A kind of preparation method of environment-friendly melamine-based foamed plastics

A foam and melamine-based technology, which is applied in the field of preparation of environmentally friendly melamine-based foam plastics, can solve problems such as hindering product application range, restricting market application fields, and affecting people's physical and mental health, achieving non-volatile, stable reaction, and The effect of convenient storage

Active Publication Date: 2021-10-08
PUYANG GREEN FOAM CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high formaldehyde emission of melamine-based foam plastics currently on the market, which pollutes the environment and affects people's physical and mental health, it seriously hinders the promotion of the product's application range and limits its market application field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of environment-friendly melamine-based foamed plastics
  • A kind of preparation method of environment-friendly melamine-based foamed plastics
  • A kind of preparation method of environment-friendly melamine-based foamed plastics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The preparation method of the environment-friendly melamine-based foam plastic of the present invention, the detailed steps of the preparation method are as follows:

[0042] (1) Preparation of expandable low-formaldehyde melamine-based resin:

[0043] a, with melamine, paraformaldehyde and water as main raw materials; expressed in weight kg, the addition of three main raw materials is respectively melamine 600Kg, paraformaldehyde 328.6Kg and desalted water 310Kg;

[0044] B, take by weighing melamine, paraformaldehyde and water according to the addition of three kinds of main raw materials described in step a, add three kinds of raw materials that take by weighing in the reactor and stir evenly, then add modified monomer benzomelamine 3Kg, then Add a sodium hydroxide solution with a mass percentage concentration of 20% to adjust the pH value to 8-9; when the steam is heated until the temperature of the reaction solution reaches 90°C, reduce the amount of steam introduc...

Embodiment 2

[0058] Embodiment 2: basically the same as Embodiment 1, the difference is:

[0059] The preparation method of the environment-friendly melamine-based foamed plastic of the present invention is basically the same as that of Example 1, except that:

[0060] (1) Preparation of expandable low-formaldehyde melamine-based resin:

[0061] a, represented by weight kg, the addition of three main raw materials is respectively melamine 600Kg, paraformaldehyde 357.1Kg and desalted water 319Kg;

[0062] b. Then use a sodium hydroxide solution with a mass percentage concentration of 25% to adjust the pH value to 8-9, then add 6Kg of modified monomer ultrafine polyimide resin powder; Reduce the amount of steam input and react at a constant temperature for 2.5 hours, close the steam inlet valve, and the reaction is over;

[0063] c. Then add 6.4Kg of aldehyde-removing functional monomer 1,3-dimethyl-2-imidazolidinone;

[0064] (2) Preparation of mixing aids:

[0065] Add 60Kg of 40% sodi...

Embodiment 3

[0074] Embodiment 3: basically the same as Embodiment 1, the difference is:

[0075] The preparation method of the environment-friendly melamine-based foamed plastic of the present invention is basically the same as that of Example 1, except that:

[0076] (1) Preparation of expandable low-formaldehyde melamine-based resin:

[0077] a, represented by weight kg, the addition of three main raw materials is respectively 600Kg of melamine, 400Kg of paraformaldehyde and 340Kg of desalted water;

[0078] b. Then use a sodium hydroxide solution with a concentration of 25% by mass to adjust the pH value to 8-9, then add 9Kg of modified monomer tris-(2-hydroxyethyl)isocyanate; , turn down the amount of steam into the constant temperature reaction for 2 hours, close the steam inlet valve, the reaction is over;

[0079] c, then add 13.4Kg of aldehyde-removing functional monomer melamine,

[0080] (2) Preparation of mixing aids:

[0081] Add 64Kg of 25% sodium alkylnaphthalene sulfona...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an environment-friendly melamine-based foam plastic. First, add melamine, paraformaldehyde and water into the reactor, and add modified monomers to adjust the pH value of the solution, and then heat the reaction with steam; after the reaction, add aldehyde-removing functional monomers and continue to stir the reaction to obtain volatile low-formaldehyde Melamine-based resin; add emulsifier, compound curing agent and foaming agent to the auxiliary reaction kettle in sequence and mix well to obtain mixing auxiliary; cool down the temperature of the obtained resin, and then enter the twin-screw machine by metering and mixing auxiliary at the same time. High-speed emulsification, microwave foaming after emulsification, to obtain melamine-based foam M1; finally, the melamine-based foam M1 is dried by superheated steam and microwave drying in sequence, and an environmentally friendly melamine-based foam plastic product is obtained after drying. The invention realizes the industrialized production of zero-formaldehyde-releasing melamine-based foam plastic products, and solves the key indicators of the industrialization of the melamine-based foam plastic and the bottleneck of environmental protection and safety technology.

Description

1. Technical field: [0001] The invention belongs to the technical field of material preparation, and in particular relates to a method for preparing an environment-friendly melamine-based foam plastic. 2. Background technology: [0002] Melamine-based foam, also known as melamine foam, is mostly made of melamine formaldehyde resin through microwave foaming to obtain a three-dimensional network cross-linked structure with an opening rate of more than 99%. This product has excellent sound absorption and flame retardancy. Performance, heat insulation, anti-fungal, friction, health and safety and good secondary processability and other comprehensive properties. These characteristics make the product widely used in the fields of aerospace, navigation and aviation, construction venues, factory construction, air conditioning equipment, rail transit, electronic products, biological pollution control engineering and other fields, especially for flame retardant, high temperature, high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G12/40C08J9/14C08L61/32
Inventor 史悦智胜兆泉陈言胜何利华蒋凡顺魏兰军刘军法李金纳李慧霞孟凡会孙伟李岳站程红光陈永达
Owner PUYANG GREEN FOAM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com