Bamboo fiber reinforced nylon composite material and preparation method thereof

A nylon composite material and bamboo fiber technology, which is applied in the field of nylon composite materials to achieve the effects of excellent molding and processing performance, excellent mechanical properties and light weight

Inactive Publication Date: 2019-05-17
ZHEJIANG XINLI NEW MATERIAL CO LTD
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But did not use compatibilizer and coupling agent to modify bamboo fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo fiber reinforced nylon composite material and preparation method thereof
  • Bamboo fiber reinforced nylon composite material and preparation method thereof
  • Bamboo fiber reinforced nylon composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The formula is as follows:

[0037]

[0038] Raw materials of the following weight are taken: PA6 (Xinhui Meida, M2500I) 85Kg, PA1212 (Shandong Dongchen Engineering Plastic Co., Ltd., PA1212) 60Kg moso bamboo fiber (diameter is 5mm-10mm, Gaobeidian City Liangjiaying Shengli Hemp Rope Processing Factory ) 40Kg, lysine-based isocyanate (L-lysine ethyl diisocyanate, Suzhou Fulu Biotechnology Co., Ltd.) 4Kg, POE (Mitsui Chemicals DF740, sold by Dongguan Yuyu Plastic Raw Materials Co., Ltd.) 6Kg, POE-g -MAH (Shanghai Hongshun Biotechnology Co., Ltd.) 5Kg.

[0039] The preparation process is as follows:

[0040] First, at an ambient temperature of 25°C, use a high-speed mixer to mix the above-mentioned weighed raw materials uniformly to obtain a uniformly mixed material; then, add the mixed material to a twin-screw extruder for melt blending (mixed The materials are sequentially passed through the melting and blending intervals with temperatures of 220°C, 230°C, 230°C, 2...

Embodiment 2

[0042] The formula is as follows:

[0043]

[0044] Weigh the following ingredients by weight:

[0045] PA6 (Xinhui Meida, M2500I) 60Kg, bamboo fiber (5mm-10mm in diameter, Gaobeidian City Liangjiaying Shengli Hemp Rope Processing Factory) 25Kg, lysine-based isocyanate (L-lysine ethyl diisocyanate, Suzhou Fulu Biotechnology Co., Ltd.) 3Kg, POE (Mitsui Chemicals DF740, Dongguan Yuyu Plastic Material Co., Ltd.) 5Kg, POE-g-MAH (Shanghai Hongshun Biotechnology Co., Ltd.) 7Kg.

[0046] The preparation process is as described in Example 1.

Embodiment 3

[0048] The formula is as follows:

[0049]

[0050] Weigh the following ingredients by weight:

[0051] PA6 (Xinhui Meida, M2500I) 60Kg, Moso bamboo fiber (5mm-10mm in diameter, Gaobeidian City Liangjiaying Shengli Hemp Rope Processing Factory) 30Kg, lysine-based isocyanate (L-lysine ethyl diisocyanate, Suzhou Fulu Biotechnology Co., Ltd.) 4Kg, PP-g-MAH (Ziheng Plastic Factory, Dongyuan County, Heyuan City, Guangdong Province, 9905B) 5Kg, POE-g-MAH (Shanghai Hongshun Biotechnology Co., Ltd.) 1Kg.

[0052] The preparation process is as described in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a bamboo fiber reinforced nylon composite material and a preparation method thereof. The bamboo fiber reinforced nylon composite material is prepared from the raw materials inpercentage by weight: 33-72% of PA6, 0-35% of PA1212, 10-40% of bamboo fiber, 1-6% of lysine based isocyanate, 2-10% of toughening agents and 1-8% of POE-g-MAH. The preparation method comprises the steps that the PA6, the PA1212, the bamboo fiber, the lysine based isocyanate, the toughening agents and the POE-g-MAH are mixed uniformly by using a mixing machine, and then the bamboo fiber reinforcednylon composite material is obtained after melt blending extrusion, bracing, air cooling and pelleting are carried out by using a twin-screw extruder. According to the bamboo fiber reinforced nylon composite material and the preparation method thereof, the material mechanical properties are excellent, the preparation cost is low, and the preparation technology is simple.

Description

technical field [0001] The invention relates to the technical field of nylon composite materials, in particular to a bamboo fiber reinforced nylon composite material and a preparation method thereof. Background technique [0002] Bamboo fiber is a kind of natural environment-friendly green fiber in the true sense. Due to its low cost, low density and good processability, bamboo fiber has become the fifth largest natural fiber after cotton, hemp, wool and silk. It is a high-strength low-elongation fiber with high abrasion resistance and good dyeability. In addition, bamboo fiber has natural characteristics incomparable to other fibers such as rich sources, green environmental protection, negative ion health care, natural antibacterial, antibacterial, mite removal, deodorization, moisture absorption and release, good air permeability, and UV resistance. A big hot spot for friendly material. In addition, the extensive use of bamboo fiber is conducive to alleviating the shorta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L77/06C08L97/02C08L23/08C08L51/06C08K5/29C08J5/04
Inventor 虞瑞雷陈培叶耀挺叶定坤祁瑾钰
Owner ZHEJIANG XINLI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap