Polyester fabric for dustproof garment and making method of fabric

A polyester and fabric technology, applied in the field of polyester fabrics for dust-proof wear and its preparation, can solve the problems of easy dust contamination, poor hygroscopicity, poor dust-proof ability, etc., to improve the dispersion effect, reduce the addition amount, and improve the dust-proof effect. Effect

Inactive Publication Date: 2019-05-03
湖州双林金辉船舶制造有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor dustproof ability and easy to be stained with dust, which greatly restricts the application and development of polyester fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of dust-proof polyester fabric for clothing, which uses dust-proof and anti-static polyester fiber as raw material, and the dust-proof and anti-static polyester fiber includes the following raw materials in weight percentage:

[0036] Antistatic modifier 1.7%

[0037] Anti-dust treatment agent 0.35%

[0038] Molybdenum disulfide 2.2%

[0039] Polyester chip allowance.

[0040] In the described antistatic modifier, the weight percent of each raw material is:

[0041] Superfine copper wire 12.5%

[0042] Graphene 0.15%

[0043] Calcined Shell Powder 55%

[0044] Gelatin balance.

[0045] The diameter of the ultrafine copper wire is 0.012-0.015mm.

[0046] The particle size of the calcined shell powder is 10-50 μm.

[0047] In the described dust-proof treatment agent, the weight percent of each raw material is:

[0048] Nano Titanium Dioxide 1.8%

[0049] Polystyrene 10.5%

[0050] Lanthanum oxide 0.025%

[0051] Ethyl acetate balance.

[0052] A kind o...

Embodiment 2

[0059] A kind of dust-proof polyester fabric for clothing, which uses dust-proof and anti-static polyester fiber as raw material, and the dust-proof and anti-static polyester fiber includes the following raw materials in weight percentage:

[0060] Antistatic modifier 1%

[0061] Dust-proof treatment agent 0.2%

[0062] Molybdenum disulfide 3%

[0063] Polyester chip allowance.

[0064] In the described antistatic modifier, the weight percent of each raw material is:

[0065] Superfine copper wire 10%

[0066] Graphene 0.05%

[0067] Calcined Shell Powder 50%

[0068] Gelatin balance.

[0069] The diameter of the ultrafine copper wire is 0.012-0.015mm.

[0070] The particle size of the calcined shell powder is 10-50 μm.

[0071] In the described dust-proof treatment agent, the weight percent of each raw material is:

[0072] Nano Titanium Dioxide 1%

[0073] Polystyrene 12%

[0074] Lanthanum oxide 0.02%

[0075] Ethyl acetate balance.

[0076] A kind of preparati...

Embodiment 3

[0083] A kind of dust-proof polyester fabric for clothing, which uses dust-proof and anti-static polyester fiber as raw material, and the dust-proof and anti-static polyester fiber includes the following raw materials in weight percentage:

[0084] Antistatic modifier 2%

[0085] Dust-proof treatment agent 0.5%

[0086] Molybdenum disulfide 2%

[0087] Polyester chip allowance.

[0088] In the described antistatic modifier, the weight percent of each raw material is:

[0089] Superfine copper wire 15%

[0090] Graphene 0.2%

[0091] Calcined Shell Powder 60%

[0092] Gelatin balance.

[0093] The diameter of the ultrafine copper wire is 0.012-0.015mm.

[0094] The particle size of the calcined shell powder is 10-50 μm.

[0095] In the described dust-proof treatment agent, the weight percent of each raw material is:

[0096] Nano Titanium Dioxide 3%

[0097] Polystyrene 8%

[0098] Lanthanum oxide 0.05%

[0099] Ethyl acetate balance.

[0100] A kind of preparation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a polyester fabric for a dustproof garment. A dustproof anti-static polyester fiber is used as a raw material. The dustproof anti-static polyester fiber comprises the raw materials of an anti-static modifier, a dustproof treatment agent, molybdenum disulfide and a polyester chip. A superfine copper wire is added into the fiber, the anti-static effect can be achieved, and compared with a common fiber blending mode, the addition amount is smaller than 1%; by mixing calcined shell powder with the superfine copper wire, the function of a dispersion agent can be achieved, themain component of the shell powder is calcium carbonate, after the shell powder is cleaned through a faintly acid detergent and then can be continuously and slightly dissolved, and it can be guaranteed that after the fabric is used for a long time, the anti-static effect is not weakened; by adding graphene, the addition number of the super-fine copper wire can be obviously lowered; by adding molybdenum dioxide, the dispersion effect of the anti-static modifier can be improved, and the addition number of the anti-static modifier is reduced; by adopting a special dustproof treatment agent of aninorganic, organic and catalyst combination mode, the good dustproof effect can be achieved.

Description

technical field [0001] The invention relates to the field of functional clothing fabrics, in particular to a dustproof clothing polyester fabric and a preparation method thereof. Background technique [0002] As the most widely used chemical fiber, polyester fiber has good fiber-forming and mechanical properties, high strength, good light resistance, heat resistance and acid and alkali resistance, good processability and spinnability, and can be purely spun or blended and interweave. Polyester fabrics are washable, wear-resistant, non-ironing and wrinkle-resistant, and are widely used in clothing, home textiles, decoration and product applications. However, polyester fibers also have disadvantages such as poor hygroscopicity, non-sweat-absorbing fabrics, stuffy feeling when worn, poor dust-proof ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fibers. In order to improve the wearing comfort of polyester fibers ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/09D01F1/10
Inventor 潘金江
Owner 湖州双林金辉船舶制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com