Preparation and application of nucleic acid aptamer-nickel ferricyanide nanoparticles-rgo electrode

A nucleic acid aptamer and nanoparticle technology, applied in the field of electrochemically modified electrodes, can solve the problems of high cost, time-consuming and complicated operation, and achieve the effects of convenient operation, simple method and high sensitivity

Active Publication Date: 2021-07-27
SHANXI UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a nucleic acid aptamer-nickel ferricyanide nanoparticle-RGO electrode and its preparation method, which is used for rapid, highly sensitive and highly selective detection of PCB77, so as to overcome the existing detection method of PCB77 Complicated operation, time-consuming and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of nucleic acid aptamer-nickel ferricyanide nanoparticles-rgo electrode
  • Preparation and application of nucleic acid aptamer-nickel ferricyanide nanoparticles-rgo electrode
  • Preparation and application of nucleic acid aptamer-nickel ferricyanide nanoparticles-rgo electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] This embodiment provides a preparation of an electrochemically modified electrode for detecting PCB77.

[0032] The preparation method of PDDA-protected RGO is: measure 3.0mL of 1.2mg / mL graphene oxide solution in a reaction bottle, add 55.0ul of 10.5wt% PDDA and mix well. Then, adjust the pH to 10 by 0.13mL 28% ammonia water . Add 50.0 uL of 80% hydrazine hydrate, stir vigorously for 20 min, and then set the volume to 10 mL. Put the reaction bottle into a 60°C water bath and heat for 3.5 h to obtain a stable black suspension RGO.

[0033] The synthesis method of nickel-iron nanoparticles-RGO composite material is as follows: use 0.1M HCl to adjust the pH of the RGO solution to 3, and adjust the concentration to 20.0mM K 3 [Fe(CN) 6 ] and Ni(NO 3 )2 Under rapid stirring, add to the RGO solution, first Fe(CN) 6 3- Due to electrostatic interaction, it is adsorbed on the surface of RGO, and then the same amount of Ni(NO 3 ) 2 After working with the solution, continu...

Embodiment 2

[0036] The present embodiment provides an electrochemical analysis method for detecting PCB77, and the analysis steps are as follows:

[0037] (1)) Prepare a series of PCB77 standard solutions with different concentrations, ranging from 1.0 to 300.0 ng / L;

[0038] (2) With the nucleic acid aptamer-nickel ferricyanide nanoparticles-RGO electrode as the working electrode, the platinum electrode as the counter electrode, and the silver-silver chloride electrode as the reference electrode, the three electrodes were placed in 0.1M phosphate buffer (pH 7.41) as the electrolyte solution, the standard solution prepared in step (1) was sequentially reacted with the nucleic acid aptamer-nickel ferricyanide nanoparticles-RGO electrode, the reaction time was 60min, and the different concentrations were recorded by differential pulse voltammetry The peak current corresponding to PCB77, the differential pulse voltammogram of the peak current changing with the concentration of PCB77 is as fo...

Embodiment 3

[0041] A 50.0ng / L PCB77 solution and an interfering substance solution with a concentration 100 times that of PCB77 were prepared, and the interfering substances were PCB81, p-nitrophenol, lead ions, mercury ions, nitrobenzene, and copper ions respectively. The selectivity of nucleic acid aptamer-nickel ferricyanide nanoparticles-RGO electrode to PCB77 was investigated. Using the test conditions in Example 2, the above solutions were respectively added into the test system, reacted for 60 min, and the peak current was recorded by differential pulse voltammetry. The relative change of its peak current is as Figure 5 As shown, the nucleic acid aptamer-nickel ferricyanide nanoparticles-RGO electrode is tested against PCB77 (the first bar graph), and secondly, the electrode is tested one by one for the interfering substances (the second to seventh bar graphs). The results show that the relative change of the current of the prepared electrode is only 53.7% when detecting PCB77. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the preparation of a nucleic acid aptamer-nickel ferricyanide nanoparticle-RGO electrode and its electrochemical analysis method for PCB77. In this method, nickel-ferricyanide nanoparticles with a diameter of about 5 nm were co-deposited on the surface of reduced graphene oxide (RGO) in situ, and after being modified on the gold electrode, the PCB77 aptamer was immobilized on the nickel-ferricyanide surface through a covalent bonding reaction. Nanoparticle-RGO composite material, a nucleic acid aptamer-nickel ferricyanide nanoparticle-RGO electrode was prepared, and the electrode was used for rapid and real-time detection of PCB77 in the environment. Compared with the existing PCB77 detection method, the present invention uses a highly sensitive electrochemical method combined with an aptamer with specific recognition ability to realize highly sensitive and selective detection of the inert molecule PCB77. The detection limit can reach 0.22ng / L. Moreover, the present invention has the advantages of simple equipment, low analysis cost, rapidity and convenience.

Description

technical field [0001] The invention relates to an electrochemically modified electrode, in particular to a nucleic acid aptamer-nickel ferricyanide nanoparticle-reduced graphene oxide (RGO) electrode and a preparation method thereof, and an electrochemical analysis method of the electrode to PCB77. [0002] technical background [0003] Polychlorinated biphenyls (PCBs) can exist stably in the environment for a long time through waste discharge during production and leakage, volatilization and incineration during use, and participate in the surface cycle, and then accumulate in the biological environment through the food chain. body and the human body. Chronic low-dose PCBs exposure can cause liver damage, reproductive abnormalities, nervous and endocrine system disorders and other problems. Therefore, PCBs are listed as the first class of pollutants to be controlled by the Stockholm Convention on Persistent Organic Pollutants. Toxicologists have found that some dioxin-like...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N27/327
CPCG01N27/3278
Inventor 范丽芳王贵珍梁桂芳梁文婷刘雪峰郭玉晶董川
Owner SHANXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com