Composite film for guiding tissue repair and preparation method and application thereof

A technology to guide tissue and tissue repair, applied in medical science, prosthesis, etc., can solve problems such as difficult regeneration process, slow living process, cell shedding and death, etc., to improve protection effect, accelerate repair, and speed up repair Effect

Active Publication Date: 2019-05-10
GUANGZHOU RAINHOME PHARM&TECH CO LTD
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the regenerative composite membrane provided by the invention cannot make the cells adhere well, and the growth of the cells themselves in the three-dimensional environment is called slow, which easily causes the cells to fall off and die.
[0005] Although the existing tissue regeneration mem...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite film for guiding tissue repair and preparation method and application thereof
  • Composite film for guiding tissue repair and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1 A Composite Membrane for Guided Tissue Repair

[0034] A composite membrane that guides tissue repair, comprising a protective barrier layer made of chitosan and polyethylene glycol and a layer made of hyaluronic acid, sodium alginate, arginine-glycine-aspartame A tissue repair layer made of amino acid sequences and nano-microspheres that guides the growth of tissue cells.

[0035] The molecular weight of the polyethylene glycol is 4000Da.

[0036] The preparation method of the composite membrane for guiding tissue repair comprises the following steps:

[0037] S1 10mg chitosan is dissolved in 1% aqueous acetic acid solution by mass percentage to obtain a 1% chitosan solution by mass percentage, and 220 mg polyethylene glycol is dissolved in deionized water to obtain 22% polyethylene glycol by mass percentage. Diol solution, the resulting chitosan solution and polyethylene glycol solution were mixed and stirred for 24 hours to obtain a protective solution, w...

Embodiment 2

[0045] Example 2 A Composite Membrane for Guided Tissue Repair

[0046] A composite membrane that guides tissue repair, comprising a protective barrier layer made of chitosan and polyethylene glycol and a layer made of hyaluronic acid, sodium alginate, arginine-glycine-aspartame A tissue repair layer made of amino acid sequences and nano-microspheres that guides the growth of tissue cells.

[0047] The molecular weight of the polyethylene glycol is 8000Da.

[0048] The preparation method of the composite membrane for guiding tissue repair comprises the following steps:

[0049] S1 is that 30mg chitosan is dissolved in the acetic acid aqueous solution of 3% by mass percentage, is the chitosan solution of 3% by mass percentage, and 320mg polyethylene glycol is dissolved in deionized water, is the polyethylene glycol of 32% by mass percentage. Diol solution, the resulting chitosan solution and polyethylene glycol solution were mixed and stirred for 30 hours to obtain a protecti...

Embodiment 3

[0057] Example 3 A Composite Membrane for Guided Tissue Repair

[0058] A composite membrane that guides tissue repair, comprising a protective barrier layer made of chitosan and polyethylene glycol and a layer made of hyaluronic acid, sodium alginate, arginine-glycine-aspartame A tissue repair layer made of amino acid sequences and nano-microspheres that guides the growth of tissue cells.

[0059] The molecular weight of the polyethylene glycol is 6000Da.

[0060] The preparation method of the composite membrane for guiding tissue repair comprises the following steps:

[0061] S1 20mg chitosan is dissolved in 0.2% aqueous acetic acid solution by mass percentage to obtain a 2% chitosan solution by mass percentage, and 280 mg polyethylene glycol is dissolved in deionized water to obtain 28% polyethylene glycol by mass percentage. Diol solution, the resulting chitosan solution and polyethylene glycol solution were mixed and stirred for 28 hours to obtain a protective solution,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Molecular weightaaaaaaaaaa
Molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of biomedical materials, in particular to a composite film for guiding tissue repair and a preparation method and application thereof. The composite film for guidingtissue repair comprises a protection layer prepared from chitosan and polyethylene glycol and a tissue repairing layer prepared from hyaluronic acid, sodium alga acid, an arginine-glycine-aspartic acid sequence and nanoparticles, the protection layer achieves a protection effect, and the tissue repairing layer is used for guiding tissue cell growth. The protection layer degradation time is proper, the tissue repairing layer below can be effectively protected, chitosan and chitosan oligosaccharide ingredients are contained, and external bacterium intrusion can be stopped well. The tissue repairing layer of the composite film can continuously release cell factors, and the cells are guided to grow towards the tissue repairing layer; the arginine-glycine-aspartic acid sequence is contained, adhesion of the cell can be improved, and then repairing of injured tissue is promoted.

Description

technical field [0001] The invention belongs to the field of biomedical materials, and in particular relates to a composite membrane for guiding tissue repair and its preparation method and application. Background technique [0002] The prototype of guided tissue regeneration technology began in the late 1970s and early 1980s. Researchers applied guided tissue regeneration technology to immediate dental implants, and used it to guide bone regeneration around the implant, achieving ideal bone regeneration effects. Now, guided tissue regeneration technology has been widely used in alveolar surgery, periodontics, oral implantology, orthopedics and other fields. At present, there are many kinds of guided tissue regeneration membranes available clinically, which can be divided into two categories according to whether they can be absorbed: absorbable membranes and non-absorbable membranes; non-absorbable membranes must be removed by secondary surgery when used, which brings great ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L27/40A61L27/58A61L27/50A61L27/60
Inventor 刘少辉车七石李新霞
Owner GUANGZHOU RAINHOME PHARM&TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap