Graphene antibacterial fabric and preparation method thereof

A kind of antibacterial fabric and graphene technology, which is applied in the field of fabric processing, can solve the problems of fabric antibacterial performance limitation, fabric antibacterial finishing, etc., and achieve the effect of improving color fastness, high antifouling performance and good dyeability

Inactive Publication Date: 2019-08-09
南通尚坊布业有限公司
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although graphene nylon composite fiber, bamboo fiber and other fibers with antibacterial properties are used in the existing technical solutions, no further antibacterial finishing is carried out on the fabric, so the antibacterial performance of the fabric will be limited to a certain extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene antibacterial fabric and preparation method thereof
  • Graphene antibacterial fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A graphene antibacterial fabric, comprising the following components by weight:

[0049] 80 parts of graphene composite fiber, 10 parts of bamboo charcoal fiber, 6 parts of PTT, 30 parts of cotton, and 8 parts of antibacterial agent; wherein, graphene composite fiber includes 0.6 part of graphene and 79.4 parts of fiber matrix.

[0050] The preparation steps of graphene composite fiber are as follows:

[0051] S1. Pretreatment: put the graphene and fiber matrix into a vacuum oven for drying, the drying temperature is 60°C, and the drying time is 8 hours;

[0052] S2, dry mixing: put graphene and fiber matrix into a high-speed mixer, adjust the rotating speed to 220rpm, mix for 1min, then adjust the rotating speed to 800rpm, and continue mixing for 1min to obtain the premix of graphene-fiber matrix;

[0053] S3. Blending and granulation: put the graphene-fiber matrix pre-mixture into a twin-screw blender for blending and granulation. The melt blending temperature is 180 °...

Embodiment 2

[0064] A graphene antibacterial fabric, comprising the following components by weight:

[0065] 92 parts of graphene composite fiber, 12 parts of bamboo charcoal fiber, 8 parts of PTT, 35 parts of cotton, and 9 parts of antibacterial agent; wherein, graphene composite fiber includes 0.8 part of graphene and 91.2 parts of fiber matrix.

[0066] The preparation steps of graphene composite fiber are as follows:

[0067] S1. Pretreatment: put the graphene and fiber matrix into a vacuum oven for drying, the drying temperature is 70°C, and the drying time is 10 hours;

[0068] S2, dry mixing: put graphene and fiber matrix into a high-speed mixer, adjust the rotating speed to 240rpm, mix for 2min, then adjust the rotating speed to 850rpm, and continue mixing for 1min to obtain the premix of graphene-fiber matrix;

[0069] S3. Blending and granulation: put the graphene-fiber matrix pre-mixture into a twin-screw blender for blending and granulation. The melt blending temperature is 19...

Embodiment 3

[0080] A graphene antibacterial fabric, comprising the following components by weight:

[0081] 104 parts of graphene composite fiber, 13 parts of bamboo charcoal fiber, 10 parts of PTT, 40 parts of cotton, and 10 parts of antibacterial agent; wherein, graphene composite fiber includes 1 part of graphene and 103 parts of fiber matrix.

[0082] The preparation steps of graphene composite fiber are as follows:

[0083] S1. Pretreatment: put the graphene and fiber matrix into a vacuum oven for drying, the drying temperature is 80°C, and the drying time is 12 hours;

[0084] S2, dry mixing: put graphene and fiber matrix into a high-speed mixer, adjust the rotating speed to 260rpm, mix for 3min, then adjust the rotating speed to 900rpm, and continue mixing for 1min to obtain the premix of graphene-fiber matrix;

[0085] S3. Blending and granulation: put the graphene-fiber matrix pre-mixture into a twin-screw blender for blending and granulation. The melt blending temperature is 20...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene antibacterial fabric. The fabric comprises, by weight, 80-140 parts of graphene composite fibers, 10-15 parts of bamboo charcoal fibers, 6-12 parts of PTT, 30-50 parts of cotton and 8-12 parts of an antibacterial agent, wherein the graphene composite fibers comprise 0.6-1.5 parts of graphene and 79.4-138.5 parts of a fiber matrix. A preparation method of the graphene composite fibers includes the following steps of S1, pretreatment; S2, dry mixing, S3, blending and granulating; S4, melt spinning; S5, drawing and shaping, and then the graphene composite fibersare obtained. A preparation method of the graphene antibacterial fabric comprises the following steps of S1, yarn blending, S2, mercerizing; S3, warping and weaving; S4, fabric weaving; S5, antibacterial finishing; S6, post-treatment including dyeing and finishing, washing, shaping and pre-shrinking. The graphene antibacterial fabric has the advantages of being comfortable, soft, breathable, cool, durable in antibacterial performance and high in efficiency.

Description

technical field [0001] The invention relates to the technical field of fabric processing, in particular to a graphene antibacterial fabric and a preparation method thereof. Background technique [0002] As one of the three elements of clothing, fabric is the material used to make clothing. It can not only interpret the style and characteristics of clothing, but also directly relates to the performance of clothing color and shape. With the gradual improvement of people's living standards, people have put forward more and more multifunctional and style requirements for fabrics, so conventional fabrics cannot meet the needs of the market. [0003] Functional fibers mainly include: modified fibers, such as modified fibers at the raw material stage to obtain anti-pilling, antistatic, hydrophilic, flame retardant, etc.; functional finishing generally includes: comfortable finishing, which is reflected in breathability, Finishing in terms of moisture permeability, lightness, smoot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02G3/04D06M13/513D06M13/463D01F6/92D01F6/94D01F1/10D01F1/09D01D5/08D01D5/12D06M101/32D06M101/40D06M101/06
CPCD01D5/08D01D5/12D01F1/09D01F1/103D01F6/92D01F6/94D02G3/04D03D15/00D06M13/463D06M13/513D06M16/00D06M2101/06D06M2101/32D06M2101/40D10B2101/12D10B2201/02D10B2331/04D10B2401/13
Inventor 尤丽刘井忠韩小利
Owner 南通尚坊布业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More