A solid resin and application for preparing carbon fiber composite materials

A technology for curing resin and composite materials, applied in the field of curing resin for preparing carbon fiber composite materials, can solve the problems of excess low-end products, insufficient high-end products, lack of competitiveness, etc., achieve high production efficiency, fast reaction molding speed, and avoid agglomeration effect of the phenomenon

Active Publication Date: 2022-08-05
SHANGHAI RES INST OF CHEM IND
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are also many problems in my country's epoxy resin industry: excess low-end products and insufficient high-end products, resulting in the lack of competitiveness of my country's epoxy resin in the international market
However, the mechanical properties such as tensile strength, flexural modulus, and flexural strength of the carbon fiber composite material obtained by this patented technology need to be further improved, thereby broadening the application field of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A solid resin and application for preparing carbon fiber composite materials
  • A solid resin and application for preparing carbon fiber composite materials
  • A solid resin and application for preparing carbon fiber composite materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The carbon fiber reinforced olefin polymer material in Example 1 is prepared by vacuum infusion process using olefin polymer monomer, catalyst, inorganic components, organic polymer additives and carbon fiber cloth (3K / 220g) as raw materials. The olefin polymer monomer is a polymerization grade, specifically dicyclopentadiene monomer; the catalyst is a catalyst toluene solution, which is a one-component catalyst and is a complex of Ru transition metals; the mass ratio of the olefin polymer monomer to the catalyst is 1000:1; the addition amount of the inorganic component is 5% of the mass of the olefin polymer monomer, and the addition amount of the organic macromolecular additive is 10% of the mass of the olefin polymer monomer; the inorganic component is nano-montmorillonite, and the organic The macromolecular auxiliary is a silane-containing coupling agent; the reaction temperature of vacuum perfusion is 35℃, and the reaction time is 15min. The amount of carbon fiber ...

Embodiment 2

[0054] The carbon fiber reinforced olefin polymer material in Example 2 is prepared by vacuum infusion process using olefin polymer monomer, catalyst, inorganic components, organic polymer additives and carbon fiber cloth (3K / 220g) as raw materials. The olefin polymer monomer is a polymerization grade, specifically dicyclopentadiene monomer; the catalyst is a catalyst toluene solution; it belongs to a one-component catalyst, which is a complex compound of Ru transition metal; the mass ratio of the olefin polymer monomer to the catalyst is 1000:1; the addition amount of the inorganic component is 5% of the mass of the olefin polymer monomer, and the addition amount of the organic polymer additive is 10% of the mass of the olefin polymer monomer; the inorganic component is kaolin, and the organic polymer auxiliary The agent is a high molecular polymer of hydroxymethyl cellulose; the reaction temperature of vacuum infusion is 35°C. The amount of carbon fiber cloth added is twice ...

Embodiment 3

[0058] The carbon fiber reinforced olefin polymer material in Example 3 is prepared by vacuum infusion process using olefin polymer monomer, catalyst, inorganic components, organic polymer additives and carbon fiber cloth (3K / 220g) as raw materials. The olefin polymer monomer is a polymerization grade, specifically dicyclopentadiene monomer; the catalyst is a catalyst toluene solution; it belongs to a one-component catalyst, which is a complex compound of Ru transition metal; the mass ratio of the olefin polymer monomer to the catalyst is 1000:1; the addition amount of the inorganic component is 5% of the mass of the olefin polymer monomer, and the addition amount of the organic macromolecular additive is 10% of the mass of the olefin polymer monomer; the inorganic component is iron-containing kaolin, and the organic high The molecular auxiliary is a silane-containing coupling agent; the reaction temperature of vacuum infusion is 35°C. The amount of carbon fiber cloth added is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a cured resin for preparing carbon fiber composite materials and its application. The raw materials include olefin polymer monomers, catalysts, inorganic components and organic macromolecular auxiliary agents; The mass ratio of the inorganic components is 100-3500:1, the addition amount of the inorganic component is 0.1-10% of the mass of the olefin polymer monomer, and the addition amount of the organic macromolecular auxiliary agent is 1% of the mass of the olefin polymer monomer. ~20%. Compared with the prior art, the present invention can be combined with carbon fiber materials to obtain carbon fiber composite materials, the composite materials have better comprehensive mechanical properties, simple and easy preparation conditions, easy to operate, easy to automate control, suitable for large-scale production, and can effectively replace the current carbon fiber. The epoxy resin system commonly used in the preparation of composite materials has good industrial application prospects.

Description

technical field [0001] The invention relates to a new method in the technical field of processing and molding of high-resolution materials, in particular to a cured resin for preparing carbon fiber composite materials and its application. Background technique [0002] Olefin polymers are a new type of green engineering plastics, which can be obtained from petroleum cracked olefin polymer monomers through ring-opening shift polymerization. Olefin polymer materials are light in weight and have excellent comprehensive properties, especially excellent mechanical properties, high modulus, high impact resistance and high creep resistance. Combined with Reaction Injection Molding (RIM), it can not only retain the excellent balance of toughness and rigidity of olefin polymers, but also can effectively prepare key parts of automobiles. It is becoming a new type of high-impact material to replace current engineering plastics. Carbon fiber is a key composite material for a new generat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L65/00C08K3/34C08K5/54C08K7/06C08G61/08C08J5/04C08L1/28C08L45/00C08L25/08C08F232/08C08F212/08C08F236/08C08L47/00C08F112/08C08L25/06C08F136/08
Inventor 付宏伟杨维成罗勇乔新锋乔拟春李秀君刘建段高坤
Owner SHANGHAI RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap