High-gloss anti-warping toughened nylon PA66/PC alloy

A PA66, anti-warping technology, applied in the field of high-gloss anti-warping and toughened nylon PA66/PC alloy, can solve the problems of poor product surface, easy to scratch, can not meet, etc., to achieve the effect of good compatibility

Inactive Publication Date: 2019-07-19
SUZHOU WEIRUICHENG NEW MATERIAL
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Conventional PA66 reinforced material has good rigidity effect, and generally adds 10-50% of glass fiber. Due to the arrangement of glass fiber and the shrinkage of the finished product, it is easy to cause uneven products, floating fibers on the surface of the product, and poor product surface, which cannot meet the use of high-demand products. At the same time, the reinforced nylon surface has poor smoothness and high density
[0005] PC (polycarbonate) is a high molecular polymer containing carbonate groups in the molecular chain. It has excellent characteristics such as good rigidity, good toughness, small shrinkage rate and stable size, but the internal stress is large, and the surface is not wear-resistant and easy to scratch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-gloss anti-warping toughened nylon PA66/PC alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A high-gloss anti-warpage and toughened nylon PA66 / PC alloy, which includes the following components in parts by weight:

[0033] Polyamide resin (PA66) 60 parts

[0034] Polycarbonate (PC) 40 parts

[0035] Compatibility agent 15 parts

[0036] Antioxidant 1098 0.02 parts

[0037] Antioxidant 626 0.02 parts

[0038] Lubricant 0.5 parts.

[0039] Specifically, the viscosity of the polyamide resin (PA66) is 2.7. Wherein, the polyamide resin (PA66) is EPR27 of Shenma Group.

[0040] Specifically, the viscosity of the polycarbonate (PC) is 2.4. Wherein, the polycarbonate (PC) Bayer BAYER 2405 of Germany.

[0041] Specifically, the compatibilizer is POE-g-MAH, PE-g-ST, PP-g-ST, ABS-g-MAH, PP-g-MAH, EVA, SEBS, SEBS-g-MAH, PE -Two or more of g-MAH. In addition, a compound compatible toughening agent can be added to reduce stress and improve dispersion. Among them, the compound compatible toughening agent is French Arkema 4700 / EEA ethylene-ethyl acrylate copolymer.

[0042] Specifically,...

Embodiment 2

[0051] The difference between this embodiment and embodiment 1 is that a high-gloss anti-warping toughened nylon PA66 / PC alloy includes the following components in parts by weight:

[0052] 70 parts of polyamide resin (PA66)

[0053] Polycarbonate (PC) 30 parts

[0054] Compatibility agent 12 parts

[0055] Antioxidant 1098 0.02 parts

[0056] Antioxidant 626 0.02 parts

[0057] Lubricant 0.5 parts.

[0058] The invention also discloses a method for preparing the nylon PA66 / PC alloy, which includes the following steps:

[0059] (1) Preparation of raw materials: 70 parts by weight of polyamide resin (PA66), 30 parts of polycarbonate (PC), 12 parts of compatibilizer, 0.02 parts of antioxidant 1098, 0.02 parts of antioxidant 626, 0.5 parts of lubricant;

[0060] (2) Dry and pre-treat the raw materials weighed according to the above ratio, add and blend them in sequence, mix them in a high-speed mixer for a total of 10 minutes, and then send them to the twin-screw extruder for melting, mixing ...

Embodiment 3

[0063] The difference between this embodiment and embodiment 1 is that a high-gloss anti-warping toughened nylon PA66 / PC alloy includes the following components in parts by weight:

[0064] Polyamide resin (PA66) 80 parts

[0065] Polycarbonate (PC) 20 parts

[0066] Compatibilizer 10 parts

[0067] Antioxidant 1098 0.02 parts

[0068] Antioxidant 626 0.02 parts

[0069] Lubricant 0.5 parts.

[0070] The invention also discloses a method for preparing the nylon PA66 / PC alloy, which includes the following steps:

[0071] (1) Preparation of raw materials: 80 parts by weight of polyamide resin (PA66), 20 parts of polycarbonate (PC), 10 parts of compatibilizer, 0.02 parts of antioxidant 1098, 0.02 parts of antioxidant 626, 0.02 parts by weight, 0.5 parts of lubricant;

[0072] (2) Dry and pre-treat the raw materials weighed according to the above ratio, add and blend them in sequence, mix them in a high-speed mixer for a total of 10 minutes, and then send them to the twin-screw extruder for me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-gloss anti-warping toughened nylon PA66 / PC alloy and a preparation method thereof. The alloy comprises the following components in parts by weight: 60-80 parts of polyamide resin (PA66), 20-40 parts of polycarbonate (PC), 5-15 parts of a compatilizer, 0.02-0.05 part of an antioxidant 1098, 0.02-0.05 part of an antioxidant 626 and 0.5-2 parts of a lubricant. The alloy has the characteristics of high gloss, smooth surface, toughening, warping prevention, dimensional stability and the like, is used for engineering plastics of structures and appearance parts of electronics, electric appliances, automobiles and the like, is prepared from safe and environment-friendly raw materials, and is widely applied to structural parts, appearance parts and other products with high gloss, good toughness and dimensional stability requirements in the fields of household appliances, machinery, automobiles and the like.

Description

Technical field [0001] The invention relates to the technical field of polymer materials, in particular to a high-gloss anti-warping toughened nylon PA66 / PC alloy. Background technique [0002] PA66 (polyamide resin) is also known as nylon 66; Chinese name: polyhexamethylene adipamide; English name: Polyamide 66, abbreviation nylon 66, translucent or opaque milky white crystalline polymer, widely used in the manufacture of machinery, automobiles, Parts for chemical and electrical installations. [0003] Conventional PA66 as an engineering plastic is generally reinforced with glass fiber, the purpose is to improve the material's impact strength, tensile strength, flexural modulus, flexural strength, and reduce shrinkage to meet industrial use. [0004] Conventional PA66 reinforced materials have good rigidity. Generally, 10-50% of glass fiber is added. Due to the arrangement of glass fibers and the shrinkage of the finished product, it is easy to cause unevenness of the product, floa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L69/00C08L51/06C08L55/02C08L23/08C08L53/02C08L51/00C08K5/20C08K5/527
CPCC08L77/06C08L2201/08C08L69/00C08L51/06C08L55/02C08L23/0853C08L53/025C08L51/006C08K5/20C08K5/527
Inventor 唐强王克成李世平
Owner SUZHOU WEIRUICHENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com