Preparation method of anti-seismic and high-temperature-resistant glue

A technology of high temperature resistant adhesive and parts by weight, applied in the field of refractory materials, can solve the problems of decreased retention, poor high temperature resistance, decreased peel strength of tapes, etc., and achieves the effect of not easy to fall off and good adhesion.

Inactive Publication Date: 2019-07-23
太仓斯迪克新材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional adhesives include acrylic adhesives, natural rubber adhesives and synthetic rubber adhesives. Among the three adhesives, synthetic rubber adhesives have the worst high temperature resistance, while acrylic adhesives have better high temperature resistance, but at higher temperatures, acrylic adhesives The heat resistance becomes worse and worse. As the temperature rises to 100°C, the peel strength of the tape will gradually decrease and the holding force will also decrease significantly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This example adopts the following preparation process: nitrile rubber: 110 parts, wax 654: 2 parts, zinc oxide: 6.5 parts, ethylene glycol dimethacrylate: 30 parts, nano silicon dioxide: 6 parts, deionized water : 300 parts, vinyl triisopropenyloxysilane: 7.5 parts, octadecyl acrylate: 30 parts, phenyltrimethoxysilane: 8 parts, polyvinyl alcohol: 4 parts, vinylphenyl silicone oil: 8 parts, Emulsifier: 9 parts, vulcanizing agent: 8 parts; its preparation process includes the following steps, 1. Take out the nitrile rubber and add it to a high-power mixer to stir evenly, and mix vinyl triisopropenyloxysilane and vinyl triisopropene Oxysilane, phenyltrimethoxysilane, octadecyl acrylate, ethylene glycol dimethacrylate, and wax 654 are mixed and stirred evenly; 2. Put nano-silica, polyvinyl alcohol, and vinyl into the extruder Extrude with phenyl silicone oil, emulsifier, and vulcanizing agent; 3. Put the extruded product and deionized water into a high-power mixer to contin...

Embodiment 2

[0021] This example adopts the following preparation process: nitrile rubber: 100 parts, wax 654: 1 part, zinc oxide: 5 parts, ethylene glycol dimethacrylate: 20 parts, nano silicon dioxide: 2 parts, deionized water : 200 parts, vinyl triisopropenyloxysilane: 5 parts, octadecyl acrylate: 20 parts, phenyltrimethoxysilane: 6 parts, polyvinyl alcohol: 2 parts, vinylphenyl silicone oil: 6 parts, Emulsifier: 8 parts, vulcanizing agent: 6 parts; its preparation process includes the following steps, 1. Take out the nitrile rubber and add it to a high-power mixer to stir evenly, and mix vinyl triisopropenyloxysilane and vinyl triisopropene Oxysilane, phenyltrimethoxysilane, octadecyl acrylate, ethylene glycol dimethacrylate, and wax 654 are mixed and stirred evenly; 2. Put nano-silica, polyvinyl alcohol, and vinyl into the extruder Extrude with phenyl silicone oil, emulsifier, and vulcanizing agent; 3. Put the extruded product and deionized water into a high-power mixer to continue mi...

Embodiment 3

[0023] This example adopts the following preparation process: nitrile rubber: 120 parts, wax 654: 3 parts, zinc oxide: 8 parts, ethylene glycol dimethacrylate: 40 parts, nano silicon dioxide: 10 parts, deionized water : 400 parts, vinyl triisopropenyloxysilane: 10 parts, octadecyl acrylate: 40 parts, phenyltrimethoxysilane: 10 parts, polyvinyl alcohol: 2-6 parts, vinyl phenyl silicone oil: 10 parts Parts, emulsifier: 10 parts, vulcanizing agent: 10 parts; its preparation process includes the following steps, 1. Take out the nitrile rubber and add it to a high-power mixer to stir evenly, mix vinyl triisopropenyloxysilane, vinyl three Isopropenyloxysilane, phenyltrimethoxysilane, octadecyl acrylate, ethylene glycol dimethacrylate, wax 654, mix and stir evenly; 2. Put nano silicon dioxide and polyvinyl alcohol into the extruder , vinyl phenyl silicone oil, emulsifier, and vulcanizing agent for extrusion; 3. Put the extruded product and deionized water into a high-power mixer to c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of refractory materials, in particular to a preparation method of anti-seismic and high-temperature-resistant glue. The preparation method comprises stepsas follows: step one, nitrile rubber is added to a stirrer and stirred uniformly, and is mixed and stirred uniformly with vinyltriisopropenyloxysilane, phenyltrimethoxysilane, octadecyl acrylate and ethylene glycol dimethacrylate; step two, nano-silica, polyvinyl alcohol, vinyl phenyl silicone oil, an emulsifier and a vulcanizing agent are added to an extruder for extrusion; step three, an extrudate and deionized water are added to the stirrer for continuous mixing and stirring; step four, a stirred substance is subjected to high-temperature desulfurization for a period of time, and plastic rubber is obtained; step five, the desulfurized plastic rubber passes through an open mill and a refining mill in sequence, and the anti-seismic and high-temperature-resistant glue is obtained. With theadoption of the technical scheme, the anti-seismic and high-temperature-resistant glue has good binding property, is not prone to falling off, has temperature resistance up to 200-300 DEG C, can be used for a long time and has certain anti-seismic capacity.

Description

technical field [0001] The invention relates to the technical field of refractory materials, in particular to a preparation method of shock-resistant and high-temperature-resistant glue. Background technique [0002] What is heat-resistant glue? There is no strict classification standard at present. Generally speaking, high-temperature resistance should be evaluated according to whether it can maintain the bonding strength required by the design in a specific temperature, time and medium, or have a certain strength retention rate. However, the requirements of various industries are not exactly the same. If someone starts from the requirements of aircraft manufacturing, it is considered that the adhesive that can be used for a long time above 150 degrees is a high temperature resistant adhesive. Some people think that after 100 hours of heat aging, the heat aging temperature at which the strength retention rate is above 30% is the high temperature resistance of the adhesive....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/06C08L9/02C08L83/07C08L29/04C08K13/02C08K3/22C08K3/36C08K5/5419C08K5/5425
CPCC08K2003/2296C08K2201/011C08L91/06C08L2201/08C08L2205/035C08L9/02C08L83/04C08L29/04C08K13/02C08K3/22C08K3/36C08K5/5419C08K5/5425
Inventor 金闯
Owner 太仓斯迪克新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap