C09D133/04C08L63/00C08L5/08C08K9/06C08K9/12C08K3/08C08K3/22
Inventor 陈玲玲
Owner 陈玲玲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com