A kind of manufacturing method of negative ion impregnated paper/negative ion facing artificial board substrate/negative ion facing artificial board

A production method and negative ion technology are applied in the production of negative ion veneer wood-based panels and the production of negative ion impregnated paper, which can solve problems such as damage to the use environment, loss of negative ion function, and damage to appliances.

Active Publication Date: 2021-03-09
成都市美康三杉木业有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are some negative ion boards on the market, most of which are sprayed on the surface of the board, which is easy to be damaged by the environment such as foot friction, etc., and is also easy to be gradually damaged by cleaning utensils such as mops, losing the function of negative ions
There are also some plate products that add negative ions in the middle of the product or are covered by the surface structure, which cannot play the role of negative ions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of negative ion impregnated paper/negative ion facing artificial board substrate/negative ion facing artificial board
  • A kind of manufacturing method of negative ion impregnated paper/negative ion facing artificial board substrate/negative ion facing artificial board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] A kind of preparation method of negative ion impregnated color paper, comprises the following steps:

[0066] S1: By weight, 40 parts of tourmaline powder, 5 parts of borax, 5 parts of aluminum oxide, 3 parts of nano-silver, 10 parts of nano-zinc, 1 part of sodium fluorosilicate and 45 parts of deionized water are used to prepare negative ion mixture liquid;

[0067] S2: Utilize the negative ion mixed solution prepared in step S1, by weight: negative ion mixed solution: melamine glue=1:25 ratio to prepare negative ion glue; the density of melamine glue is 1.25g / cm 3 , the viscosity is 70MPa·s, the pH value is 8, and the mass percentage of solid is 40%;

[0068] S3: Pass the impregnated paper through the negative ion glue solution prepared in step S2. When impregnating, the temperature of the negative ion glue solution is 40°C. The color paper is submerged and infiltrated from the pool containing the negative ion glue solution through the conveyor belt of the assembly l...

Embodiment 2

[0070] A kind of preparation method of negative ion impregnated color paper, comprises the following steps:

[0071] S1: By weight, 30 parts of tourmaline powder, 5 parts of borax, 5 parts of aluminum oxide, 3 parts of nano-silver, 10 parts of nano-zinc, 1 part of sodium fluorosilicate and 70 parts of deionized water are used to prepare negative ion mixture liquid;

[0072] S2: Utilize the negative ion mixed solution prepared in step S1, the ratio by weight is: negative ion mixed solution: melamine glue=1:25 ratio to prepare negative ion glue; the density of melamine glue is 1.0g / cm 3 , the viscosity is 25MPa·s, the pH value is 9, and the mass percent content of solid is 35%;

[0073] S3: pass the impregnated paper through the negative ion glue solution prepared in step S2. When impregnating, the temperature of the negative ion glue solution is 35°C. The temperature is 157 ℃, and the wind speed is 3 levels for drying. After drying, anion-impregnated color paper is formed.

Embodiment 3

[0075] A preparation method of negative ion impregnated wear-resistant paper, comprising the following steps:

[0076] S1: By weight, 34 parts of tourmaline powder, 5 parts of borax, 5 parts of aluminum oxide, 3 parts of nano-silver, 10 parts of nano-zinc, 1 part of sodium fluorosilicate and 40 parts of deionized water are used to prepare negative ion mixture liquid;

[0077] S2: Utilize the negative ion mixed liquid prepared in step S1, the ratio by weight is: negative ion mixed liquid: melamine glue = 1:25 ratio to prepare negative ion glue; melamine glue is pre-added aluminum oxide wear-resistant particles;

[0078] S3: passing the impregnated paper through the anion glue solution prepared in step S2, impregnating and drying, and forming anion-impregnated wear-resistant paper after drying.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
viscosityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for making anion-impregnated paper / anion-decorated artificial board base material / anion-decorated artificial board, wherein the method for preparing the impregnated paper comprises S1: by weight, 30-40 parts of tourmaline powder, 5 parts of borax 1 part, 5 parts of aluminum oxide, 3 parts of nano-silver, 10 parts of nano-zinc, 1 part of sodium fluorosilicate and 40-70 parts of deionized water to prepare an anion mixture; S2: use the anion mixture prepared by step S1 Liquid, by weight ratio is: negative ion mixed liquid: melamine glue=1:25 ratio prepares negative ion glue; The density of melamine glue is 1.0-1.25g / cm 3 , the viscosity is 20-70MPa·s, the pH value is 8-9.5, and the mass percentage of solids is ≥30%; S3: impregnating the impregnated paper with the negative ion glue prepared in step S2, impregnated, and then dried to form the impregnated paper.

Description

technical field [0001] The invention belongs to the technical field of negative ion flooring, and in particular relates to a production method of negative ion impregnated paper, a production method of an anion-decorated artificial board base material and a production method of an anion-decorated artificial board. Background technique [0002] The concentration of negative ions in the air is one of the signs of good or bad air quality. The World Health Organization has also carried out relevant regulations on the standard concentration of negative ions in fresh air. my country has also incorporated negative ions into the weather monitoring system, which is widely used in air environmental protection and other fields. We can usually feel the air is extremely fresh by the waterfall, in the forest, and after a thunderstorm, because the air contains a lot of negative ions. Negative ions are called "air vitamins". Its functions include: dust removal, floating hair removal, odor r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/28D21H17/67D21H17/00D21H17/66D21H17/51D21H21/36D21H19/14D21H19/84D21H21/14B27M3/04B27D1/08
Inventor 张焕兵叶昌海蒲加镛
Owner 成都市美康三杉木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com