Water-based adhesive remover

A glue and water-based technology, applied in the direction of chemical paint/ink remover, detergent composition, detergent compounding agent, etc., can solve the problem of human body hazards for operators, high chemical oxygen demand, and inability to remove magnesium materials. Glue and other problems, to achieve the effect of high glue removal efficiency, low chemical oxygen demand, not easy to burn and catch fire

Inactive Publication Date: 2019-05-07
KANGZHUN ELECTRONICS TECH KUNSHAN
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, magnesium is very active and has a low ignition point. General glue removers cannot be used to remove glue from magnesium materials.
In addition, traditional glue removers generally use highl...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] In this embodiment, the water-based glue remover includes sodium hydroxide, benzyl alcohol, N-methylpyrrolidone, diethylene glycol monobutyl ether, sodium dodecylbenzenesulfonate, OP-10, benzotriazole , methyl cellulose, alkali-resistant penetrant OEP-70, paraffin, water.

[0025] In the water-based glue remover, the mass concentration of the sodium hydroxide is 250g / L, the mass concentration of the benzyl alcohol is 50g / L, and the mass concentration of the N-methylpyrrolidone is 100g / L, so The mass concentration of said diethylene glycol monobutyl ether is 100g / L, and the mass concentration of said sodium dodecylbenzenesulfonate is 25g / L, and the mass concentration of said OP-10 is 25g / L, and said benzene The mass concentration of triazole is 10g / L, and the mass concentration of described methylcellulose is 20g / L, and the mass concentration of described alkali-resistant penetration agent OEP-70 is 10g / L, and the mass concentration of described paraffin is 20g / L, the b...

Embodiment 2

[0028] In this embodiment, the water-based glue remover includes sodium hydroxide, n-octanol, methyl isoamyl ketone, ethylene glycol monoethyl ether, α-olefin sulfonate, Span-80, benzotriazole, Methylcellulose, alkali-resistant penetrant OEP-70, paraffin, water.

[0029] In the water-based glue remover, the mass concentration of the sodium hydroxide is 250g / L, the mass concentration of the n-octanol is 50g / L, and the mass concentration of the methyl isoamyl ketone is 100g / L , the mass concentration of the ethylene glycol monoethyl ether is 100g / L, the mass concentration of the α-olefin sulfonate is 25g / L, the mass concentration of the Span-80 is 25g / L, the benzo The mass concentration of triazole is 10g / L, the mass concentration of described methyl cellulose is 20g / L, the mass concentration of described alkali-resistant penetration agent OEP-70 is 10g / L, and the mass concentration of described paraffin is 20g / L, the balance is water.

[0030] Sodium hydroxide and Span-80 ar...

Embodiment 3

[0033] In this embodiment, the water-based glue remover includes monoethanolamine, n-octanol, N-methylpyrrolidone, tripropylene glycol methyl ether, fatty alcohol polyoxyethylene ether sulfate, OP-10, benzotriazole, silicon Magnesium aluminum acid, alkali-resistant penetrant AEP, paraffin, water.

[0034] The mass concentration of the monoethanolamine in the water-based glue remover is 300g / L, the mass concentration of the n-octanol is 50g / L, the mass concentration of the N-methylpyrrolidone is 100g / L, and the three The mass concentration of propylene glycol methyl ether is 100g / L, the mass concentration of the fatty alcohol polyoxyethylene ether sulfate ester salt is 25g / L, the mass concentration of the OP-10 is 25g / L, and the benzotriazole The mass concentration is 10g / L, the mass concentration of the magnesium aluminum silicate is 5g / L, the mass concentration of the alkali-resistant penetrating agent AEP is 10g / L, the mass concentration of the paraffin is 20g / L, and the bal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-based adhesive remover. The water-based adhesive remover comprises strong alkali, a main solvent, a volatilization inhibitor, a cosolvent, a corrosion inhibitor, a penetrating agent, a thickening agent, a surfactant and water. The water-based adhesive remover is a water-based formula, and the water-based formula is not prone to volatilizing or burning; when the water-based adhesive remover is used for removing the adhesive on the surface of a magnesium material, it can be guaranteed that the magnesium material cannot be burnt, the safety is high, and a magnesiumalloy substrate cannot be corroded. The water-based adhesive remover can be used by heating, thus curing adhesives which are difficult to remove can be quickly removed, and the adhesive removing efficiency is high. The water-based adhesive remover further has good degradability and little harm to the environment. The water-based adhesive remover does not contain chlorine or benzene, has low toxicity and is environmentally friendly and healthy. The water-based adhesive remover does not contain specific fluorine-chlorine carbohydrates, ethane or other harmful substances which damage the ozone layer, and has a low chemical oxygen demand. The surface of the magnesium material treated by the water-based adhesive remover does not contain grease residues and can be directly washed with water.

Description

technical field [0001] The invention relates to a glue remover, in particular to a water-based glue remover. Background technique [0002] At present, magnesium alloy is used in the components of electronic products. For example, the material of the notebook case is a combination of magnesium alloy and glass fiber plastic. During manufacture, the two materials of magnesium alloy and glass fiber plastic need to be bonded together with an adhesive (for example, AB glue). If there are defective products in the production process, in order to save costs, the defective products will generally be repaired, and glue removers need to be used to remove the adhesive and recycle the magnesium material. [0003] However, magnesium is very active and has a low ignition point, so general glue removers cannot be used to remove glue from magnesium materials. In addition, traditional glue removers generally use highly toxic solvents such as toluene and methylene chloride, which have high v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/22
CPCC11D1/123C11D1/143C11D1/22C11D1/29C11D1/667C11D1/72C11D1/74C11D1/83C11D3/0073C11D3/044C11D3/08C11D3/10C11D3/128C11D3/18C11D3/201C11D3/2013C11D3/2034C11D3/2041C11D3/2068C11D3/2072C11D3/2093C11D3/222C11D3/225C11D3/28C11D3/30C11D3/3753C11D3/43C09D9/005C11D1/12C11D3/2003
Inventor 欣小波陈敬华许维贤成梅春蔡娜
Owner KANGZHUN ELECTRONICS TECH KUNSHAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap