Separator modifying method for zinc negative electrode battery

A zinc negative electrode and diaphragm technology, which is applied in the field of diaphragm modification for zinc negative electrode batteries, can solve the problems of high internal impedance of the battery, small pore size, and unfriendly environment, and achieve the effects of consistent potential distribution, reduced contact angle, and low cost

Inactive Publication Date: 2019-06-21
江苏羊羊绿色电池有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical problem to be solved: This application provides a method for modifying the diaphragm for zinc negative batteries, which can suppress zinc dendrites in a wide temperature range, and solve the problem that existing diaphragms for zinc negative batteries are toxic, unfriendly to the environment, expensive, and the pore size Technical issues such as small pores and high internal impedance of the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Separator modifying method for zinc negative electrode battery
  • Separator modifying method for zinc negative electrode battery
  • Separator modifying method for zinc negative electrode battery

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] Preparation of the positive electrode sheet: first dissolve the binder polyvinylidene fluoride in N-methylpyrrolidone to make a dispersion with a mass fraction of 5%, and add Na 0.44 MnO 4 , acetylene black, and polyvinylidene fluoride are mixed in a mass ratio of 75:20:5, stirred evenly in a high-speed mixer, and the resulting mixture is evenly coated on the surface of graphite conductive paper, moved into a 120°C vacuum oven, and taken out after 6 hours , cut out to get the positive plate.

[0024] Electrolyte preparation: 28.4g of anhydrous sodium sulfate and 28.755g of zinc sulfate heptahydrate plus deionized water were fixed to 100mL, prepared to contain 2mol / L Na 2 SO 4 and 1mol / L ZnSO 4 aqueous solution to obtain an electrolyte.

[0025] Battery assembly: Zinc foil is used as the negative electrode, and the positive electrode sheet is used as the positive electrode, containing 2mol / L Na 2 SO 4 and 1mol / L ZnSO 4 The aqueous solution is used as the electroly...

Embodiment 1

[0035] Such as figure 1 As shown, a diaphragm modification method for zinc negative battery, first disperses 1.0g polyvinylpyrrolidone in 100g deionized water to prepare an aqueous dispersion with a mass fraction of about 1%, and then evenly coats the aqueous solution of polyvinylpyrrolidone Put it in a 0.3mm thick cellulose isolation film, put it in an oven to dry, and set aside, the density of polyvinylpyrrolidone coating surface is 3-5mg / cm 2 , to obtain the self-made modified diaphragm 1.

[0036] Battery assembly: the prepared positive electrode sheet is used as the positive electrode, and the zinc foil is used as the negative electrode, containing 2mol / L Na 2 SO 4 and 1mol / L ZnSO 4 The aqueous solution is used as the electrolyte, the diaphragm is self-made modified diaphragm 1, and the battery is assembled by lamination process. The battery test system for the assembled laminated hard-shell battery is tested. The test temperature is 25°C and 60°C, the test current is...

Embodiment 2

[0039] Such as figure 1 As shown, a method for modifying a diaphragm for a zinc negative electrode battery, first heats and disperses 1.0 g of agar in 100 g of deionized water to prepare an aqueous solution with a mass fraction of about 1%, and evenly coats the agar aqueous solution on a 0.3 mm thick Put it in a cellulose isolation film, put it in an oven to dry, and set aside, the density of the coated surface of agar is 1-3mg / cm 2 A self-made modified diaphragm 2 was obtained.

[0040] Battery assembly: the prepared positive electrode sheet is used as the positive electrode, and the zinc foil is used as the negative electrode, containing 2mol / L Na 2 SO 4 and 1mol / L ZnSO 4 The aqueous solution is used as the electrolyte, the diaphragm is self-made modified diaphragm 2, and the battery is assembled by lamination process. The battery test system for the assembled laminated hard-shell battery is tested. The test temperature is 25°C and 60°C, the test current is 35mA / g, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application discloses a method for suppressing zinc dendrite in a zinc negative electrode battery over a wide temperature range, and in particular to a separator modifying method for a zinc negative electrode battery. High-molecular compounds having hydrophilic groups are uniformly dispersed in separators to lower the contact angle between the electrolyte and the zinc negative electrode such that the potential distribution on the surface of the zinc negative electrode is more uniform, thereby making the deposition of zinc ions more uniform. Compared with the existing method for inhibitingzinc dendrite, the method provided by the invention not only has more obvious effect of inhibiting zinc dendrites, but also is more conducive to practical operations with lower cost.

Description

technical field [0001] The application relates to the technical field of chemical power sources, in particular to a method for modifying a diaphragm for a zinc negative battery. Background technique [0002] Zinc anode battery is a kind of battery that uses metallic zinc as the negative electrode of the battery. Due to the advantages of abundant resources, low price, green environmental protection, and high theoretical specific capacity (nearly 820mAh / g), zinc metal has become the current field of electrochemical energy storage. research focus. However, zinc anode batteries also have major problems, especially the problem of zinc dendrites. Zinc dendrites will lead to premature failure of the battery, and more seriously, it will cause battery explosion. The core problem with the battery. At present, anti-dendrite separators are often used in zinc anode batteries to inhibit the growth of zinc dendrites. At present, anti-dendrite separators are used in nickel-zinc batteri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M2/14H01M50/403H01M50/414
CPCH01M50/403Y02E60/10
Inventor 刘小林
Owner 江苏羊羊绿色电池有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com