SBR modified asphalt and preparation method thereof

A technology of styrene-butadiene rubber and modified asphalt, which is applied in building components, building insulation materials, construction, etc., can solve the problems of no improvement in the performance of modified asphalt, poor compatibility of asphalt, and low tensile strength, and achieve thermal Improved storage stability, improved thermal storage stability, and improved aging resistance

Active Publication Date: 2019-07-12
山东海方橡胶科技有限公司
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods have disadvantages such as high energy consumption, low tensile strength of modifier-modified asphalt produced, and easy segregation of modifier and asphalt during thermal storage.
Chinese patent ZL93115289.5 involves cutting the general-purpose synthetic SBR styrene-butadiene rubber into small granules and using a small amount of water as the release agent or the condensed water-containing fluffy body taken from the production line, adding it to the solvent (rubber filling oil), and then heating up and dehydrating. Made SBR styrene-butadiene rubber masterbatch filled with 65%~90% oil; the modified agent prepared by this patent has low tensile strength after asphalt modification, and the problems of easy segregation between modifier and asphalt during thermal storage are still unsolved
A method is disclosed in Chinese patent ZL97110667.3, using general-purpose styrene-butadiene rubber emulsion as raw material, styrene and maleic anhydride are polymerized into a copolymer as coating agent, superfine calcium carbonate is used as release agent, and coagulant is added. into a powdered styrene-butadiene rubber; the coating agent in this patent is too polar and incompatible with asphalt. to the role of modified asphalt
Chinese patent ZL97111343.2 mentions that the styrene-butadiene rubber emulsion is pre-crosslinked and then grafted with styrene, acrylonitrile, acrylate and other monomers to modify the styrene-butadiene rubber, adding a copolymer of styrene and maleic anhydride As a coating agent for coagulation, a modified styrene-butadiene rubber product is obtained; the coating agent in this patent is difficult to dissolve with asphalt, and a large amount of grafted polar monomers make the modified styrene-butadiene rubber difficult to Soluble in asphalt, so when used in modified asphalt, it hardly improves the performance of modified asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1) Vulcanization graft modification of general-purpose synthetic styrene-butadiene rubber emulsion

[0031] 1.1 Add 2791 grams of 1500-type styrene-butadiene rubber emulsion with a solid content of 21.5% into the reaction kettle, start stirring, and the rotation speed is 150r / min;

[0032] 1.2 Add 64 grams of disproportionated potassium abietate soap with a concentration of 25%, 3.3 grams of benzoyl peroxide, 22 grams of diphenylmethane diisocyanate (MDI), isopropyl dioleic acid acyloxy (diisooctyl phosphate Oxygen) titanate 24 grams, 30 grams of sodium metabisulfite aqueous solution of 1% concentration;

[0033] 1.3 After the addition, stir for 50 minutes at 30°C and a stirring speed of 150r / min to fully disperse the material;

[0034] 1.4 Heat up to 65°C and react at 65°C for 4 hours to obtain the cross-linked grafted styrene-butadiene rubber emulsion;

[0035]2) Micronization of cross-linked grafted styrene-butadiene rubber

[0036] 2.1 Add 1500 grams of cross-lin...

Embodiment 2

[0047] 1) Vulcanization graft modification of general-purpose synthetic styrene-butadiene rubber emulsion

[0048] 1.1 Add 2715 grams of 1502-type styrene-butadiene rubber emulsion with a solid content of 22.1% into the reactor, start stirring, and the speed is 150r / min;

[0049] 1.2 Add 48 grams of disproportionated potassium abietate soap with a concentration of 25%, 4.5 grams of dicumyl peroxide, 12 grams of triallyl isocyanurate (TAIC), isopropyl dioleic acid acyloxy (di 42 grams of isooctyl phosphate acyloxy) titanate, 20 grams of 1% sodium metabisulfite aqueous solution;

[0050] 1.3 After the addition, stir for 30 minutes at 35°C and a stirring speed of 180r / min to fully disperse the material;

[0051] 1.4 Heat up to 66°C and react at 65°C for 5 hours to obtain the cross-linked grafted styrene-butadiene rubber emulsion;

[0052] 2) Micronization of cross-linked grafted styrene-butadiene rubber

[0053] 2.1 Add 1500 grams of cross-linked branched 1502 type styrene-but...

Embodiment 3

[0064] 1) Vulcanization graft modification of general-purpose synthetic styrene-butadiene rubber emulsion

[0065] 1.1 Add 2927 grams of 1502-type styrene-butadiene rubber emulsion with a solid content of 20.5% into the reaction kettle, start stirring, and the rotation speed is 240r / min;

[0066] 1.2 Add 100 grams of fatty acid potassium soap with 20% concentration, 1.2 grams of dicumyl hydroperoxide, 18 grams of toluene diisocyanate (TDI), 12 grams of isopropyl trioleate acyloxy titanate, 1% concentration of 45 grams of sodium bisulfite aqueous solution;

[0067] 1.3 After the addition, stir for 60 minutes at 25°C and a stirring speed of 240r / min to fully disperse the material;

[0068] 1.4 Heat up to 73°C and react at 70°C for 4 hours to obtain the cross-linked grafted styrene-butadiene rubber emulsion;

[0069] 2) Micronization of cross-linked grafted styrene-butadiene rubber

[0070] 2.1 Add 1500 grams of cross-linked branched 1502 type styrene-butadiene rubber emulsion...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an SBR (styrene-butadiene rubber) modified asphalt and a preparation method thereof, and belong to the technical field of asphalt modification. Raw materials of the SBR modified asphalt comprise, by mass, 80-84.5% of matrix asphalt, 12-15% of aromatic oil and 3.5-5% of an SBR asphalt modifier, wherein raw materials of the SBR asphalt modifier comprise, by weight, 100 partsof a modified SBR emulsion (by dry rubber), 0.1-1 part of an antioxidant, 5-10 parts of an isolating agent, 3-6 parts of a dicyandiamide-formaldehyde condensate and 2-6 parts of potassium aluminum sulfate. The preparation method comprises the following steps: heating the matrix asphalt until melting, adding the aromatic oil and the SBR asphalt modifier, and shearing and swelling the obtained mixture to obtain the SBR modified asphalt. The SBR modified asphalt has good low temperature performances, ductility and bonding property, and has greatly improved viscosity, high temperature performancesand anti-aging property.

Description

technical field [0001] An SBR styrene-butadiene rubber modified asphalt and a preparation method thereof belong to the technical field of asphalt modification. Background technique [0002] SBR styrene-butadiene rubber modified asphalt has outstanding low-temperature performance, ductility and bonding performance. Compared with base asphalt, the high-temperature performance, viscosity toughness, toughness and anti-aging performance of modified asphalt are also improved. At present, SBR styrene-butadiene rubber-modified asphalt at home and abroad is polymerized at low temperature (5°C) with butadiene and styrene as polymerized monomers, rosin acid soap or fatty acid soap as emulsifier, and combined with styrene at 23.5±1 % of styrene-butadiene rubber raw materials for production. Because the tensile strength of styrene-butadiene rubber is relatively small, the tensile strength, viscous toughness, and toughness indicators of modified asphalt will be low; the proportion of but...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L91/00C08L15/00C08K5/18C08K3/26
CPCC08K2003/265C08L95/00C08L2205/03C08L91/00C08L15/00C08K5/18C08K3/26
Inventor 李洪强王涛李美霞
Owner 山东海方橡胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com