Unsaturated polyester material with excellent covering power, black edge covering capacity and combination property and preparation method of unsaturated polyester material

A comprehensive performance, polyester material technology, applied in the field of unsaturated polyester material and its preparation, can solve the problems of poor covering power and poor black edge blocking ability of carved carved panels, achieve excellent stability, reduce shrinkage, The effect of improving flow properties

Inactive Publication Date: 2019-05-17
CHENGDU ZHANCHEN PAINT
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The high-solid unsaturated polyester solid-color materials on the market generally have irregular-shaped parts, edge-beveled objects, and shaped carved boards, which have poor hiding power and poor ability to hide black edges

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Formula: 36 parts of air-drying unsaturated polyester resin, 5 parts of 20% CAB551-0.2 liquid, 0.3 part of dispersant, grinding aid: 5 parts of zinc stearate, active solvent: 5 parts of styrene, inorganic filler: transparent 9 parts of powder, 9 parts of titanium dioxide, 32 parts of barium white powder, anti-settling agent: 0.5 parts of fumed silica, 1 part of bentonite, defoamer: 0.3 parts of defoaming polymer containing silicone, leveling agent: poly 0.4 parts of acrylate compound, polyamide wax dispersion rheological additive: 0.4, rheological additive with 40% active content: 1.5 parts

[0040] Production process: put air-drying unsaturated polyester resin and 20% CAB551-0.2 liquid into it → add styrene → stir evenly at low speed → add polyamide wax dispersion, dispersant, defoamer and leveling agent in sequence → medium speed Disperse for 10 minutes → add fumed silica, bentonite, titanium dioxide, barium white powder, transparent powder and zinc stearate in sequen...

Embodiment 2

[0043] Formula: 38 parts of air-drying unsaturated polyester resin, 4 parts of 20% CAB551-0.2 liquid, 0.5 part of dispersant, grinding aid: 5 parts of zinc stearate, active solvent: 5 parts of styrene, inorganic filler: transparent 10 parts of powder, 8 parts of titanium dioxide, 31 parts of barium white powder, anti-settling agent: 0.4 parts of fumed silica, bentonite: 0.8 parts, defoaming agent: 0.3 parts of defoaming polymer containing silicone, leveling agent: poly 0.3 parts of acrylate compound, polyamide wax dispersion rheological additive: 0.3, rheological additive with 40% active content: 1.3 parts

[0044] Production process: put air-drying unsaturated polyester resin and 20% CAB551-0.2 liquid into it → add styrene → stir evenly at low speed → add polyamide wax dispersion, dispersant, defoamer and leveling agent in sequence → medium speed Disperse for 10 minutes → add fumed silica, bentonite, titanium dioxide, barium white powder, transparent powder and zinc stearate ...

Embodiment 3

[0047]Formula: 40 parts of air-drying unsaturated polyester resin, 3 parts of 20% CAB551-0.2 liquid, 0.3 parts of dispersant, grinding aid: 3 parts of zinc stearate, active solvent: 3 parts of styrene, inorganic filler: transparent 5 parts of powder, 9 parts of titanium dioxide, 34 parts of barium white powder, anti-settling agent: 0.3 parts of fumed silica, bentonite: 0.6 parts, defoaming agent: 0.2 parts of defoaming polymer containing silicone, leveling agent: poly Acrylic compound 0.3 part, polyamide wax dispersion rheological additive: 0.3, rheological additive with 40% active content: 1 part

[0048] Production process: put air-drying unsaturated polyester resin and 20% CAB551-0.2 liquid into liquid → add styrene → stir evenly at low speed → add polyamide wax dispersion, dispersant, defoamer and leveling agent in sequence → middle Disperse at high speed for 10 minutes → add fumed silica, bentonite, titanium dioxide, barium white powder, transparent powder and zinc steara...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tack-free timeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an unsaturated polyester material with excellent covering power, black edge covering capacity and combination property. The unsaturated polyester material is prepared from components in parts by weight as follows: 35-45 parts of PE resin, 2-4 parts of a 20% CAB551-0.2 solution (CAB551-0.220: BAC80), 0.2-0.4 parts of a dispersant, 1-3 parts of a polishing aid, 2-5 parts of an active solvent, 45-55 parts of inorganic filler, 0.2-0.4 parts of fumed silica, 0.2-0.5 parts of a polyamide wax dispersion rheological aid, 0.5-1.5 parts of 40% active content rheological aid, 0.5-1 part of a thickening rheological agent, 0.1-0.3 parts of a defoaming agent and 0.2-0.5 parts of a leveling agent. The unsaturated polyester material with excellent covering power, black edge covering capacity and combination property has excellent covering power and black edge covering capacity for special-shaped parts, chamfered objects and molded carved plates and has the characteristics of good leveling performance, good fullness and good rubbing property and the like of the unsaturated polyester material.

Description

technical field [0001] The invention belongs to the field of unsaturated polyester materials, and in particular relates to an unsaturated polyester material with excellent hiding power, black edge hiding ability and comprehensive performance and a preparation method thereof. Background technique [0002] High-solid unsaturated polyester solid-color materials on the market generally have irregular-shaped parts, edge-beveled objects, and shaped carved panels with poor hiding power and poor ability to hide black edges. [0003] In view of the deficiencies of the existing technology, there is an urgent need to develop an unsaturated polyester material with excellent hiding power, black edge hiding ability and comprehensive performance in this field, so as to broaden the construction tolerance of the unsaturated polyester primer and achieve the purpose of reducing environmental pollution . Contents of the invention [0004] Aiming at the deficiencies of the prior art, the inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D7/61C09D7/63C09D7/65
Inventor 兰春风黎健
Owner CHENGDU ZHANCHEN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com